Environment-friendly agate glaze and preparation process thereof

A preparation process and agate glaze technology are applied in the field of environment-friendly agate glaze and its preparation process, which can solve the problems of poor physical and chemical properties such as plasticity and fire resistance, low appearance quality and mechanical resistance, and achieve enhanced opacity and appearance. Improved quality and mechanical strength, reduced glaze curling effect

Inactive Publication Date: 2021-02-23
江西亚航科技有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the existing agate firing process, there are still great defects. After firing, the intrinsic, appearance quality and mechanical resistance are low, and the phy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly agate glaze and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] see figure 1 , the present invention provides a technical solution: an environment-friendly agate glaze prepared from the following raw materials:

[0023] The raw materials are as follows in parts by weight: 25 parts of agate stone, 15 parts of plant ash, 1 part of magnesium oxide, 3 parts of iron oxide, 0.6 part of nano-titanium dioxide, 3 parts of feldspar, 5 parts of diatomaceous earth, 1 part of antibacterial agent, 4 parts of quartz, 5 parts of talc, 2 parts of wollastonite and 18 parts of distilled water.

[0024] In this embodiment, specifically: the feldspar is any one of white feldspar or yellow feldspar or a mixture of both, the particle size of the nano-titanium dioxide is 150um, and the particle size of the magnesium oxide and iron oxide is 50um .

[0025] A kind of environment-friendly type agate glaze preparation process, comprises the following steps:

[0026] Step 1. Preparation of powder: put agate, feldspar, talc, quartz and wollastonite into a cor...

Embodiment 2

[0035] see figure 1 , the present invention also provides a technical solution, which is different from Embodiment 1 in that: an environment-friendly agate glaze is prepared from the following raw materials:

[0036] The raw materials are as follows in parts by weight: 30 parts of agate stone, 12 parts of plant ash, 1 part of magnesium oxide, 2 parts of iron oxide, 1 part of nano-titanium dioxide, 4 parts of feldspar, 7 parts of diatomaceous earth, 2 parts of antibacterial agent, 5 parts of quartz, 7 parts of talc, 3 parts of wollastonite and 122 parts of distilled water.

[0037] In this embodiment, specifically: the feldspar is any one of white feldspar or yellow feldspar or a mixture of both, the particle size of the nano-titanium dioxide is 200um, and the particle size of the magnesium oxide and iron oxide is 250um .

[0038] A kind of environment-friendly type agate glaze preparation process, comprises the following steps:

[0039] Step 1. Preparation of powder: put ag...

Embodiment 3

[0048] see figure 1 , the present invention also provides a technical solution, which is different from Embodiment 1 in that: an environment-friendly agate glaze is prepared from the following raw materials:

[0049] The raw materials are as follows in parts by weight: agate stone, 35 parts, plant ash 8, parts, magnesium oxide 2 parts, iron oxide 3 parts, nano-titanium dioxide 1.2 parts, feldspar 5 parts, diatomaceous earth 8 parts, antibacterial agent 3 parts , 6 parts of quartz, 8 parts of talc, 4 parts of wollastonite and 25 parts of distilled water.

[0050] In this embodiment, specifically: the feldspar is any one of white feldspar or yellow feldspar or a mixture of both, the particle size of the nano-titanium dioxide is 250um, and the particle size of the magnesium oxide and iron oxide is 350um .

[0051] A kind of environment-friendly type agate glaze preparation process, comprises the following steps:

[0052] Step 1. Preparation of powder: put agate, feldspar, talc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly agate glaze and a preparation process thereof. The ceramic material is prepared from the following raw materials in parts by weight: 25-35 parts of agate, 8-15 parts of plant ash, 1-2 parts of magnesium oxide, 1-3 parts of ferric oxide, 0.6-1.2 parts of nano titanium dioxide, 3-5 parts of feldspar, 5-8 parts of diatomite, 1-3 parts of an antibacterial agent, 4-6 parts of quartz, 5-8 parts of talc, 2-4 parts of wollastonite and 18-25 parts of distilled water. The agate and the plant ash are used as base materials and matched with the feldspar, thediatomite, the quartz and the wollastonite, so that the fired agate glaze has good plasticity, fire resistance and other physicochemical properties, the fired agate glaze is excellent in smoothness and jade sense layering sense, and the talc is used for improving the thermal stability, expanding the firing range and enhancing the opacification effect; and theglaze curling is reduced, the internalquality, the appearance quality and the mechanical strength resistance of the agate glaze are greatly improved, and the agate glaze has great environmental protection performance.

Description

technical field [0001] The invention relates to the technical field of agate glaze, in particular to an environment-friendly agate glaze and a preparation process thereof. Background technique [0002] Agate is also known as onyx, agate, horse brain, etc. It is a kind of chalcedony minerals, and it is often a striped block mixed with opal and aphanitic quartz. It has a hardness of 6.5-7 degrees, a specific gravity of 2.65, and a similar color. There are layers; [0003] There are many types of agate, including pictographic agate (agate natural pattern, agate picture stone, pictographic slice, pattern agate, water plant agate, marine chalcedony, landscape agate, pattern agate, shadow agate, etc.), southern red agate, Warring States red Agate, Rock Sugar Agate, Northern Red Agate, Green Agate, Purple Green Agate, Yanyuan Agate, Silk Agate, Fire Agate, Gobi Agate, Grape Agate, Wolf Blood Agate, Xinjiang Hotan Agate Seed Material, Insect Agate, etc. [0004] In the existing ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022
Inventor 涂祈林
Owner 江西亚航科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap