Tracer agent for tracing detection on polar solvent and tracing detection method
A polar solvent and tracer technology, applied in the field of detection and analysis, can solve the problems of large amount of chemical tracer, low test resolution, large detection error, etc., to achieve high economic value and social value, accurate tracer detection High degree of resistance, the effect of preventing adhesion and adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0084] 1. Preparation of tracer:
[0085]Preparation of carbon quantum dots: Add 60mg of rhodamine B, 20mL of 0.3M aqueous sodium hydroxide solution, 3mL of PEG800 and 1.2g of phloroglucinol into the polytetrafluoroethylene lining, and put them into the reactor for hydrothermal reaction , the reaction temperature is 180°C, the reaction time is 10h, after the reaction is complete, it is naturally cooled to obtain the crude reactant liquid, and then the crude reactant liquid is subjected to centrifugal purification treatment to obtain carbon quantum dots with a wavelength of 578nm and a half-peak width of 40nm. 84%, emit orange-yellow light, and the fluorescence emission spectrum is as follows figure 1 As shown, PEG1000 groups are bonded to the surface of the carbon quantum dots, and the content of the surface-bonded PEG1000 groups in the carbon quantum dots is 16%.
[0086] The purified carbon quantum dot solution was used as a tracer, and the maximum solubility of the tracer ...
Embodiment 2
[0111] 1. Preparation of Tracers
[0112] Add 52mg of sodium fluorescein, 20mL of 0.3M aqueous sodium hydroxide solution, 3mL of PEG 800 and 1g of citric acid into the polytetrafluoroethylene lining, and put them into the reactor for hydrothermal reaction. The reaction temperature is 195°C. Time 10h, natural cooling after the reaction is complete, the reactant crude liquid is obtained, and then the reactant crude liquid is subjected to centrifugal purification treatment to obtain carbon quantum dots with a wavelength of 515nm, a half-maximum width of 36nm, and a quantum yield of 86%. The fluorescence emission spectrum is as follows: image 3 As shown, the carbon quantum dot surface is bonded with PEG800 groups, and in the carbon quantum dots, the content of the surface bonded PEG800 groups is 15%.
[0113] The purified carbon quantum dot solution was used as a tracer, and the maximum solubility of the tracer in water was 300g / L under the condition of 15-150°C, so as to carry o...
Embodiment 3
[0138] 1. Preparation of tracer:
[0139] Preparation of carbon quantum dots: add 40mg of rhodamine 6G, 20mL of 0.1M aqueous sodium hydroxide solution, and 3g of PEG-COOH (the molecular weight of PEG is 800) into the polytetrafluoroethylene lining, and put it into the reaction kettle for hydrothermal Reaction, the reaction temperature is 160°C, the reaction time is 5h, after the reaction is complete, it is naturally cooled to obtain the crude reactant liquid, and then the crude reactant liquid is subjected to centrifugal purification treatment to obtain carbon quantum dots with a wavelength of 556nm and a half-peak width of 42nm. rate of 80%, emitting yellow light, the fluorescence emission spectrum is shown as Figure 5 As shown, PEG-COOH groups are bonded to the surface of the carbon quantum dots, and the content of the surface-bonded PEG-COOH groups in the carbon quantum dots is 16%.
[0140] The purified carbon quantum dot solution was used as a tracer, and the maximum so...
PUM
Property | Measurement | Unit |
---|---|---|
solubility (mass) | aaaaa | aaaaa |
full width at half maximum | aaaaa | aaaaa |
wavelength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap