Anti-freeze-thaw water-based terrace and construction method thereof

A freeze-thaw-resistant and floor-resistant technology, used in metal-free paints, cellulose coatings, building structures, etc., can solve problems such as floor deformation, floor surface damage, melting, etc., achieving low cost and improved use. performance, the effect of improving crack resistance and impermeability

Inactive Publication Date: 2020-09-08
黄永华
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, during the preparation and construction of the floor, if there is too much moisture remaining in the floor layer, when the temperature drops below zero and rises above zero, the moisture in the floor will freeze and thaw, making The floor is continuously and periodically subjected to stress and deformation, resulting in damage to the floor, especially the surface of the floor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-freeze-thaw water-based terrace and construction method thereof
  • Anti-freeze-thaw water-based terrace and construction method thereof
  • Anti-freeze-thaw water-based terrace and construction method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The invention discloses a freeze-thaw resistant water-based floor, which comprises a concrete floor base and a freeze-thaw resistant layer arranged on the concrete floor base. The raw materials of the freeze-thaw layer include the following components by weight: 57 parts of siloxane , 36 parts of modified silane, 61 parts of water-based varnish, 20 parts of polypropylene glycol diglycidyl ether, 20 parts of o-cresyl glycidyl ether, 25 parts of calcium oxide, 19 parts of volcanic ash, 30 parts of (100 mesh) carbon fiber, ( 90 orders) 25 parts of ramie fibers, 18 parts of fillers, 25 parts of antioxidants.

[0039] The filler includes the following components in parts by weight: 25 parts of polydimethylsiloxane, 22 parts of hydrogenated nitrile rubber, and 15 parts of foamed aluminum powder.

[0040] The water-based glazing oil comprises the following components in parts by weight: 42 parts of water-soluble acrylic resin, 30 parts of water, 6 parts of vinyl bis-stearamide...

Embodiment 2

[0051] The invention discloses a freeze-thaw resistant water-based floor, which comprises a concrete floor base and a freeze-thaw resistant layer arranged on the concrete floor base. The raw materials of the freeze-thaw layer include the following components by weight: 60 parts of siloxane , 40 parts of modified silane, 60 parts of water-based varnish, 22 parts of polypropylene glycol diglycidyl ether, 18 parts of o-cresyl glycidyl ether, 28 parts of calcium oxide, 21 parts of volcanic ash, 28 parts of (110 mesh) carbon fiber, ( 120 orders) 29 parts of ramie fibers, 22 parts of fillers, 23 parts of antioxidants.

[0052] The filler includes the following components in parts by weight: 28 parts of polydimethylsiloxane, 20 parts of hydrogenated nitrile rubber, and 18 parts of foamed aluminum powder.

[0053] The water-based glazing oil comprises the following components in parts by weight: 40 parts of water-soluble acrylic resin, 33 parts of water, 5 parts of vinyl bis-stearamid...

Embodiment 3

[0064] The invention discloses a freeze-thaw-resistant water-based floor, which comprises a concrete floor base and a freeze-thaw-resistant layer arranged on the concrete floor base. The raw materials of the freeze-thaw layer include the following components by weight: 67 parts of siloxane , 40 parts of modified silane, 65 parts of water-based varnish, 28 parts of polypropylene glycol diglycidyl ether, 20 parts of o-cresyl glycidyl ether, 32 parts of calcium oxide, 30 parts of volcanic ash, 36 parts of (150 mesh) carbon fiber, ( 160 orders) 29 parts of ramie fibers, 26 parts of fillers, 25 parts of antioxidants.

[0065] The filler includes the following components in parts by weight: 30 parts of polydimethylsiloxane, 26 parts of hydrogenated nitrile rubber, and 19 parts of foamed aluminum powder.

[0066] The water-based glazing oil comprises the following components in parts by weight: 54 parts of water-soluble acrylic resin, 59 parts of water, 7 parts of vinyl bis-stearamid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-freeze-thaw water-based terrace and a construction method thereof. According to the technical key points, the anti-freeze-thaw water-based terrace comprises a concreteterrace base layer and an anti-freeze-thaw layer arranged on the concrete terrace base layer, the anti-freeze-thaw layer comprises the following raw materials by weight: 57-85 parts of siloxane, 36-48parts of modified silane, 60-78 parts of water-based varnish, 20-35 parts of polypropylene glycol diglycidyl ether, 18-33 parts of o-tolyl glycidyl ether, 25-36 parts of calcium oxide, 19-36 parts ofvolcanic ash, 28-45 parts of carbon fiber, 25-36 parts of ramie fiber, 18-35 parts of filler and 23-35 parts of an antioxidant. The anti-freeze-thaw layer paint prepared by the preparation method disclosed by the invention has low moisture, compact texture and strong shrinkage stress bearing capacity, so that the terrace has excellent anti-freeze-thaw performance, and the preparation and construction processes are very simple and convenient.

Description

technical field [0001] The invention relates to the field of concrete floors, more specifically, it relates to a freeze-thaw resistant water-based floor and a construction method thereof. Background technique [0002] Concrete wear-resistant floor, commonly known as emery floor; the mineral alloy aggregate ground hardener is composed of mineral alloy aggregate with a certain particle size distribution, special cement, other admixtures and admixtures, which are evenly spread on the upcoming The concrete surface in the initial setting stage is processed by special means, so that it can form a whole with the concrete ground, and has a high-performance wear-resistant ground with high density and coloring. [0003] The existing application publication number is the Chinese patent of CN110256007A, discloses a kind of concrete wear-resistant floor and its construction method, and its concrete wear-resistant floor includes a concrete base and a wear-resistant floor, and the concrete...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D133/04C09D101/02C09D7/20C09D7/61C09D7/63C09D7/65C09D5/38E04F15/12E04F15/18C04B26/32
CPCC04B26/32C08K2003/2206C08L2205/035C08L2205/16C09D5/38C09D183/04C09D7/20C09D7/61C09D7/63C09D7/65C09D7/70E04F15/12E04F15/181C08L33/04C08L1/02C08K13/04C08K7/06C08K3/00C08K3/22C08K5/20C04B24/32C04B24/023C04B22/064C04B14/14C04B14/386C04B18/265C04B24/2641C04B24/124C04B24/00C04B24/04C04B22/06C04B22/04C04B24/24C04B14/02
Inventor 黄永华
Owner 黄永华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap