A composite durable antistatic non-bitumen-based self-adhesive gas isolation board and its preparation method

A non-asphalt-based, antistatic technology, applied in the direction of adhesives, adhesive types, adhesive additives, etc., can solve the problems of size change, gas leakage, etc., and achieve the advantages of improving strength, prolonging the life of the sheet, and increasing the weather resistance Effect

Active Publication Date: 2022-04-15
SICHUAN WEIDUN JIANGXIN CONSTR CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a composite durable antistatic non-bitumen-based self-adhesive gas insulation board and its preparation method to solve the problem that the gas insulation board in the prior art is a hard plastic board due to the long-term high and low temperature in the use environment. Changes, there are dimensional changes, which lead to technical problems of gas leakage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite durable antistatic non-bitumen-based self-adhesive gas isolation board and its preparation method
  • A composite durable antistatic non-bitumen-based self-adhesive gas isolation board and its preparation method
  • A composite durable antistatic non-bitumen-based self-adhesive gas isolation board and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0128] S1. Preparation of polymer waterproof board:

[0129] ①Raw materials, as shown in Table 1 below:

[0130] Table 1 embodiment 1 prepares the raw material that polymer waterproof board adopts

[0131]

[0132] ②Preparation method:

[0133] A1. Raw material premixing: Inhale all raw materials into the high-mixer through the vacuum pump according to the ratio, and dry them in the high-mixer at a temperature of 53°C, and the mixing time is 3 minutes, and then put them into the low-mixer for 5 minutes. , the raw materials are mixed evenly;

[0134] A2. Extrusion molding: The raw materials mixed uniformly in step A1 are transported into the twin-screw extruder through the twin-screw conveyor, and the polymer waterproof board is extruded through the extrusion temperature of 220°C-240°C, and then passed through three Cool to normal temperature after the roll forming machine is thickened and formed;

[0135]A3. Internal stress treatment: The polymer waterproof board formed...

Embodiment 2

[0154] S1. Preparation of polymer waterproof board:

[0155] ① Raw materials, as shown in Table 3 below:

[0156] Table 3 embodiment 2 prepares the raw material that polymer waterproof board adopts

[0157]

[0158] ②Preparation method:

[0159] A1. Raw material premixing: Inhale all the raw materials into the high mixer through the vacuum pump according to the ratio, and then dry them in the high mixer at a temperature of 50°C, and the mixing time is 2 minutes, and then put them into the low mixer for 6 minutes. , the raw materials are mixed evenly;

[0160] A2. Extrusion molding: The raw materials mixed uniformly in step A1 are transported into the twin-screw extruder through the twin-screw conveyor, and the polymer waterproof board is extruded through the extrusion temperature of 220°C-240°C, and then passed through three Cool to normal temperature after forming by roller forming machine to set thickness (2.0mm);

[0161] A3. Internal stress treatment: The polymer wa...

Embodiment 3

[0180] S1. Preparation of polymer waterproof board:

[0181] ① Raw materials, as shown in Table 5 below:

[0182] Table 5 embodiment 3 prepares the raw material that polymer waterproof board adopts

[0183]

[0184] ②Preparation method:

[0185] A1. Raw material premixing: Inhale all raw materials into the high-mixer through the vacuum pump according to the ratio, and dry them in the high-mixer at a temperature of 55°C, and the mixing time is 4 minutes, and then put them into the low-mixer for 4 minutes. , the raw materials are mixed evenly;

[0186] A2. Extrusion molding: The raw materials mixed uniformly in step A1 are transported into the twin-screw extruder through the twin-screw conveyor, and the polymer waterproof board is extruded through the extrusion temperature of 220°C-240°C, and then passed through three Cool to normal temperature after forming by roller forming machine to set thickness (2.0mm);

[0187] A3. Internal stress treatment: The polymer waterproof ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The present invention provides a composite durable antistatic non-asphalt-based self-adhesive gas insulation board and its preparation method, which solves the problem that the gas insulation board in the prior art is a hard plastic board due to long-term high and low temperature changes in the use environment. It has the phenomenon of dimensional change, which leads to the technical problem of gas leakage. It includes a polymer waterproof board layer, a self-adhesive material layer and a polyurethane coating layer; the polymer waterproof board layer is the bottom layer, the self-adhesive material layer is covered on the polymer waterproof board layer, and the polyurethane The paint layer is the surface layer. The invention forms a composite weather-resistant and antistatic non-asphalt-based self-adhesive gas isolation board for gas tunnels through the compounding of polymer waterproof board layer, self-adhesive rubber material layer and polyurethane coating layer, thereby effectively preparing an excellent Mechanical properties, good flexibility, weather resistance, excellent gas insulation performance, excellent flame retardancy and antistatic properties, and easy construction and transportation of gas insulation panels.

Description

technical field [0001] The invention relates to a gas isolation board, in particular to a composite durable antistatic non-asphalt-based self-adhesive gas isolation board and a preparation method thereof. Background technique [0002] The anti-gas and waterproof isolation projects of tunnels in my country mainly need to meet gas barrier properties, flame retardancy, antistatic properties and excellent mechanical properties. Most of the gas barrier panels currently in use have poor gas barrier properties, are not antistatic, and are hard Due to the long-term high and low temperature changes in the use environment, there are dimensional changes in the plastic sheet, which leads to gas insulation performance defects; because of the long-term harsh use environment, the material has performance attenuation, and due to the lack of flexibility of the material, It is not easy to fold, which also causes some troubles for road transportation, and has the disadvantage of poor constructio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/24C09J7/30C09J157/02C09J153/02C09J11/06C09J11/08C08L23/08C08L77/02C08L51/06C08K5/00C08K5/3492C09D175/04C09D5/08
CPCC09J7/241C09J7/30C09J157/02C09J11/06C09J11/08C08L23/0815C08L77/02C08L23/0846C09D175/04C09D5/08C08L2205/035C08L2207/062C08L2205/08C08L2201/14C08L2201/02C08L2201/04C08L2205/025C09J2423/04C09J2477/006C08L51/06C08K5/00C08K5/34928C08L57/02C08L53/02C08L23/22
Inventor 刘勇曹潇尹楚珑晟袁志涛李雷郑贤方
Owner SICHUAN WEIDUN JIANGXIN CONSTR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap