A kind of environment-friendly trace lubricant and preparation method thereof

A technology of trace lubricant and lubricant composition, applied in the field of lubrication, can solve the problems of environmentally unfriendly sulfur-containing and chlorine-containing additives, pollution, large amount of lubricant used, etc., and achieves remarkable environmental protection effect and good biodegradability. , the effect of good lubricating performance

Active Publication Date: 2021-11-02
上海贝能环保科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional metal cutting generally uses mineral oil / vegetable oil / cutting fluid for a large amount of shower lubrication and cooling. The amount of lubricant used is large, which not only wastes resources, but also causes huge pollution to the processing site and the environment, and also seriously affects the health of the operators. Healthy body
[0003] In order to solve these problems, some progress has been made in the recent research on micro-quantity lubrication technology at home and abroad. The micro-quantity lubrication technology has solved the problems of large amount of lubricant used and serious pollution. Excessive use of sulfur and chlorine-containing lubricants that are not friendly to the environment additive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly trace lubricant and preparation method thereof
  • A kind of environment-friendly trace lubricant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh 304.42g (1mol) lactoic acid and 344.52g (2mol) capric acid into the reactor, add a catalyst (8g cation exchange resin), and react at a temperature of 220°C for 3 hours under nitrogen protection; Moisture is removed under reduced pressure; ie, a lubricant composition.

[0035] Weigh and weigh 400g of lubricant composition, 200g of sophorolipid, 100g of polysucrose caprate, 50g of sodium castor oil sulfonate, 50g of isostearyl alcohol, and 200g of deionized water, mix and stir at room temperature until translucent. A micro lubricant.

[0036] The preparation method of above-mentioned polysucrose decanoate:

[0037] Step 1: Add 342.3g (1mol) of sucrose, 139.28g (1.2mol) of maleic acid, 1033.56g (6mol) of n-decanoic acid, and 10g of catalyst (10% dilute sulfuric acid) into the reaction kettle, at a reaction temperature of 220°C React for 4 hours; after the reaction, depressurize and discharge the water, which is sucrose caprate;

[0038] Step 2. When the temperatur...

Embodiment 2

[0040] Weigh 304.42g (1mol) of lactoic acid and 300.48g (1.5mol) of lauric acid into the reactor, add the catalyst (1.8g of phosphotungstic acid), and react at a temperature of 180°C for 5 Hours; decompression to remove moisture; that is, a lubricant composition.

[0041] Weigh and weigh 300g of lubricant composition, 300g of sophorolipid, 200g of polysucrose laurate, 70g of sodium castor oil sulfonate, 80g of isostearyl alcohol, and 50g of deionized water, mix and stir at room temperature until translucent. A micro lubricant.

[0042] The preparation method of above-mentioned polysucrose laurate:

[0043] Step 1: Add 342.3g (1mol) of sucrose, 116.07g (1mol) of fumaric acid, 900.96g (3mol) of lauric acid, and 2g of phosphotungstic acid into the reactor, and react at a reaction temperature of 180°C for 5 hours; after the reaction Decompress and discharge water, which is sucrose laurate;

[0044] Step 2. When the temperature in the reactor drops below 100°C, add 1g of initiat...

Embodiment 3

[0046] Weigh 304.42g (1mol) of lactoic acid and 342.56g (1.5mol) of myristic acid into the reaction kettle, add the catalyst (1g of phosphotungstic acid), and react at a temperature of 200°C for 4 hours under nitrogen protection ; Decompression to remove moisture; that is, a lubricant composition.

[0047] Weigh and weigh 350g of lubricant composition, 250g of sophorolipid, 150g of polysucrose stearate, 60g of sodium castor oil sulfonate, 90g of isostearyl alcohol, and 100g of deionized water, mix and stir at room temperature until translucent. It is a micro lubricant.

[0048] The preparation method of above-mentioned polysucrose stearate:

[0049]Step 1: Add 342.3g (1mol) of sucrose, 98.08g (1mol) of maleic anhydride, 1137.92g (4mol) of stearic acid, and 5g of phosphotungstic acid into the reactor, and react at a reaction temperature of 200°C for 4.5 hours; After decompression to discharge water, it is sucrose stearate;

[0050] Step 2. When the temperature in the reactor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A lubricant composition provided by the present invention is characterized in that, it is prepared from lac jatrophic acid and fatty acid; the molar ratio of lac jatrophic acid and fatty acid is 1:1-2. The lubricant composition prepared by adopting the invention is a kind of fatty acid ester of lactoic acid, is a good non-ionic surfactant and lubricant, and has good lubricating performance; at the same time, it has good biodegradability and is friendly to the environment. The present invention also provides a lubricant composition to prepare a micro-lubricant, which is characterized in that it is prepared from the following components in weight percentage: lubricant composition 30-40%; sophorolipid 20-30%; polysucrose fat Ester 10‑20%; Sodium castor oil sulfonate 5‑10%; Isostearyl alcohol 5‑10%; Deionized water balance. The micro-quantity lubricant prepared by the invention can meet the lubricating cooling, extreme pressure anti-wear and anti-rust requirements of metal processing; when used with a micro-quantity lubrication device, the amount of lubricant used can be saved by more than 90%.

Description

technical field [0001] The invention belongs to the technical field of lubrication, and in particular relates to an environment-friendly trace lubricant and a preparation method. Background technique [0002] Traditional metal cutting generally uses mineral oil / vegetable oil / cutting fluid for a large amount of shower lubrication and cooling. The amount of lubricant used is large, which not only wastes resources, but also causes huge pollution to the processing site and the environment, and also seriously affects the health of the operators. In good health. [0003] In order to solve these problems, some progress has been made in the recent research on micro-quantity lubrication technology at home and abroad. The micro-quantity lubrication technology has solved the problems of large amount of lubricant used and serious pollution. Excessive use of sulfur and chlorine-containing lubricants that are not friendly to the environment additive. [0004] Due to the relatively large...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M173/00C10M177/00C10N30/06C10N30/04C10N30/12C10N40/22
CPCC10M173/00C10M177/00C10M2207/021C10M2207/289C10M2207/2895C10M2209/086C10M2219/044
Inventor 张兆平张苗苗张乃庆
Owner 上海贝能环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products