Fair-faced concrete and preparation method thereof

A technology of fair-faced concrete and cement, which is applied in the field of building materials, can solve problems such as unsatisfactory high compressive strength, general compressive strength, and limited use prospects, and achieve improved comprehensive performance and compressive strength, good decorative effect, and bleeding low rate effect

Inactive Publication Date: 2021-02-09
韩昌龙
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The pumping clear-water concrete, by adding river sand and mineral powder, has certain energy-saving and environmental protection significance, and reduces the production cost of pumping clear-water concrete, but its compressive strength is average, which cannot meet the needs of high compressive strength, and the use prospect is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1 provides a kind of fair-faced concrete, is characterized in that, comprises the following components by weight to make: 30 parts of cement, 15 parts of pozzolans, nano-hybrid hyperbranched polymer HB-SiO 2 3 parts, 75 parts of silica sand, 85 parts of coarse aggregate, 3 parts of basalt fiber, 1 part of graphene oxide fiber, 7.5 parts of composite admixture, 15 parts of water, 1 part of carboxyl metal organic framework, 1 part of zirconium citrate, oxidation Zinc nanofiber 2 parts.

[0033] The composite admixture is made from the following raw materials by weight percentage: hyperbranched sulfonate surfactant SHBP-1 10%, palygorskite 20%, defoamer 2%, and the balance is 4-phosphorus Trimethyl crotonate / 4-(2-furyl)-1-buten-4-ol / trifluchrysmic acid ionized N,N-(2-hydroxyethyl)-2-aminoethanesulfonic acid Copolymer; the sum of the weight percentages of the above-mentioned raw materials is 100%; the defoamer is polyacrylamide.

[0034] The 4-phosphobutenoic a...

Embodiment 2

[0040] Embodiment 2 provides a kind of fair-faced concrete, is characterized in that, comprises the following components by weight to make: 33 parts of cement, 17 parts of pozzolans, nano-hybrid hyperbranched polymer HB-SiO 2 4 parts, 78 parts of silica sand, 88 parts of coarse aggregate, 3.5 parts of basalt fiber, 1.5 parts of graphene oxide fiber, 7.7 parts of composite admixture, 16 parts of water, 1.5 parts of metal organic framework with carboxyl group, 1.5 parts of zirconium citrate, oxide 2.5 parts of zinc nanofibers.

[0041] The composite admixture is made from the following raw materials by weight percentage: hyperbranched sulfonate surfactant SHBP-1 12%, palygorskite 23%, defoamer 2.5%, and the balance is 4-phosphorus Trimethyl crotonate / 4-(2-furyl)-1-buten-4-ol / trifluchrysmic acid ionized N,N-(2-hydroxyethyl)-2-aminoethanesulfonic acid Copolymer; the sum of the weight percentages of the above-mentioned raw materials is 100%; the defoamer is alkylphenol polyoxyethy...

Embodiment 3

[0048] Embodiment 3 provides a kind of fair-faced concrete, is characterized in that, comprises the following components by weight to make: 35 parts of cement, 20 parts of pozzolans, nano-hybrid hyperbranched polymer HB-SiO 2 4.5 parts, 80 parts of silica sand, 90 parts of coarse aggregate, 4 parts of basalt fiber, 2 parts of graphene oxide fiber, 8 parts of composite admixture, 17.5 parts of water, 2 parts of carboxyl metal organic framework, 2 parts of zirconium citrate, 3.5 parts of zinc nanofibers.

[0049] The composite admixture is made from the following raw materials by weight percentage: hyperbranched sulfonate surfactant SHBP-1 20%, palygorskite 25%, defoamer 3%, and the balance is 4-phosphorus Trimethyl crotonate / 4-(2-furyl)-1-buten-4-ol / trifluchrysmic acid ionized N,N-(2-hydroxyethyl)-2-aminoethanesulfonic acid Copolymer; the sum of the weight percentages of the above-mentioned raw materials is 100%; the defoamer is polyether.

[0050] The 4-phosphobutenoic acid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses fair-faced concrete and a preparation method thereof. The concrete is prepared from the following components in parts by weight: 30-40 parts of cement, 15-25 parts of volcanicash, 3-6 parts of nano hybrid hyperbranched polymer HB-SiO2, 75-85 parts of silica sand, 85-95 parts of coarse aggregate, 3-5 parts of basalt fibers, 1-3 parts of graphene oxide fibers, 7.5-8.5 partsof a composite additive, 15-20 parts of water, 1-3 parts of a carboxyl metal organic framework, 1-3 parts of zirconium citrate and 2-5 parts of zinc oxide nanofibers. The invention also provides a preparation method of the fair-faced concrete. The fair-faced concrete provided by the invention is better in comprehensive performance, higher in compressive strength and flowability, lower in bleedingrate, better in durability, environmental protection property and decorative effect, very good in appearance, smooth in surface and less in pores.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a fair-faced concrete and a preparation method thereof. Background technique [0002] In recent years, with the progress of the society and the development of the economy, the enthusiasm for urban modernization has been high, and various construction projects have emerged one after another. Behind these projects, the use of building materials is inseparable. Building materials are the basis for ensuring the quality of engineering projects. Concrete is the most widely used man-made building material in contemporary times. It has the characteristics of rich raw materials, low price, simple production process, and good compressive performance. It is widely used in project construction. [0003] Fair-faced concrete is one-time pouring and molding without any external plastering and other decorations. At present, with the continuous improvement of people's environmental pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/08
CPCC04B28/04C04B28/08C04B2111/00008C04B2201/50C04B7/13C04B24/24C04B14/06C04B14/048C04B18/082C04B18/023C04B18/12C04B14/4643C04B14/386C04B22/002C04B24/16C04B14/102C04B2103/50C04B24/161
Inventor 韩昌龙
Owner 韩昌龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com