A kind of environmental protection diatom mud and preparation method thereof

A diatom mud and environmental protection technology, applied in the field of decorative materials, can solve the problems of low wear resistance, insufficient hardness, and the effect of moisture absorption and dehumidification needs to be further improved, so as to achieve excellent wear resistance, long service life and low preparation cost. Effect

Active Publication Date: 2022-03-29
浙江蓝天知识产权运营管理有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of diatom mud still has low wear resistance, insufficient hardness, and the moisture absorption and release effect needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An environmentally friendly diatom mud is characterized in that it is composed of the following components in parts by weight: 30 parts of modified diatomite, 0.5 parts of black phosphorus quantum dots, 8 parts of palygorskite powder, 6 parts of illite powder, surface 10 parts of modified Ti-Nd-O, 0.3 parts of hydroxypropyl methylcellulose, 3 parts of sodium polyacrylate superabsorbent resin, and 25 parts of water.

[0032] The preparation method of the surface modified Ti-Nd-O comprises the following steps:

[0033] ⅠAdd chemically pure titanium chloride and rubidium nitrate to ethanol, stir ultrasonically for 0.5h, then slowly add sodium acetate, and stir vigorously for 1h, then transfer the solution to a polyvinyl fluoride-lined hydrothermal reaction kettle, Reaction at 180°C for 15h. Take out the reaction kettle, wash the reaction system repeatedly with deionized water and absolute ethanol after cooling, and finally dry it in a vacuum oven at 70°C for 18 hours, the...

Embodiment 2

[0040] An environmentally friendly diatom mud is characterized in that it is composed of the following components in parts by weight: 35 parts of modified diatomite, 1 part of black phosphorus quantum dots, 9 parts of palygorskite powder, 6.5 parts of illite powder, surface 12 parts of modified Ti-Nd-O, 0.4 parts of polyvinyl alcohol, 4 parts of starch-grafted acrylate superabsorbent resin, and 27 parts of water.

[0041] The preparation method of the surface modified Ti-Nd-O comprises the following steps:

[0042] ⅠAdd chemically pure titanium nitrate and rubidium sulfate to ethanol, stir ultrasonically for 0.7h, then slowly add sodium acetate, and stir vigorously for 1.2h, transfer the solution to a polyvinyl fluoride-lined hydrothermal reaction kettle, Reaction at 190°C for 17h. Take out the reaction kettle, wash the reaction system repeatedly with deionized water and absolute ethanol after cooling, and finally dry it in a vacuum oven at 73°C for 20 hours, then burn it in ...

Embodiment 3

[0049] An environmentally friendly diatom mud is characterized in that it is composed of the following components in parts by weight: 40 parts of modified diatomite, 1.5 parts of black phosphorus quantum dots, 10 parts of palygorskite powder, 7 parts of illite powder, surface 15 parts of modified Ti-Nd-O, 0.45 parts of hydroxypropyl methylcellulose, 4.5 parts of cross-linked hydroxyethyl cellulose grafted acrylamide polymer superabsorbent resin, and 30 parts of water.

[0050] The preparation method of the surface modified Ti-Nd-O comprises the following steps:

[0051] Ⅰ Add chemically pure titanium sulfate and rubidium chloride to ethanol, stir ultrasonically for 0.7h, then slowly add sodium acetate, and stir vigorously for 1.5h, then transfer the solution to a polyvinyl fluoride-lined hydrothermal reaction kettle, Reaction at 200°C for 18h. Take out the reaction kettle, wash the reaction system repeatedly with deionized water and absolute ethanol after cooling, and finally...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environmentally friendly diatom mud, which is characterized in that it is composed of the following components in parts by weight: 30-50 parts of modified diatomite, 0.5-2.5 parts of black phosphorus quantum dots, and 8 parts of palygorskite powder ‑12 parts, illite powder 6‑8 parts, surface modification Ti‑Nd‑O 10‑20 parts, dispersant 0.3‑0.6 parts, humidity conditioner 3‑6 parts, water 25‑35 parts. The invention also discloses a preparation method of the environment-friendly diatom mud. The environmentally friendly diatom mud disclosed by the invention has low cost, long service life, safety and fire resistance, good air purification, moisture absorption and dehumidification effects, excellent wear resistance, high hardness, safety and environmental protection in use and preparation process.

Description

technical field [0001] The invention relates to the technical field of decorative materials, in particular to an environment-friendly diatom mud and a preparation method thereof. Background technique [0002] In recent years, with the development of social economy and the improvement of people's living standards, the understanding of environmental issues has gradually deepened, the desire to improve the home environment has become more and more urgent, and the environmental protection of decorative materials has become more and more important. However, artificial boards such as plywood and decorative panels on the market, adhesives such as urea-formaldehyde resin, phenolic resin, and formaldehyde resin, and decorative materials such as various decorative impregnation materials, wall coatings, wallpapers, floors, and chemical fiber carpets are inseparable. Open formaldehyde, the formaldehyde contained in the decorative material itself, and the harmful gases such as formaldehy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B20/02C04B14/30C04B14/36
CPCC04B28/001C04B20/023C04B14/30C04B2111/00482C04B2111/00017C04B2111/00025C04B2111/00827C04B14/08C04B14/36C04B24/383C04B24/2641C04B24/2623C04B24/38
Inventor 闫明亮
Owner 浙江蓝天知识产权运营管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com