Ceramic material with high dielectric constant and high Qf value as well as preparation method and application thereof

A high dielectric constant, ceramic material technology, applied in ceramics, inorganic insulators, etc., can solve the problem of shortage of microwave dielectric ceramic materials, and achieve the effect of high dielectric constant

Active Publication Date: 2021-01-26
XIAMEN SUNYEAR ELECTRONICS CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the advancement of mobile communication and radar technology, microwave electronic components are gradually developing towards high frequency. Therefore, microwave dielectric ceramic materials with high dielectric constant, high quality factor, and near-zero resonance frequency temperature coefficient have become more and more research hotspots. Microwave dielectric ceramic materials with these three properties are in short supply

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic material with high dielectric constant and high Qf value as well as preparation method and application thereof
  • Ceramic material with high dielectric constant and high Qf value as well as preparation method and application thereof
  • Ceramic material with high dielectric constant and high Qf value as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The preparation method of the ceramic material of high dielectric constant high Qf value of the present invention comprises the following steps:

[0030] ①Synthesis of main material Ba by solid phase method 4+2x ln 4+8x Ti 22-7x o 54 : According to the proportion of elements in the compound, weigh the corresponding mass of high-purity barium carbonate, rare earth oxide Ln 2 o 3 and titanium dioxide are placed in a ball mill, and water is added in a mass ratio of solid material: water = 1: (1.0-2.0) for wet ball milling. After the ball is milled into a uniform powder, the particle size D50 can be 0.4-1.0um, and then dried by a spray drying tower or other methods; then calcined in an air furnace at a temperature range of 1130°C to 1250°C for 2 to 4 hours; finally the main Material Ba 4+2x ln 4+8x Ti 22-7x o 54 powder.

[0031] ② Synthesis of auxiliary material Zr by solid phase method 0.8 sn 0.2 TiO 4 : Mix zirconium dioxide, tin oxide and titanium dioxide in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a ceramic material with a high dielectric constant and a high Qf value and a preparation method thereof, and relates to the field of information function materials. The ceramicmaterial comprises a main crystalline phase and a modified additive. The main crystalline phase includes a main material and an auxiliary material. The general chemical formula of the main crystal phase is Ba4+2xLn4+8xTi22-7xO54. yZr0.8Sn0.2TiO4, wherein x is larger than 0 and smaller than 0.13, and y is larger than 0 and smaller than 0.05. Ba4+2xLn4+8xTi22-7xO54 is the chemical general formula ofthe main material, and Ln is selected from one or more of La, Y, Sm, Dy, Ho, Er and Nd. Zr0.8Sn0.2TiO4 is used as a chemical formula of an auxiliary material. The mass fraction of the main crystal phase in the ceramic material is 99-99.5 wt%, and the mass fraction of the modified additive in the ceramic material is 0.5-1wt%. The main material and the auxiliary material are respectively synthesized by adopting a solid-phase method to prepare a uniform powdery ceramic material, the powdery ceramic material is sintered to obtain the ceramic material with high dielectric constant and high Qf value, and the material can meet the requirements of microwave devices on high dielectric constant and high Qf value.

Description

technical field [0001] The invention relates to the field of information functional materials, and in particular to a ceramic material with high dielectric constant and high Qf value, its preparation method and application. Background technique [0002] Microwave dielectric ceramic materials are a new type of functional ceramic materials developed rapidly in recent years. It is the core basic material of new microwave circuits and devices including dielectric resonators, filters, oscillators, duplexers, antennas, dielectric substrates, etc. It is widely used in modern microwave communication and satellite navigation systems and equipment. With the advancement of mobile communication and radar technology, microwave electronic components are gradually developing towards high frequency. Therefore, microwave dielectric ceramic materials with high dielectric constant, high quality factor, and near-zero resonance frequency temperature coefficient have become more and more research...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/49C04B35/622C04B35/626C04B35/638C04B35/64C04B35/632C04B35/634H01B3/12
CPCC04B35/49C04B35/4686C04B35/622C04B35/62605C04B35/6261C04B35/638C04B35/64C04B35/632C04B35/63488C04B35/63416H01B3/12C04B2235/3293C04B2235/3224C04B2235/3294C04B2235/3298C04B2235/3284C04B2235/3262C04B2235/3267C04B2235/661C04B2235/6562C04B2235/6567
Inventor 杨和成张军志罗昌宸
Owner XIAMEN SUNYEAR ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com