High-temperature-resistant and corrosion-resistant solar silica gel plate and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A solar energy and corrosion-resistant technology, applied in the field of high-temperature and corrosion-resistant solar silica gel sheet and its preparation, can solve the problems of hard and brittle, shortened service life, poor acid and alkali resistance, etc. The effect of temperature performance and excellent mechanical properties
Pending Publication Date: 2021-09-24
JIANGYIN TIANXIANG PLASTIC BELT
View PDF4 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The existing solar silica gel panels have poor acid and alkali resistance, and are prone to become hard and brittle after a period of use, shortening the service life
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] The invention provides a high-temperature-resistant and corrosion-resistant solar silica gel plate, which comprises: 31.70% dimethyl silica gel, 9.78% white carbon black, 3.70% hydroxyl silicone oil, 10.64% temperature-resistant agent, 21.54% polyimide fiber, 22.64% organic solvent; the temperature-resistant agent includes: 19.40% epoxy resin, 14.20% expanded graphite, 16.50% nanocellulose airgel, 14.50% Nano cerium oxide, 14.80% nano silicon carbide, 20.6% nano silicon nitride;
[0027] The organic solvent is made by compounding one or more of N-methylpyrrolidone (NMP), ethylene glycol (EG), n-butanol, and terpineol;
[0028] The present invention also provides a method for preparing a high-temperature-resistant and corrosion-resistant solar silica gel plate, and the specific preparation steps are as follows:
[0029] Step 1: Weigh the above-mentioned dimethyl silica gel, white carbon black, hydroxyl silicone oil, temperature-resistant agent, polyimide fiber and organ...
Embodiment 2
[0039]Different from Example 1, it includes: 33.30% dimethyl silica gel, 10.42% white carbon black, 4.50% hydroxy silicone oil, 11.06% temperature resistant agent, 23.86% polyimide fiber by weight percentage , 16.86% organic solvent; the temperature-resistant agent includes: 21.40% epoxy resin, 15.10% expanded graphite, 17.10% nano-cellulose airgel, 15.10% nano-cerium oxide, 16.10% Nano silicon carbide, 15.20% nano silicon nitride.
Embodiment 3
[0041] The difference from Examples 1-2 is that it includes: 32.50% dimethyl silica gel, 10.10% white carbon black, 4.10% hydroxy silicone oil, 10.85% temperature resistant agent, 22.70% polyamide Imine fiber, 19.75% organic solvent; the temperature-resistant agent includes: 20.40% epoxy resin, 14.65% expanded graphite, 16.80% nano-cellulose airgel, 14.80% nano-cerium oxide , 15.45% nano-silicon carbide, 17.90% nano-silicon nitride.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-temperature-resistant and corrosion-resistant solar silica gel plate and a preparation method thereof, and particularly relates to the technical field of solar silica gel plates, and the high-temperature-resistant and corrosion-resistant solar silica gel plate comprises dimethyl silica gel, white carbon black, hydroxyl silicone oil, a temperature-resistant agent, polyimide fibers and an organic solvent. The acid and alkali resistance of the high-temperature-resistant and corrosion-resistant solar silica gel plate can be effectively improved, the high-temperature-resistant and corrosion-resistant solar silica gel plate can be used under acid and alkali conditions for a long time, the hardening and embrittlement problems cannot occur, and the service life is guaranteed; the temperature-resistant agent in the formula can realize composite modification treatment on the silica gel material and the polyimide fiber respectively, is used for enhancing the temperature resistance and the safety performance of the solar silica gel plate, and can improve the acid and alkali resistance and the service life of the solar silica gel plate; the polyimide fiber in the formula serves as a framework of the solar silica gel plate, the internal structural strength of the solar silica gel plate can be effectively improved, and the acid and alkali resistance, the structural strength and the safety performance of the solar silica gel plate can be effectively improved.
Description
technical field [0001] The invention relates to the technical field of solar silica gel panels, more specifically, the invention relates to a high-temperature-resistant and corrosion-resistant solar silica gel panel and a preparation method thereof. Background technique [0002] Silica gel sheet is an industrial rubber sheet made of silica gel as the main raw material. Gaskets, gaskets and seals can be punched, mainly used in food industry, machinery industry, electronic appliances, automobile industry, chemical industry, light industry, metal and paint and other fields. On the solar laminator, a silica gel plate is used as a backing plate. The silica gel plate divides the table top and the upper cover of the laminator into two chambers. Because it also has a certain degree of elasticity, the upper and lower chambers are vacuumed. At the same time, start to inflate the upper chamber to make it deform and exert pressure on the components located in the lower chamber. This is...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more