EVA edge-sealing hot melt adhesive with no adhesive line and low adhesive coating amount and preparation method of EVA edge-sealing hot melt adhesive
A technology of glue coating amount and hot melt adhesive, which is used in adhesives, photovoltaic power generation, adhesive additives, etc., can solve the problems of affecting the appearance of furniture, lowering the grade of furniture, inconsistent color of edge banding, etc., achieving light weight and reducing glue coating. Good quantity and bonding strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0063] A second aspect of the invention provides a method of preparing a wireless, low-glue amount of EVA blocking thermal melt glue, the preparation method comprising the steps of:
[0064] The viscosity modifier, ethylene-vinyl acetate copolymer, heating, when the temperature is 80-110 ° C, until the above feedstock is completely dissolved; the anti-oxygen-maintaining material temperature is 130-160 ° C until dissolution is uniform, add tackifying resin, petroleum resin, and fillers are mixed well, and then remove 30-50 min after completion of the raw material, then cool to 125-150 ° C, which is obtained.
[0065] In a preferred embodiment, the non-rubber, low-glued amount of EVA blocking thermal melt adhesive, including the following steps:
[0066] The viscosity modifier, ethylene-vinyl acetate copolymer, heating, when the temperature is 90 ° C, until the above feedstock is completely dissolved, and the antioxidant maintains the material temperature at 150 ° C until dissolved ...
Example Embodiment
[0071] Example 1
[0072] Provides a rubber, low-glued EVA blocking hot melt glue, according to weight, prepared materials including: ethylene-vinyl acetate copolymer 36 parts, oil resin, 6 tackifier resins, viscosity Seven parts of regulators, 30 fillers, 0.03 antioxidants.
[0073] The ethylene-vinyl acetate copolymer can be obtained by commercially available, and the grades are 25% by weight of DuPont 4455, vinyl acetate.
[0074] The petroleum resin is a C5 hydrodermic oil resin.
[0075] The tackifying resin is a rosin resin.
[0076] The viscosity modifier is a polyethylene wax, which can be obtained by commercially available, and the manufacturer is Ninghai Boy Chemical Co., Ltd., the number BR-1.
[0077] The filler is a combination of calcium carbonate and titanium white powder in which the mass ratio of calcium carbonate and titanium white powder is 3: 1.
[0078] The preparation method of the preparation method of EVA blocking thermal melt adhesive, the preparation met...
Example Embodiment
[0080] Example 2
[0081]Provides a rubber, low-glued EVA blocking hot melt glue, preparation of raw materials, 25 parts of ethylene-vinyl acetate, 15 parts of petroleum resin, 2 parts of oil resin, 2 parts, viscosity There were 5 regulators, 20 fillers, and 0.01 antioxidants.
[0082] The ethylene-vinyl acetate copolymer can be obtained by commercially available, and the grades are 25% by weight of DuPont 4455, vinyl acetate.
[0083] The petroleum resin is a C5 hydrodermic oil resin.
[0084] The tackifying resin is a rosin resin.
[0085] The viscosity modifier is a polyethylene wax, which can be obtained by commercially available, and the manufacturer is Ninghai Boy Chemical Co., Ltd., the number BR-1.
[0086] The filler is a combination of calcium carbonate and titanium white powder in which the mass ratio of calcium carbonate and titanium white powder is 3: 1.
[0087] The preparation method of the preparation method of EVA blocking thermal melt adhesive, the preparation m...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap