Composite electroplating brightener and preparation method thereof

A composite electroplating and brightener technology, which is applied in the field of electroplating additives, can solve the problems of general hole filling effect, poor brightening effect, and little improvement effect, so as to achieve good hole filling effect, save manpower and equipment costs, and improve the coating quality. The effect of high gloss on the surface

Inactive Publication Date: 2020-04-24
浙江金欣新材料科技股份有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] 1. The function is single. In addition to achieving the bright effect, it lacks the improvement effect on the current efficiency, elongation and tensile strength of the coating, or the improvement effect is very small;
[0009] 2. The hole filling effect on the surface of electroplating (such as electroplating copper or electrogalvanizing) is average, the gloss is not high, and the bright effect is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A composite electroplating brightener, according to the volume fraction of each raw material in every liter of electroplating bath, comprises the following raw materials in parts by weight:

[0047] Copolymer of 2,2-dimethyl-1,3-propanediol and 1,2-ethylene glycol 7mL / L,

[0048] Sodium phenyl dithiopropane sulfonate 12mL / L,

[0049] Diphenylaminothiourea 6mL / L,

[0050] Triethanolamine 6mL / L,

[0051] Sodium polydithiodipropane sulfonate 2.2mL / L,

[0052] Nitrogen-containing heterocyclic compounds 14mL / L.

[0053] In this embodiment, the nitrogen-containing heterocyclic compound is methyl violet.

[0054] In the present embodiment, the preparation method of the composite electroplating brightener comprises the following steps:

[0055] A, according to the total volume of electroplating bath, calculate respectively the addition of each raw material of described composite electroplating brightener;

[0056] B. Weigh each raw material of the composite electroplating...

Embodiment 2

[0058] A composite electroplating brightener, according to the volume fraction of each raw material in every liter of electroplating bath, comprises the following raw materials in parts by weight:

[0059] Copolymer of 2,2-dimethyl-1,3-propanediol and 1,2-ethylene glycol 12mL / L,

[0060] Sodium phenyl dithiopropane sulfonate 7mL / L,

[0061] Diphenylaminothiourea 3mL / L,

[0062] Triethanolamine 10mL / L,

[0063] Sodium polydithiodipropane sulfonate 1.2mL / L,

[0064] Nitrogen-containing heterocyclic compounds 17mL / L.

[0065] In this embodiment, the nitrogen-containing heterocyclic compound is basic yellow.

[0066] In the present embodiment, the preparation method of the composite electroplating brightener comprises the following steps:

[0067] A, according to the total volume of electroplating bath, calculate respectively the addition of each raw material of described composite electroplating brightener;

[0068] B. Weigh each raw material of the composite electroplating...

Embodiment 3

[0070] A composite electroplating brightener, according to the volume fraction of each raw material in every liter of electroplating bath, comprises the following raw materials in parts by weight:

[0071]Copolymer of 2,2-dimethyl-1,3-propanediol and 1,2-ethylene glycol 9mL / L,

[0072] Sodium phenyl dithiopropane sulfonate 10.5mL / L,

[0073] Diphenylaminothiourea 4.8mL / L,

[0074] Triethanolamine 8mL / L,

[0075] Sodium polydithiodipropane sulfonate 1.8mL / L,

[0076] Nitrogen-containing heterocyclic compounds 15mL / L.

[0077] In this embodiment, the nitrogen-containing heterocyclic compound is a mixture of methyl violet, saffron and basic yellow.

[0078] In this embodiment, the nitrogen-containing heterocyclic compound is a mixture of methyl violet, saffron and basic yellow. The nitrogen-containing heterocyclic compound is one of the mass of methyl violet, saffron and basic yellow. The ratio is 10:3.5:15.

[0079] In the present embodiment, the preparation method of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite electroplating brightener. Every liter of an electroplating solution comprises the following raw materials in parts by volume: 7 to 12 mL/L of copolymer of 2,2-dimethyl-1,3-propanediol and 1,2-ethylene glycol, 7 to 12 mL/L of sodium phenyldithiopropane sulfonate, 3 to 6 mL/L of diphenylamine thiourea, 6 to 10 mL/L of triethanolamine, 1.2 to 2.2 mL/L of sodium polydithiodipropane sulfonate and 14-17 mL/L of a nitrogenous heterocyclic compound. The composite electroplating brightener can be suitable for various electroplating processes such as copper plating,zinc plating, copper-zinc alloy plating and the like, has multiple functions, achieves the brightening effect, and also has remarkable improvement effects on the current efficiency, the elongation, the tensile strength and other properties of a plating layer; and the electroplating brightener has a good hole filling effect on the surface of an electroplated (such as electrocoppering or electrogalvanizing) base material, the surface gloss of the plating layer is high, and the brightening effect is good.

Description

technical field [0001] The invention relates to the technical field of additives for electroplating, in particular to a composite electroplating brightener and a preparation method thereof. Background technique [0002] Electroplating is the process of plating a thin layer of other metals or alloys on the surface of certain metals using the principle of electrolysis. It is a process of using electrolysis to attach a layer of metal film to the surface of metal or other material parts to prevent metal oxidation ( Such as rust), improve wear resistance, electrical conductivity, reflective properties, corrosion resistance (copper sulfate, etc.) and enhance the appearance. [0003] The main function of the brightener is to remove the oil, oxidized and unoxidized surface impurities staying on the metal surface through the active surface, and to maintain the cleanliness, gloss and color fastness of the outside of the object. The texture of the appearance is affected by the grindin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/22C25D3/38C25D3/56C25D3/58
CPCC25D3/22C25D3/38C25D3/565C25D3/58
Inventor 潘璐洁黄海宾
Owner 浙江金欣新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap