High-toughness antistatic foamed polypropylene and preparation method thereof

A foamed polypropylene and antistatic technology, applied in the field of polypropylene materials, can solve the problems of reduced strength, different sizes, and low lifespan, and achieve the effect of light weight and uniform size

Pending Publication Date: 2021-01-29
JIANGSU HAOSHENG PLASTIC IND TECH CO LTD
View PDF21 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Expanded polypropylene has the advantages of light weight and heat insulation, so it is widely used in daily necessities, industry, and agriculture. Expanded polypropylene needs to be obtained by cutting and foaming polypropylene. When cutting, the size of the cutting will be different, and the size of the foamed polypropylene particles produced at the end will be uneven. When the product is subsequently hot-pressed into a board, the internal cavity will be formed due to the different size, resulting in a decrease in strength.
During the use of polypropylene, it is unavoidable to come into contact with air, water, etc., which will cause some fungi to form colonies on the surface of polypropylene, which will corrode polypropylene. The polypropylene available on the market has not been made. Very good treatment method leads to low service life, frequent replacement of materials, and increased use cost
In order to obtain particles with a larger foaming ratio, the general treatment method is to increase the amount of foaming agent. The foaming agent added is generally composed of surfactants. Adding too much foaming agent will cause The voids in the polypropylene particles become larger, which reduces the hardness of the product and leads to a decrease in the pass rate of the product. Therefore, it is particularly important to invent a polypropylene foam particle and its foaming process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness antistatic foamed polypropylene and preparation method thereof
  • High-toughness antistatic foamed polypropylene and preparation method thereof
  • High-toughness antistatic foamed polypropylene and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A high-toughness antistatic foamed polypropylene, according to parts by weight, including 20 parts of colorless polypropylene particles, 10 parts of colored polypropylene particles, 2 parts of carbon black, 5 parts of antistatic agent, 2 parts of antibacterial agent, 3 parts of anti-aging agent, 2 parts of lubricant, 8 parts of cyclic fatty acid methyl ester, 4 parts of methyl phosphate, 3 parts of sodium dodecylbenzenesulfonate.

[0029] The raw materials of each component of the antistatic agent are as follows, in parts by weight, 5 parts of octadecyltrimethylammonium bromide and 3 parts of sodium dodecylsulfonate.

[0030] The raw materials of each component of the antibacterial agent are as follows, in parts by weight, 5 parts of 3-ethoxy-4-hydroxybenzaldehyde and 2 parts of vanillin.

[0031] The raw materials of each component of the antiaging agent are as follows, in parts by weight, 5 parts of trichlorotoluene, 2 parts of phenol, and 5 parts of N-N'-diphenyl-p-p...

Embodiment 2

[0043] A high-toughness antistatic foamed polypropylene, according to parts by weight, including 23 parts of colorless polypropylene particles, 14 parts of colored polypropylene particles, 3 parts of carbon black, 7 parts of antistatic agent, 2 parts of antibacterial agent, 4 parts of anti-aging agent, 4 parts of lubricant, 9 parts of cyclic fatty acid methyl ester, 7 parts of methyl phosphate, 4 parts of sodium dodecylbenzenesulfonate.

[0044] The raw materials of each component of the antistatic agent are as follows, in parts by weight, 6 parts of octadecyltrimethylammonium bromide and 6 parts of sodium dodecylsulfonate.

[0045] The raw materials of each component of the antibacterial agent are as follows, in parts by weight, 6 parts of 3-ethoxy-4-hydroxybenzaldehyde and 3 parts of vanillin.

[0046] The raw materials of each component of the antiaging agent are as follows, in parts by weight, 7 parts of trichlorotoluene, 4 parts of phenol, and 7 parts of N-N'-diphenyl-p-p...

Embodiment 3

[0058] A high-toughness antistatic foamed polypropylene, according to parts by weight, including 25 parts of colorless polypropylene particles, 15 parts of colored polypropylene particles, 4 parts of carbon black, 10 parts of antistatic agent, 3 parts of antibacterial agent, 5 parts of anti-aging agent, 5 parts of lubricant, 10 parts of cyclic fatty acid methyl ester, 8 parts of methyl phosphate, 5 parts of sodium dodecylbenzenesulfonate.

[0059] The raw materials of each component of the antistatic agent are as follows, in parts by weight, 7 parts of octadecyltrimethylammonium bromide and 7 parts of sodium dodecylsulfonate.

[0060] The raw materials of each component of the antibacterial agent are as follows, in parts by weight, 7 parts of 3-ethoxy-4-hydroxybenzaldehyde and 4 parts of vanillin.

[0061] The raw materials of each component of the antiaging agent are as follows, in parts by weight, 10 parts of trichlorotoluene, 5 parts of phenol, and 8 parts of N-N'-diphenyl-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-toughness antistatic foamed polypropylene and a preparation method of the high-toughness antistatic foamed polypropylene. The high-toughness antistatic foamed polypropylene comprises the following components in parts by weight: 20-25 parts of colorless polypropylene particles, 10-15 parts of colored polypropylene particles, 2-4 parts of carbon black, 5-10 parts of an antistatic agent, 2-3 parts of a bacteriostatic agent, 3-5 parts of an anti-aging agent, 2-5 parts of a lubricant, 8-10 parts of cyclic fatty acid methyl ester, 4-8 parts of methyl phosphate and 3-5 parts of sodium dodecyl benzene sulfonate. The preparation method has the advantages of light weight and heat insulation, twice screening is carried out in the preparation process, particles with uniform sizes can be screened out each time, and uniform sizes of foamed polypropylene particles are guaranteed; added phenol can be mixed with trichlorotoluene and N-N '-diphenyl-p-phenylenediamine for use, the ageing resistance of the product is improved, bromine water is added in the preparation process, inert gas can be emitted in the combustion process, then the oxygen content is reduced, the certain flame retardant purpose is achieved, and the flame retardant property is improved.

Description

technical field [0001] The invention relates to the technical field of polypropylene materials, in particular to a high-toughness antistatic foamed polypropylene and a preparation method thereof. Background technique [0002] Expanded polypropylene has the advantages of light weight and heat insulation, so it is widely used in daily necessities, industry, and agriculture. Expanded polypropylene needs to be obtained by cutting and foaming polypropylene. When cutting, the size of the cutting will be different, and the size of the foamed polypropylene particles produced at the end will be uneven. When the product is subsequently hot-pressed into a board, the internal cavity will be formed due to the different size, resulting in a decrease in strength. During the use of polypropylene, it is unavoidable to come into contact with air, water, etc., which will cause some fungi to form colonies on the surface of polypropylene, which will corrode polypropylene. The polypropylene avail...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08K3/04C08K5/19C08K5/42C08K5/13C08K5/18C08K5/053C08K5/03C08K3/34C08K13/02C08J9/30C08J9/00B29B9/06B29B9/16
CPCC08J9/30C08J9/0061C08J9/0095B29B9/06B29B9/16C08J2323/12C08J2423/12C08K2201/014C08K3/04C08K5/19C08K5/42C08K5/13C08K5/18C08K5/053C08K5/03C08K3/34C08K3/346C08K13/02
Inventor 顾鹏程
Owner JIANGSU HAOSHENG PLASTIC IND TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products