Nano titanium dioxide-doped water-based paint with sterilization function and production process thereof

A technology of nano-titanium dioxide and water-based coatings, applied in the field of coatings, can solve problems such as bacterial metabolic disorders, protein structure destruction, and death, and achieve the effects of strong negative ion release, strong photocatalytic performance, and rapid bacterial death

Pending Publication Date: 2020-12-18
安徽喜尔奇日用品有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Silver ions have a strong bactericidal ability, but when they come into contact with bacteria, silver ions quickly...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A water-based coating with bactericidal function doped with nano-titanium dioxide is made of the following raw materials in weight percentage: 27% of water-based acrylate emulsion (Tg is 27°C), 3% of iron-doped nano-titanium dioxide, and 1% of cerium-doped nano-titanium dioxide %, silver-loaded tourmaline powder 3%, rectorite fine powder 8%, aluminum citrate 0.8%, silane coupling agent KH550 0.5%, ethanol 8%, and the balance is water.

[0029] The preparation method of silver-loaded tourmaline powder is:

[0030] (1) select particle diameter to be the tourmaline powder of 1-50 micron, standby; Prepare silver nitrate aqueous solution, the concentration of silver nitrate aqueous solution is 1mol / L;

[0031] (2) Add tourmaline powder to silver nitrate aqueous solution, so that the mass ratio of silver nitrate to tourmaline powder is 1:16.

[0032] (3) Stir at high speed for 2 hours at room temperature, and then spray dry to obtain silver-loaded tourmaline powder.

[0033...

Embodiment 2

[0036] A water-based coating with bactericidal function doped with nano-titanium dioxide is made of the following raw materials in weight percentage: 32% of water-based acrylate emulsion (Tg is 20°C), 1% of iron-doped nano-titanium dioxide, 1.5% of cerium-doped nano-titanium dioxide %, silver-loaded tourmaline powder 2%, rectorite fine powder 6%, aluminum citrate 0.6%, silane coupling agent KH570 0.2%, ethanol or ethylene glycol 10%, and the balance is water.

[0037] The preparation method of silver-loaded tourmaline powder is:

[0038] (1) select particle diameter to be the tourmaline powder of 1-50 micron, standby; Prepare silver nitrate aqueous solution, the concentration of silver nitrate aqueous solution is 0.5mol / L;

[0039] (2) Add tourmaline powder to the silver nitrate aqueous solution so that the mass ratio of silver nitrate to tourmaline powder is 1:10.

[0040] (3) Stir at high speed for 1 hour at room temperature, and then spray dry to obtain silver-loaded tourm...

Embodiment 3

[0044] A water-based coating with bactericidal function doped with nano-titanium dioxide is made of the following raw materials in weight percentage: 20% of water-based acrylate emulsion (Tg is 30°C), 1.8% of iron-doped nano-titanium dioxide, 0.5% of cerium-doped nano-titanium dioxide %, silver-loaded tourmaline powder 2%, rectorite fine powder 12%, aluminum citrate 0.5%, silane coupling agent KH550 0.3%, ethanol or ethylene glycol 6%, and the balance is water.

[0045] The preparation method of silver-loaded tourmaline powder is:

[0046] (1) select particle diameter to be the tourmaline powder of 1-50 micron, for subsequent use; Prepare silver nitrate aqueous solution, the concentration of silver nitrate aqueous solution is 1.5mol / L;

[0047] (2) Add tourmaline powder to the silver nitrate aqueous solution so that the mass ratio of silver nitrate to tourmaline powder is 1:20.

[0048] (3) Stir at high speed for 1.5 hours at room temperature, and then spray dry to obtain sil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a nano titanium dioxide-doped water-based paint with a sterilization function and a production process thereof. The water-based paint is prepared from the following raw materials in percentage by weight: 20-32% of water-based acrylate emulsion, 1-3% of iron-doped nano titanium dioxide, 0.5-1.5% of cerium-doped nano titanium dioxide, 2-5% of silver-loaded tourmaline powder, 6-12% of rectorite micro powder, 0.5-0.8% of aluminum citrate, 0.2-0.5% of silane coupling agent, 6-10% of alcohol solvent and the balance of water. The coating produced by the method is smooth in appearance, high in adhesive force and high in strength, and has excellent air purification performance and antibacterial performance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based coating with bactericidal function doped with nano-titanium dioxide and a production process. Background technique [0002] With the development of science and technology, the improvement of living standards and the use of various chemical and chemical products, some air pollution will occur in some places in people's lives. Air pollution is mainly caused by dust, bacteria, and poisonous gases. Especially in some closed environments, such as bathrooms, cars, bedrooms, etc., the air quality is worse. Tests have proved that the odor in life is mainly caused by the metabolism of humans or animals, as well as smoke, insecticides, cleaning agents, sewage, feces, industrial gases, oil washing, adhesives, etc. Distributed various substances such as: ammonia, formaldehyde, hydrogen sulfide, methyl mercaptan and other components. [0003] With the introduction of various...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D5/14C09D7/61C09D7/63
CPCC08K2003/2241C08K2201/011C09D5/14C09D133/04C09D7/61C09D7/63C08K13/06C08K9/12C08K3/28C08K3/38C08K3/22C08K3/346C08K9/06C08K5/098
Inventor 胡冰
Owner 安徽喜尔奇日用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap