Electrolyte solution for ultra-low temperature aluminum electrolytic capacitor and preparation method thereof

An aluminum electrolytic capacitor, ultra-low temperature technology, applied in the direction of electrolytic capacitors, capacitor manufacturing, capacitors, etc., can solve the problems of small capacity of aluminum electrolytic capacitors, easy to corrode sealing rubber, and failure to start electrical appliances, etc., to achieve low cost and less self-consumption energy , The effect of less heat generated by the product

Active Publication Date: 2022-02-11
ZHUHAI GREE XINYUAN ELECTRONICS +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the electrolytic solution used in the above-mentioned aluminum electrolytic capacitor has a large resistivity under ultra-low temperature conditions, the capacity of the aluminum electrolytic capacitor is small, the electrical appliances cannot be started, the performance is poor at room temperature and ultra-low temperature, the sealing rubber is easy to corrode, the service life is seriously shortened, and the cost is high. Due to the extremely difficult process and other problems, the present invention provides an electrolyte solution for ultra-low temperature aluminum electrolytic capacitors and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolyte solution for ultra-low temperature aluminum electrolytic capacitor and preparation method thereof
  • Electrolyte solution for ultra-low temperature aluminum electrolytic capacitor and preparation method thereof
  • Electrolyte solution for ultra-low temperature aluminum electrolytic capacitor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] like figure 1 Shown, in order to prepare the electrolytic solution that above-mentioned ultra-low temperature aluminum electrolytic capacitor is used, its preparation method is as follows:

[0033] S1: Mix the first solvent and the second solvent evenly, and heat to 40-65°C, and keep the temperature for 5-15min;

[0034] S2: Add a third solvent to the mixed solution in S1, heat to 75-90°C, and keep the temperature constant for 20-40min;

[0035] S3: Then add the solute and high-temperature stabilizer, and heat to 100-110°C, and keep the temperature constant for 50-70min;

[0036] S4: Cool down to 80-90°C, add hydrogen remover, and keep the temperature constant for 25-35min;

[0037] S5: Lower the temperature to below 60°C to obtain an ultra-low temperature electrolyte.

[0038] That is, mix 40-50% ethylene glycol and 20-30% water, heat to 50°C and keep it for 10 minutes; then add 5-10% sulfolane, continue to heat to 85°C, keep it for 30 minutes; then add 8-15% ammoni...

Embodiment 2

[0041] Mix 43% ethylene glycol and 22% water, heat to 50°C and keep it warm for 10 minutes; then add 8% 1,2-propanediol, continue heating to 85°C, keep warm for 30 minutes; then add 13% ammonium adipate, 2% hexadiene Acid, 4% mannitol, 1% citric acid, 1.5% diammonium hydrogen phosphate, 2% ammonium succinate, 2% ammonium formate, continue heating to 105°C, keep warm for 60min; then cool down to 85°C, add 1.5% Ammonium nitrobenzoate, keep warm for 30 minutes; finally, continue to cool down to below 60°C to obtain ultra-low temperature electrolyte B.

Embodiment 3

[0043] Mix 45% ethylene glycol and 25% water, heat to 50°C and keep it for 10 minutes; then add 9% ethylene glycol monomethyl ether, continue to heat to 85°C, keep it for 30 minutes; then add 8% ammonium adipate, 1.5% adipate Diacid, 3% mannitol, 1.5% citric acid, 2% diammonium hydrogen phosphate, 3% ammonium succinate, 2% ammonium formate, continue heating to 105°C, keep warm for 60min; then cool down to 85°C, keep warm for 30min; Finally, continue to lower the temperature to below 60°C to obtain ultra-low temperature electrolyte C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of aluminum electrolytic capacitors, and in particular relates to an electrolyte solution for ultra-low temperature aluminum electrolytic capacitors and a preparation method thereof. The electrolytic solution for ultra-low temperature aluminum electrolytic capacitors of the present application includes the following raw materials in mass percentage, the first solvent 40-50%, the second solvent 20-30%, the third solvent 5-10%, solute 1-15%, additives 0.5-5%, the additives include one or more of hydrogen remover and high-temperature stabilizer, so that it will not freeze at ultra-low temperature, and the change of resistivity is small. Normal use between ℃, no corrosion to the sealing rubber of aluminum electrolytic capacitors, good sealing performance, more stable life, no need to increase additional material and process costs, suitable for mass production and use.

Description

technical field [0001] The invention belongs to the technical field of aluminum electrolytic capacitors, and in particular relates to an electrolyte solution for ultra-low temperature aluminum electrolytic capacitors and a preparation method thereof. Background technique [0002] As a commonly used device on electronic circuits, capacitors play the electrical role of filtering, bypassing, coupling, decoupling, and switching. Aluminum electrolytic capacitors are the most special and critical components of capacitors, and they are widely used in electrical appliances. , It can be said that without aluminum electrolytic capacitors, there will be no diversification and powerful functions of electrical appliances. [0003] Due to the wide range of applications of electrical appliances, especially the extremely low temperature in winter in the north, strict requirements are placed on the use of aluminum electrolytic capacitors, and the decisive role is the liquid electrolyte (comm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/035H01G9/08H01G13/00
CPCH01G9/035H01G9/08H01G13/00
Inventor 黄定胜
Owner ZHUHAI GREE XINYUAN ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap