A preparation method for preparing medium and low pressure composite medium-containing film into foil by surface self-assembly method

A technology of composite dielectric film and self-assembly method, which is applied in the direction of capacitor dielectric layer, electrolytic capacitor manufacturing, capacitors, etc., to achieve the effects of reducing production costs, easy operation, and high specific capacitance

Active Publication Date: 2021-11-26
GUANGXI UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

in Al 2 o 3 / TiO 2 Hydrolytic deposition of TiO on the surface of aluminum foil in composite film 2 The amount of deposition is the key factor to determine the specific capacity of aluminum foil, although the hydrolytic deposition method and sol-gel method have effectively improved the specific capacity of aluminum foil, but TiO 2 The amount of deposition can still be further increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Dissolve γ-mercaptopropyltrimethoxysilane in cyclohexane to make a solution with a concentration of 5mmol / L. Put the corroded foil into this solution and soak it for 5h, then take it out and dry it in the air. After that, put the dried aluminum foil into a solution made of acetic acid and 30% hydrogen peroxide at a volume ratio of 5:1 and soak for 1 hour. After soaking, take it out and dry it in the air. Then put the dried aluminum foil into butyl titanate and acetic acid and mix it at a molar ratio of 1:6, add deionized water dropwise until the concentration of Ti is 0.3mol / L and soak in the sol for 5h. After soaking, take it out and dry it in the air, then put it into a muffle furnace for heat treatment at 500°C for 2min. Put the heat-treated aluminum foil into the six-stage chemical conversion solution prepared by ammonium adipate and deionized water at room temperature in turn, with conductivity of 43, 37, 50, 46, 52, and 48 mS / cm, and heat the chemical conversion s...

Embodiment 2

[0026] Dissolve γ-mercaptopropyltrimethoxysilane in cyclohexane to make a solution with a concentration of 7mmol / L. Put the corroded foil in this solution and soak it for 5h, then take it out and dry it in the air. After that, put the dried aluminum foil into a solution made of acetic acid and 30% hydrogen peroxide at a volume ratio of 5:1 and soak for 1 hour. After soaking, take it out and dry it in the air. Then put the dried aluminum foil into butyl titanate and acetic acid to mix at a molar ratio of 1:6, add deionized water dropwise until the concentration of Ti is 0.8mol / L and soak in the sol for 8h. After soaking, take it out and dry it in the air, and put it into a muffle furnace for heat treatment at 500°C for 5 minutes. Put the heat-treated aluminum foil into the six-stage chemical conversion solution prepared by ammonium adipate and deionized water at room temperature in turn, with conductivity of 43, 37, 50, 46, 52, and 48 mS / cm, and heat the chemical conversion sol...

Embodiment 3

[0028] Dissolve γ-mercaptopropyltrimethoxysilane in cyclohexane to make a solution with a concentration of 10mmol / L. Put the corroded foil into this solution and soak it for 5h, then take it out and dry it in the air. After that, put the dried aluminum foil into a solution made of acetic acid and 30% hydrogen peroxide at a volume ratio of 5:1 and soak for 1 hour. After soaking, take it out and dry it in the air. Then put the dried aluminum foil into butyl titanate and acetic acid and mix it at a molar ratio of 1:6, add deionized water dropwise until the concentration of Ti is 0.6mol / L and soak in the sol for 10h. After soaking, take it out and dry it in the air, then put it in a muffle furnace for heat treatment at 500°C for 5 minutes, put the heat-treated aluminum foil in turn at room temperature, and prepare the conductivity of 43, 37, 50, 46, 52, 48mS / cm six grades of formation liquid, heating the formation liquid at 85°C, at a current density of 0.1A / cm 2 , the voltage is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
electrical conductivityaaaaaaaaaa
electrical conductivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for preparing medium-low pressure compound medium-containing film forming foil by surface self-assembly method. In the method, the low-pressure corroded foil is used as a raw material, and the surface of the aluminum foil is modified by a soaking method. Soak the corroded foil in the solution of 5~10mmol / L γ-mercaptopropyltrimethoxysilane and cyclohexane as solvent for 5 h, CH 3 COOH / H 2 o 2 (Vol)=5:1 solution for 1 h, 0.3~0.8mol / L Ti gel soaked for 5~10 h. Heat treatment at 500°C for 5 min after drying. After that, the aluminum foil is anodized, and ammonium adipate and ammonium citrate are used as solutes to prepare a chemical solution, according to the current density of 0.1~0.3A / cm 2 , and the voltage ranged from 12 V to 141 V to perform six-level gradient formation on the modified aluminum foil. The aluminum foil is then subjected to intermediate treatment, re-formation, heat treatment, and post-treatment operations in sequence, and finally a high specific volume medium-low pressure compound dielectric film-containing foil is obtained. The advantages of the present invention are: simple process, convenient operation; TiO 2 The amount of deposition on the surface of the aluminum foil is large, and the specific volume of the aluminum foil made is high.

Description

technical field [0001] The invention relates to the field of surface modification of aluminum foil, in particular to a method for preparing medium and low pressure composite medium-containing films into foils by means of a surface self-assembly method. Background technique [0002] In the family of electrolytic capacitors, aluminum electrolytic capacitors have been greatly developed in the world in the past 20 years due to their superior performance, low price and wide range of uses. [0003] With the continuous development of electronic products in the direction of intelligence and miniaturization, the structure of the circuit system is becoming more and more complex, and there are more and more electronic components per unit area. Aluminum electrolytic capacitors are the basic electronic components in the circuit system. It is widely used in communication equipment, mobile office, audio-visual system, household appliances, aerospace and other fields. [0004] According to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/00H01G9/055H01G9/07
CPCH01G9/0032H01G9/055
Inventor 秦祖赠徐毅远苏通明王文宝欧永聪谢新玲王灿宇罗轩
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap