Cathode component for discharge lamp, and discharge lamp
A technology for cathode parts and discharge lamps, which is applied to components of gas discharge lamps, discharge lamps, gas discharge lamps, etc., and can solve problems such as durability degradation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0094] (Examples 1 to 5, Comparative Example 1)
[0095] The following two types of mixed raw material powders of thorium oxide powder and metal tungsten powder were prepared.
[0096] The first mixed raw material powder is prepared as follows. First, ammonium tungstate (APT) powder with an average particle size of 2 μm is heated to a temperature of 500° C. in the atmosphere to turn the ammonium tungstate powder into tungsten oxide powder. Next, thorium nitrate powder with an average particle diameter of 3 μm was added to the tungsten oxide powder, and pure water was added thereto, followed by uniform mixing by stirring for 15 hours or more. Next, the water was completely evaporated to obtain a mixed powder in which thorium nitrate powder and tungsten oxide powder were uniformly mixed. Next, heating was performed at a temperature of 520° C. in the air to convert the thorium nitrate powder into thorium oxide. Next, heat treatment was performed at a temperature of 800° C. in ...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com