Carboxylic acid compound as well as preparation method and application thereof

A compound and carboxylic acid technology, applied in the field of carboxylic acid compounds, can solve the problems of complex operation procedures, environmental pollution, and high process costs

Active Publication Date: 2020-08-28
BOTREE CYCLING SCI & TECH CO LTD
View PDF7 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these extractants also have obvious disadvantages in the separation process: P507/P204 is used for the separation of nickel and cobalt, but in the recovery of lithium-ion battery cathode materials, nickel, cobalt and manganese cannot be extracted simultaneously, and the process cost of recovering nickel, cobalt and manganese separately is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carboxylic acid compound as well as preparation method and application thereof
  • Carboxylic acid compound as well as preparation method and application thereof
  • Carboxylic acid compound as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081]

[0082] Add 50g of isooctyl alcohol, 225mL of tetrahydrofuran (THF), and 8.8g of sodium particles into a three-necked flask, react at 60-70°C for 6 hours, a large amount of white solids are formed, and a small amount of sodium particles remain; L 2-bromooctanoic acid THF solution and continue to react at 60°C for 4h; after cooling, remove THF by rotary evaporation, add 200mL water and 200mL ethyl acetate (EA) to the concentrated solution, shake and separate, take the water layer; Acidify with hydrochloric acid to pH ≈ 1, extract with ethyl acetate, wash the organic phase twice with water, and spin dry to obtain 65 g of a light yellow product, namely compound BC195. 1 H NMR (400MHz, CDCl 3 )δ4.1(1H), 3.52(1H), 3.35(1H), 1.82(2H), 1.54(3H), 1.20-1.31(14H), 0.91(6H), 0.87(3H); 13 C NMR (101MHz, CDCl 3 )δ171(s), 79(s), 72(s), 36(s), 32(s), 29(s), 26-28(m), 22–23(m), 14(s), 11(s); MS[M-H] - :271.

Embodiment 2

[0084]

[0085] Add 28.6g of isooctyl alcohol, 200mL of tetrahydrofuran (THF), 8.8g of 60% sodium hydride (dispersed in mineral oil) into the three-necked flask, and react at 60-70°C for 6 hours, a large amount of white solids are formed, and a small amount of sodium particles remain; Add 20mL of 10mol / L THF solution of 2-bromohexanoic acid dropwise at 60°C and continue to react at 60°C for 4h; after cooling, remove THF by rotary evaporation, add 200mL of water and 200mL of ethyl acetate (EA) to the concentrated solution, shake The layers were separated, and the water layer was taken; the water layer was acidified with hydrochloric acid to pH ≈ 1, extracted with ethyl acetate, the organic phase was washed twice with water, and spin-dried to obtain 38 g of a light yellow product, namely compound BC196. 1 H NMR (400MHz, CDCl 3 )δ3.97(1H), 3.41(1H), 3.26(1H), 1.70(2H), 1.45(3H), 1.05-1.24(10H), 0.91(9H); 13 C NMR (101MHz, CDCl3) δ175(s), 82(s), 76(s), 40(s), 32(s), 30(s), 29(...

Embodiment 3

[0087]

[0088] Add 32g of n-octanol, 200mL of tetrahydrofuran (THF), and 5.7g of sodium particles into a three-necked flask, react at 60-70°C for 6 hours, a large amount of white solids are formed, and a small amount of sodium particles remain; L of THF solution of 2-bromohexanoic acid and continue to react at 60°C for 4 hours; after cooling, remove THF by rotary evaporation, add 200mL water and 200mL ethyl acetate (EA) to the concentrated solution, shake and separate, and take the water layer; the water layer Acidify with hydrochloric acid to pH ≈ 1, extract with ethyl acetate, wash the organic phase twice with water, and spin dry to obtain the target compound, compound BC191.

[0089] Compound BC191 1 H NMR (400MHz, CDCl 3 )δ12.53(1H), 4.01(1H), 3.32(2H), 1.65(2H), 1.20-1.32(16H), 0.89(6H); 13 C NMR (101MHz, CDCl 3 )δ173(s), 81(s), 65(s), 32-30(m), 22–23(m), 14(s); MS[M-H] - :243.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a carboxylic acid compound as well as a preparation method and application thereof. When the carboxylic acid compound is applied to extraction separation of metal ions, the separation coefficient is high, the reverse extraction acidity is low, the load rate is high, and the reverse extraction rate is high. The carboxylic acid compound serving as an extraction agent is highin stability and low in water solubility, so that the extraction process is stable, the environmental pollution can be reduced, and the cost is reduced. The carboxylic acid compound disclosed by the invention is low in cost, has a great application prospect and can be used for various systems such as ternary battery recovery and battery-grade nickel sulfate preparation.

Description

technical field [0001] The invention relates to a carboxylic acid compound, its preparation method and application. Background technique [0002] In recent years, with the rapid development and promotion of electric vehicles, the demand for lithium-ion batteries has also continued to expand. Nickel-cobalt-manganese ternary cathode material has good cycle performance, stable structure, and high cost performance. It is a new type of lithium-ion battery cathode material, and the main raw materials of the precursor product of ternary cathode material are nickel salt, cobalt salt, and manganese salt. [0003] Cobalt is mostly accompanied by nickel, and most of them appear at the same time in minerals, such as in nickel laterite ore. In many industries, waste residues containing valuable metals such as nickel and cobalt will be produced, such as waste power battery materials, waste residues containing nickel and cobalt, waste catalysts, etc. Most of these waste residues also cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C59/125C07C51/367C22B3/32C22B23/00
CPCC07C59/125C22B23/0453C22B3/32Y02P10/20Y02W30/84C07C51/367C22B3/326C22B23/0461C22B47/00
Inventor 王雪
Owner BOTREE CYCLING SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap