A kind of preparation method of composite carrier

A composite carrier and precursor technology, applied in catalyst carrier, chemical instrument and method, catalyst activation/preparation, etc., can solve problems such as difficult effective combination, carrier pore structure damage, etc., to improve carrier strength and facilitate peptization , the effect of uniform carrier properties

Active Publication Date: 2022-05-03
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method also does not avoid the addition of acid during the molding process, which will still lead to partial destruction of the carrier pore structure
At the same time, this method uses organic substances containing hydroxyl or carboxyl groups to enhance the binding ability of alumina and molecular sieves. There is no chemical reaction between alumina and molecular sieves, so it is difficult to effectively combine them. During the drying and roasting process, with the decomposition of organic substances, the product catalyst The alumina and molecular sieve components will agglomerate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of composite carrier
  • A kind of preparation method of composite carrier
  • A kind of preparation method of composite carrier

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]Put 1 L of aluminum sulfate solution (concentration of 0.2 mol / L) and 1 L of sodium metaaluminate solution (concentration of 0.3 mol / L) in the raw material tank respectively, and place 1 L of pure water in the reaction tank as the bottom liquid, pass The temperature of the reaction tank is controlled to 60° C. by water circulation, and a small amount of sodium hydroxide is added to make the pH value of the solution 8.5. Inject the aluminum sulfate solution into the reaction tank at a rate of 10 mL / min, and at the same time inject the sodium metaaluminate solution and adjust the rate so that the pH value of the reaction tank solution is constant at 8.8. After 60 min, the neutralization is completed, and the Na is fully washed to remove + ions and SO 4 2- After ionization, a certain amount of deionized water was added to obtain pseudo-boehmite slurry A with a solid-to-liquid ratio of 8% (calculated as alumina).

Embodiment 2

[0031] 50g ZSM-5 molecular sieve (SiO 2 / Al 2 o 3 The molar ratio is 30.0, the unit cell constant is 20 Å, and the relative crystallinity is 85%), and put it into the 625g pseudoboehmite slurry A obtained in Example 1, stir well and then add 200g ethanol, continue stirring evenly, then add 50g of tetraethoxysilane, after continuous stirring, a small amount of tetramethylammonium hydroxide was added to adjust the pH value of the slurry to 8.5. Put it in a closed autoclave, age at 185°C for 24 hours, take it out and filter until the water content of the filter cake is 39%, add 8g of ethylenediamine and 6g of tetraethoxysilane and knead it into a plastic body, then extrude into a strip, and dry at 100°C After 3 hours, it was calcined at 500° C. for 4 hours to obtain the final composite carrier S-1.

Embodiment 3

[0033] 10g SBA-15 mesoporous molecular sieve (SiO 2 / Al 2 o 3 The molar ratio is 35.0) into the 625g pseudo-boehmite slurry A obtained in Example 1, and then add 500g isopropanol after stirring evenly, and then add 75g dimethylvinylethoxysilane after continuing to stir evenly, After continuing to stir evenly, add a small amount of triethanolamine to adjust the pH value of the slurry to 9.0. Put it in a closed autoclave, age at 160°C for 20 hours, take it out and filter until the water content of the filter cake is 52%, add 3.5g of diethylamine and 4g of dimethylethoxysilane and knead it into a plastic body, and then extrude it into a strip. After drying at 100°C for 3 hours, it was calcined at 500°C for 4 hours to obtain the final composite carrier S-2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a composite carrier. The preparation method of the composite carrier of the present invention includes the following contents: (1) uniformly mixing pseudo-boehmite precursor slurry, molecular sieve and organic alcohol to obtain slurry A; (2) adding silane coupling agent to step (1 ) mixed evenly in the obtained slurry A, and then adjusted the pH value of the slurry to 7.5~11 to obtain the slurry B; (3) The slurry B obtained in step (2) was aged under a certain pressure, and after the aging was completed, the material was removed by filtration After a certain amount of water is added, organic amine and silane coupling agent are added to knead to form a plastic body, and after molding, drying and roasting, a composite carrier is obtained. In this method, molecular sieves are introduced during the growth process of alumina crystal nuclei, and a silane coupling agent is added. Through the hydrolysis of the silane coupling agent, the combination of alumina crystals and molecular sieves occurs in an orderly manner, avoiding the agglomeration of alumina and molecular sieves, and effectively controlling the carrier. pores and surface acid formation.

Description

technical field [0001] The invention relates to a method for preparing a composite carrier, in particular to a method for preparing a composite hydrogenation catalyst carrier. Background technique [0002] In today's petroleum refining process, catalysts play a very important role, and the physical and chemical properties of catalyst supports have a great influence on the activity of catalysts. Usually the carrier of the hydrotreating catalyst is porous acidic alumina, and there are literature patent reports to adopt porous low-acidity molecular sieve or composite alumina (CN103349995A, CN102631934A, CN105251527A, J.Catal.317 (2014) 303-317, J.Catal.317 (2010) 273-286) as a carrier to prepare a highly active hydrotreating catalyst. Compared with porous acidic alumina carrier catalyst, this catalyst has stronger hydrogen adsorption capacity, so its hydrogenation activity is higher and it is easy to 4,6- Hydrodesulfurization of dimethyldibenzothiophene (4, 6-DMDBT) which is d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/40B01J29/03B01J29/70B01J35/10B01J37/03B01J32/00B01J29/48B01J29/78
CPCB01J29/40B01J29/0308B01J29/7007B01J35/1019B01J35/1038B01J35/1042B01J37/031B01J37/0018B01J29/48B01J29/0341B01J29/7815B01J2219/18
Inventor 孙进郭蓉杨成敏段为宇姚运海
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com