A kind of injectable composite antibacterial hydrogel and preparation method thereof

A composite antibacterial and hydrogel technology, applied in the field of hydrogel, can solve the problems of short antibacterial validity period, unstable antibacterial effect, and easy leakage of antibacterial agents

Active Publication Date: 2021-11-09
CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Most of the above-mentioned hydrogels prepared by using polyvinyl alcohol are cross-linked between molecular chains through chemical cross-linking agents or physical means. This cross-linking method is irreversible. Most of the materials are blended and doped with substances with antibacterial function to endow the material with antibacterial properties. The materials prepared by this method are release-type antibacterial materials, which generally have the disadvantages of easy leakage of antibacterial agents, unstable antibacterial effect, and short antibacterial validity period.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of injectable composite antibacterial hydrogel and preparation method thereof
  • A kind of injectable composite antibacterial hydrogel and preparation method thereof
  • A kind of injectable composite antibacterial hydrogel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The invention provides a preparation method of an injectable composite antibacterial hydrogel, comprising the following steps:

[0023] In the presence of a catalyst, the carboxylated polyvinyl alcohol (C-PVA) solution is adjusted to a pH value of 3 to 4 and then reacted with ε-polylysine (EPL) to obtain an amino-modified polyvinyl alcohol solution (CPVA-g- EPL);

[0024] Blending the chitosan (CS) solution, the dextran formaldehyde solution and the amino-modified polyvinyl alcohol solution to obtain an injectable composite antibacterial hydrogel;

[0025] The mass ratio of amino-modified polyvinyl alcohol, chitosan and glucan is 4-1:1:0.05-0.5.

[0026] The method provided by the invention adopts amino-modified polyvinyl alcohol with antibacterial function, and after blending with chitosan, utilizes the amino groups on the molecular chains of the two and the aldehyde groups on the molecular chains of dextran to form a dynamic Schiff base bond , so that the prepared h...

Embodiment 1

[0043] Take 20mL of refined vinyl acetate and add it to 40mL of methanol, pass nitrogen gas to remove oxygen for 30min, then add 0.02gAIBN, 3mL acrylic acid, react at 65°C for 8h, the product is precipitated in deionized water, and the product is named P(VAc-co -AA); Then configuration mass percent is 25% P (VAc-co-AA) methanol solution, add an appropriate amount of 1mol / L sodium hydroxide methanol solution at normal temperature, make the mass of NaOH and P (VAc-co-AA) When the ratio reaches 0.02, after mixing evenly, carry out alcoholysis reaction in a constant temperature water bath at 50°C for 30 minutes to obtain a colloidal product, heat and dissolve the colloidal product with deionized water, filter to remove insoluble impurities, cool to room temperature, and use methanol as a precipitant to precipitate 3 times , filtered, and dried to obtain carboxylated polyvinyl alcohol (C-PVA).

[0044] Add 10mL of deionized water to a 100mL two-necked flask, add 1g of C-PVA, add an...

Embodiment 2

[0053] The experimental steps for preparing carboxylated polyvinyl alcohol (C-PVA), amino acid modified polyvinyl alcohol (CPVA-g-EPL-1) and dextran formaldehyde (ODEX) are the same as in Example 1.

[0054] Take 0.7mL CPVA-g-EPL-1 solution with a mass percentage of 10%, add 1.4mL chitosan solution with a mass percentage of 2.5% and 200μL ODEX solution with a mass percentage of 6%, and mix well at room temperature to prepare a hydrogel Glue, the product number is S2. Antibacterial test results show that the antibacterial rate of S2 against Escherichia coli is 99.96%, and the antibacterial rate against Staphylococcus aureus is 99.98%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention provides an injectable composite antibacterial hydrogel and a preparation method thereof. The method comprises: adjusting the pH value of a carboxylated polyvinyl alcohol solution to 3-4 in the presence of a catalyst, and then reacting with ε-polylysine. Amino-modified polyvinyl alcohol solution is obtained; chitosan solution, glucan solution and the amino-modified polyvinyl alcohol solution are blended to obtain an injectable composite antibacterial hydrogel; amino-modified polyvinyl alcohol , The mass ratio of chitosan and glucan is 4-1:1:0.05-0.5. The method adopts amino-modified polyvinyl alcohol with antibacterial function, and after blending with chitosan, utilizes the amino group on the molecular chain of the two and the aldehyde group on the molecular chain of aldodextran to construct a dynamic Schiff base bond, so that the water The gel has reversible crosslinkability and is an intrinsically antibacterial material. It also has a high antibacterial rate. The highest bacteriostatic rate of the hydrogel prepared in the embodiment of the present invention to Escherichia coli and Staphylococcus aureus both reached 99.99%.

Description

technical field [0001] The invention belongs to the field of hydrogel technology, and in particular relates to an injectable composite antibacterial hydrogel and a preparation method thereof. Background technique [0002] Hydrogel is a cross-linked body composed of natural or synthetic polymers and a certain amount of water. It not only has excellent water absorption, but also has certain elasticity and excellent biocompatibility. It can be used in tissue engineering, drug carriers and cell culture. and other fields (Y.Hao, J.L.He, X.Ma et al, A fully degradable and photo crosslinked polysaccharide-polyphosphate hydrogel for tissue engineering, Carbohydrate Polymers 225(2019) 115257). As a wound dressing, hydrogel should have certain antibacterial properties, because severe wound infection caused by bacteria can lead to sepsis, increasing the risk of amputation and death (P.G.Bowler, Woundpathophysiology, infection and therapeutic options, Ann.Med, 34(2002 ), 419-427.). Ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/075C08J3/24C08L87/00C08L5/08C08L5/02C08G81/02
CPCC08G81/024C08J3/075C08J3/246C08J2387/00C08J2405/02C08J2405/08
Inventor 杨旭姬相玲许玖多王宝龙沙迪石凯
Owner CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap