Preparation process for polypropylene composite film based on bio-based wheat straw

A technology of composite film and wheat straw, which is applied in the field of preparation process of polypropylene composite film based on bio-based wheat straw, can solve the problem of low preparation efficiency

Active Publication Date: 2020-12-25
瑞年科技(广东)有限公司
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Therefore, the present invention provides a preparation process based on bio-based wheat straw polypropylene composite film to overcome the problem of l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process for polypropylene composite film based on bio-based wheat straw
  • Preparation process for polypropylene composite film based on bio-based wheat straw

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0058]In order to make the purpose and advantages of the present invention clearer, the following further describes the present invention in conjunction with the embodiments; it should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0059]The preferred embodiments of the present invention will be described below with reference to the drawings. Those skilled in the art should understand that these embodiments are only used to explain the technical principles of the present invention, and are not intended to limit the protection scope of the present invention.

[0060]It should be noted that in the description of the present invention, the terms "upper", "lower", "left", "right", "inner", "outer" and other terms indicating directions or positional relationships are based on the attached drawings. The direction or position relationship shown is only for ease of description, and does not indicate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation process for a polypropylene composite film based on a bio-based wheat straw. The preparation process comprises the following steps of conveying crushed straw particles to a neutralizing and cleaning tank; neutralizing and cleaning the straw particles in the neutralizing and cleaning tank; making the straw particles stand in a hydrothermal reactor at constanttemperature; drying the straw particles through a vacuum drying box; mixing the straw particles with raw materials through a mixing machine; and outputting the materials to a film making machine through a screw extruder for film production. According to the preparation process, a central control unit is connected with a corresponding component, a matrix Ri is established according to the comparison result of the straw mass Ma and each value in the Ma0 matrix so as to control each device to select a corresponding operation parameter, and a matrix Sj is established according to the comparison result of the straw particle mass Mb and each value in the Mb0 matrix so as to select the amount of the corresponding raw materials and a preparation process. High-quality composite materials can be rapidly prepared while it is ensured that the content of straw particles is within a preset range, and the preparation efficiency of the process is improved.

Description

technical field [0001] The invention relates to the technical field of bio-environmental protection composite materials, in particular to a preparation process of a bio-based wheat straw polypropylene composite film. Background technique [0002] Polypropylene material is widely used in various aspects such as industry, agriculture, and life because of its advantages such as low density, high mechanical strength, good chemical resistance, low price, and easy molding. But at the same time, the chemical inertness and surface energy of polypropylene materials are very low, and the plastic products made of them are difficult to print on the surface, and the large-scale application of polypropylene materials not only brings great convenience to human production and life, but also Serious white pollution has been caused to the existing environment, and it is an urgent technical problem to be solved by those skilled in the art to find a degradable polypropylene composite material w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29B9/04B29B9/14B29C48/285B29B13/00C08L23/12C08L97/02C08L23/08C08L51/06C08J5/18
CPCB29B9/04B29B9/14B29B13/00B29C48/287C08J5/18C08J2323/12C08J2397/02C08J2423/08C08J2451/06
Inventor 王家福
Owner 瑞年科技(广东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap