Thermosetting engine oil filter paper and preparation method thereof

A kind of oil filter paper, thermosetting technology, applied in the field of filter paper, can solve the problems of unable to meet the requirements of long-term work of the oil filter, unable to coordinate filtration efficiency and dirt holding capacity, poor hydrophobicity of the oil filter paper, etc., to achieve low tightness, Low pore size, good aging resistance and temperature resistance

Pending Publication Date: 2021-01-01
TIANJIN UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The common oil filter paper on the market is usually a kind of paper filter layer made of ordinary wood pulp. Poor water resistance, poor strength, and poor temperature resistance; on the other hand, the fiber composition is single, and the relationship be

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting engine oil filter paper and preparation method thereof
  • Thermosetting engine oil filter paper and preparation method thereof
  • Thermosetting engine oil filter paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A thermosetting machine oil filter paper, comprising a paper filter layer and a resin layer, the resin layer is wrapped on the paper filter layer; and the paper filter layer is made up of the raw materials of the following mass fraction: coniferous wood fiber 20% , mercerized pulp fiber 40%, cotton linter fiber 8%, PET fiber 29.42%, glass fiber 2%, dry strength agent CPAM 0.06%, wet strength agent PAE0.5%, dispersant PEO 0.02%; the resin layer is Thermosetting phenolic resin.

[0033] The preparation method of above-mentioned thermosetting machine oil filter paper, comprises the following steps:

[0034] Step 1, beating softwood fiber, mercerized pulp fiber and cotton linter fiber respectively to obtain corresponding slurry;

[0035] Step 2. Mix the slurry obtained in step 1 with PET fiber and glass fiber, and decompose to obtain the mixed slurry, and add dry strength agent CPAM, wet strength agent PAE and dispersant PEO at the same time;

[0036] Step 3, the mixed sl...

Embodiment 2

[0040] A thermosetting machine oil filter paper, comprising a paper filter layer and a resin layer, the resin layer is wrapped on the paper filter layer; and the paper filter layer is made up of the raw materials of the following mass fraction: coniferous wood fiber 20% , mercerized pulp fiber 47%, cotton linter fiber 5%, PET fiber 18.93%, aramid fiber 5%, glass fiber 3%, dry strength agent CPAM 0.04%, wet strength agent PAE 1%, dispersant PEO 0.03% ; The resin layer is thermosetting phenolic resin.

[0041] The preparation method of above-mentioned thermosetting machine oil filter paper, comprises the following steps:

[0042] Step 1, beating softwood fiber, mercerized pulp fiber and cotton linter fiber respectively to obtain corresponding slurry;

[0043] Step 2. Mix the slurry obtained in step 1 with PET fiber, aramid fiber and glass fiber, and decompose to obtain the mixed slurry. At the same time, add dry strength agent CPAM, wet strength agent PAE and dispersant PEO;

...

Embodiment 4

[0056] A kind of thermosetting machine oil filter paper, comprises paper quality filter layer and resin layer, and described resin layer is wrapped on described paper quality filter layer; And described paper quality filter layer is made up of the raw material of following mass fraction: coniferous wood fiber 18% , mercerized pulp fiber 35%, cotton linter fiber 12%, PET fiber 24.42%, aramid fiber 7%, glass fiber 3%, dry strength agent CPAM 0.04%, wet strength agent PAE 0.5%, dispersant PEO 0.04%; The resin layer is thermosetting phenolic resin.

[0057] The preparation method of above-mentioned thermosetting machine oil filter paper, comprises the following steps:

[0058] Step 1, beating softwood fiber, mercerized pulp fiber and cotton linter fiber respectively to obtain corresponding slurry;

[0059] Step 2. Mix the slurry obtained in step 1 with PET fiber, aramid fiber and glass fiber, and decompose to obtain the mixed slurry. At the same time, add dry strength agent CPAM,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides thermosetting engine oil filter paper which comprises a paper filter layer and a resin layer, and the paper filter layer is coated with the resin layer; the paper filter layer is prepared from the following raw materials in percentage by mass: 10%-30% of coniferous wood fibers, 25%-50% of mercerized pulp fibers, 0%-15% of cotton linter fibers, 20%-40% of PET fibers, 0%-10% of aramid fibers, 0%-5% of glass fibers, 0%-0.1% of a dry strength agent, 0.5%-1.5% of a wet strength agent and 0.1% of a dispersing agent; and the resin layer is thermosetting phenolic resin. The invention further provides a preparation method of the thermosetting engine oil filter paper. The engine oil filter paper disclosed by the invention has the advantages of good strength, temperature resistance and hydrophobicity, small pore size, high air permeability and excellent filtering performance.

Description

technical field [0001] The disclosure relates to the field of filter paper technology, in particular to a thermosetting oil filter paper and a preparation method thereof. Background technique [0002] Engine oil filter paper is a filter paper with high stiffness and strength after the base paper of the filter paper is impregnated with phenolic resin, and can withstand a certain pressure difference after heat curing treatment. It is the key material of the engine filter system. It can filter out dust, metal particles and carbon deposits in the engine oil to ensure the cleanliness of the engine oil, thereby reducing the wear and tear between the mechanical parts of the engine, cleaning the engine and prolonging its service life. With the continuous development of engine technology, the performance requirements of oil filter paper continue to increase, especially as the requirements for oil filter replacement mileage continue to increase, the requirements for the amount of dirt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/08D21H11/00D21H11/12D21H13/26D21H13/40D21H13/24D21H21/18D21H21/20D21H21/08D21H19/24D21H25/06
CPCD21H27/08D21H11/00D21H11/12D21H13/26D21H13/40D21H13/24D21H21/18D21H21/20D21H21/08D21H19/24D21H25/06
Inventor 惠岚峰赵国栋杨乾孙哲刘忠
Owner TIANJIN UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap