Method and application of dye residue for preparing cement floor color paste and cement curing enhancer

A technology of cement solidification and reinforcing agent, which is applied in the direction of pigment slurry, etc., to achieve the effect of saving cost, simple method and maximizing income

Active Publication Date: 2022-02-18
HANGZHOU ZUONA IND CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, although industrial waste residues and waste liquids have been used in cement enhancers, and there are various color paste formulations and cement enhancer formulations on the market, the recycling of printing and dyeing dye residues for color floor color paste and cement curing enhancers There is no related technical publication

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Implementation 1, the dye residue slurry with a specific gravity value of 1.15 is used as a mother liquor, 70 parts by weight of mother liquor, 2 parts by weight of polyether polyol, 2 parts by weight of triethanolamine, 6 parts by weight of lithium silicate, 3 parts by weight of urea and diethylene glycol 3 parts by weight are mixed together and stirred evenly, and the stirring time is 60 to 120 minutes to obtain a cement floor color paste and a cement curing enhancer.

Embodiment 2

[0024] Implementation 2, using the dye residue slurry with a specific gravity value of 1.17 as mother liquor, 85 parts by weight of mother liquor, 6 parts by weight of polyether polyol, 8 parts by weight of triethanolamine, 10 parts by weight of lithium silicate, 10 parts by weight of urea and diethylene glycol 10 parts by weight are mixed together and stirred evenly, and the stirring time is 60 to 120 minutes to obtain a cement floor color paste and a cement curing enhancer.

Embodiment 3

[0025] Implementation 3, using the dye residue slurry with a specific gravity value of 1.16 as mother liquor, 77 parts by weight of mother liquor, 4 parts by weight of polyether polyol, 5 parts by weight of triethanolamine, 8 parts by weight of lithium silicate, 6 parts by weight of urea and diethylene glycol 6 parts by weight are mixed together and stirred evenly, and the stirring time is 60 to 120 minutes to obtain a cement floor color paste and a cement curing enhancer.

[0026] In the above embodiments, if the specific gravity of the dye residue is greater than 1.15 to 1.17, dilute with water so that the specific gravity is respectively 1.15, 1.17 or 1.16 and used as mother liquor;

[0027] If the specific gravity of the dye residue is lower than 1.15-1.17, extract polyacrylamide at 0.5-2% of the weight of the dye residue, and add an appropriate amount of dilution water at a temperature of 40-60 degrees to dissolve the polyacrylamide into a solution. The solution is added ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method and application for preparing cement floor color paste and cement solidification enhancer from dye residue. The method comprises the following steps: using dye residue to prepare mother liquor; mixing 70-85 parts by weight of mother liquor, polyether polyol 2~6 parts by weight, 2~8 parts by weight of triethanolamine, 6~10 parts by weight of lithium silicate, 3~10 parts by weight of urea and 3~10 parts by weight of diethylene glycol are mixed together and stirred evenly, and the stirring time is After 60 to 120 minutes, the cement floor color paste and cement curing enhancer are obtained, which are sealed and stored. If the specific gravity value of the dye residue is 1.15-1.17, it is used as mother liquor; if the specific gravity is lower than 1.15-1.17, the following steps are included: extracting polyacrylamide by 0.5-2% of the weight of the dye residue, adding an appropriate amount Dilution water dissolves polyacrylamide into a solution, the solution is added to the dye residue and stirred, then precipitated, and the upper part of the liquid close to water is removed, and when the specific gravity reaches 1.15~1.17, it is used as the mother liquor. The invention has the beneficial effects of simple method, convenient processing, effectively solving dye discharge and beautifying buildings.

Description

technical field [0001] The invention relates to a method and application for preparing cement floor color paste and cement solidification enhancer from dye residue. Background technique [0002] Textile printing and dyeing enterprises are major polluters. The dye uptake rate of dyes used in dyeing processing is generally only 50% to 98%, and about 2% to 50% of dyes become printing and dyeing wastewater, resulting in increased environmental protection costs for enterprises and difficulty in sewage treatment. There are many kinds of printing and dyeing dyes, the largest types are direct dyes, reactive dyes, disperse dyes, acid dyes, vat dyes, azo dyes, cationic dyes, etc., but they are basically environmentally friendly dyes. Solidification, reconciliation has a very good use in the building materials industry, but as waste discharge to produce high-concentration wastewater and secondary pollution discharge of incineration waste gas, enterprises are under huge pressure on envi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/68C09D17/00C04B24/32
CPCC04B41/68C04B41/009C09D17/001C04B41/5024C04B40/0039
Inventor 陶永春朱伟锋陶哲瀚
Owner HANGZHOU ZUONA IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products