Coating system with reinforced concrete pursuit performance, and anti-corrosion application of coating system

A reinforced concrete, follow-up technology, used in coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve problems such as lack of engineering practice applications

Active Publication Date: 2020-10-20
INST OF OCEANOLOGY - CHINESE ACAD OF SCI
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the research on these toughened epoxy resins is seldom aimed at concrete protective coatings, and there is even less engineering practice in this field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating system with reinforced concrete pursuit performance, and anti-corrosion application of coating system
  • Coating system with reinforced concrete pursuit performance, and anti-corrosion application of coating system
  • Coating system with reinforced concrete pursuit performance, and anti-corrosion application of coating system

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0081] The composition of the main agent and curing agent of the penetrating epoxy resin sealing primer of Example 1-3 of the present invention is shown in Table 1 and Table 2.

[0082] Table 1 Primer main agent formula composition

[0083]

[0084] The epoxy resin toughening agent in Table 1 is the polymer long-chain polyol compound YM-004.

[0085] Primer main agent preparation: put hydrogenated bisphenol A type epoxy resin, small molecular polyether type epoxy resin, silicone rubber modified epoxy resin, epoxy resin toughener and solvent into the dispersion stirring tank according to the raw material formula , Stir evenly and discharge.

[0086] Table 2 Primer curing agent formula composition

[0087]

[0088] The coupling agent in Table 2 is diethylaminomethyltriethoxysilane.

[0089] Preparation of primer curing agent: put polyetheramine curing agent D-230, 1-butyl-3-methylchloroimidazole, diethylaminomethyltriethoxysilane and isobutanol into the Disperse in the...

Embodiment 4-6

[0097] The composition of the solvent-free epoxy putty formulation main agent and curing agent in Examples 4-6 of the present invention is shown in Table 4 and Table 5.

[0098] Table 4 Putty main agent formula composition

[0099]

[0100] The epoxy resin putty filling glue, diluent and organic bentonite in Table 4 are the epoxy resin putty filling glue, dimethyl glycidyl ether of Germany WEICON Company and the product 881-B of Zhejiang Qinghong New Material Co., Ltd. respectively.

[0101] Preparation of putty main agent: Add epoxy resin putty filling glue into the container, add diluent, stir for 15 minutes, control the speed at 300r / min, then add titanium dioxide, light calcium hydrochloride, heavy calcium carbonate, organic bentonite, talc in sequence Powder, each kind needs to be stirred for 10 minutes after adding, and the speed is controlled at 1000r / min. After all are added, stir for another 25 minutes.

[0102] Table 5 putty curing agent formula composition

[0...

Embodiment 7-9

[0113] Table 7 shows the modified main agent of the modified high-ductility anti-corrosion intermediate paint formula in Examples 7-9 of the present invention.

[0114] Formulation composition of main agent of modified high ductility anticorrosion intermediate paint in Table 7

[0115]

[0116] The fumed silica, dispersant and defoamer in Table 7 are product A-200 from Degussa, Disperbyk103 from BYK and BYK-052 from BYK.

[0117] Preparation of polyether-modified epoxy resin in modified main agent of intermediate paint:

[0118] Step ①, under the protection of nitrogen, vacuum dehydrate 600g of polyether polyol (PPG) N-210 for 40min, slowly add 190g of toluene diisocyanate (TDI) dropwise, control the temperature at 80°C, and perform an addition reaction for 2h to obtain terminal Isocyanate prepolymers.

[0119] Step 2. After uniformly mixing the 240g terminal isocyanate prepolymer obtained above with 560g epoxy acrylic resin (3:7 mass ratio), add 0.8g of trimethylolpropan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of buildings, in particular to a coating system with reinforced concrete pursuit performance, and anti-corrosion application of the coating system, and more particularly relates to coating protection application of a concrete structure of ocean engineering. A coating sequentially comprises permeable epoxy resin seal primer, solvent-free epoxy resin putty, polyether-modified epoxy resin high-tenacity intermediate coat and elastic polyurethane top coat. The anti-corrosion application of the coating with the reinforced concrete surface pursuit performance is completed through six processes; and the coating with the reinforced concrete pursuit performance not only has excellent mechanical properties such as the good pursuit performance, high tensilestrength and matrix cracking prevention, but also has excellent protection properties of alkali resistance, aging resistance and chloride ion penetration resistance, the characteristics of short period and easy operation are achieved in the construction process, and a method is an effective method convenient to implement on site and capable of prolonging the life of the concrete structure.

Description

technical field [0001] The invention relates to the technical field of construction, in particular to a reinforced concrete crack-following coating system and its anti-corrosion application, and more particularly to the coating protection application of marine engineering concrete structures. Background technique [0002] Concrete is an inorganic material composed of cement, sand and admixtures. It is hard and wear-resistant. It is currently the most widely used structural material in the world. With the rapid development of my country's marine engineering construction, reinforced concrete structures are widely used in various coastal buildings, such as docks, cross-sea bridges, submarine tunnels and other large buildings are mainly reinforced concrete structures. [0003] In the marine environment, the exposed concrete structure surface is corroded by seawater immersion, alternating wet and dry, sunlight exposure, coastal salt spray, marine organisms and humid air for a lon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04G23/02E04B1/64E04B1/66C09D163/00C09D163/10C09D175/08C09D175/06C09D5/00C09D5/34C09D5/08C09D7/61C09D7/20C08G18/42C08G18/62C08G18/58C08G18/64
CPCE04G23/02E04G23/0203E04B1/66C09D163/00C09D163/10C09D175/06C09D5/002C09D5/34C09D5/08C09D7/61C09D7/20C08G18/4081C08G18/42C08G18/6216C08G18/58C08G18/6415C08L2205/03C08L2205/025C08L2201/08C08L2312/00C08L2205/04C08L63/00C08L75/08C08K3/34C08K3/36C08K13/02C08K5/13
Inventor 马秀敏孙丛涛侯保荣
Owner INST OF OCEANOLOGY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com