Perovskite nanocrystalline ink and application thereof

A perovskite and nanocrystal technology, applied in applications, inks, household appliances, etc., can solve the problems of high polymer viscosity, unfavorable inkjet printing, low saturation concentration, etc., achieve high saturation concentration, and not easy to spray holes Clogging and uniform film formation

Pending Publication Date: 2021-10-01
ZHIJING NANOTECH CO LTD +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the perovskite nanocrystal ink methods that have been reported so far are to prepare perovskite nanocrystals first, and then formulate them into solutions. Low
Another method is to add high molecular polymers to the perovskite precursor solution, and use the limitations of high molecular polymers to realize the preparation of nanocrystals, but the high viscosity of high molecular polymers is often not conducive to inkjet printing.
Therefore, existing quantum dot inks still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0088] 90wt% triethyl phosphate, 3wt% PbBr 2 ,2wt% of HN=CHNH 3 Cl, 0.06wt% oleylamine, 0.139wt% oleic acid, 1wt% bis(2,4,6-trimethylbenzoyl) phenylphosphine oxide, 3wt% diethylene glycol diacrylate, stirred for 2 hours , to obtain perovskite nanocrystalline ink (total mass is 10g), the measured viscosity is 2.1cps, and the surface tension is 33dyne / cm.

Embodiment 2

[0090] 30wt% N,N-dimethylformamide (DMF), 30wt% dimethylsulfoxide (DMSO), 4wt% PbBr 2 , 4wt% CH(NH)NH 2 Br, 0.05wt% oleylamine, 0.05wt% oleic acid, 1wt% (2,4,6-trimethylbenzoyl) diphenylphosphine oxide, 2wt% 2-methyl methacrylate, 26wt% Isobornyl acrylate, 2wt% silicon dioxide particle light diffusing agent, stirred for 2 hours to obtain a perovskite nanocrystalline ink (total mass 10g), the measured viscosity was 4.2cps, and the surface tension was 34dyne / cm.

Embodiment 3

[0092] 40wt% DMSO, 10wt% PbI, 5wt% CsI 2 , 5wt% CsBr, 0.5wt% didodecyldimethylammonium bromide, 1.5wt% 1-hydroxy-cyclohexyl-phenyl ketone, 35wt% ethoxyethoxyethyl acrylate, 3wt% polystyrene particle light diffusing agent, stirred for 2 hours to obtain perovskite nanocrystalline ink (total mass 10g), the measured viscosity was 4.6cps, and the surface tension was 28dyne / cm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Surface tensionaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a perovskite nanocrystalline ink and application thereof. The perovskite nanocrystalline ink comprises a perovskite precursor, a compound A and an initiator; the compound A is selected from at least one of oligomer and monomer; and the initiator is selected from at least one of a photoinitiator and a thermal initiator. The perovskite nanocrystalline ink provided by the invention can meet various requirements of ink-jet printing on ink, and a perovskite nanocrystalline composite film printed by using the ink has excellent optical properties and stability.

Description

technical field [0001] The application relates to a perovskite nanocrystal ink and its application, belonging to the technical fields of optical materials and inkjet printing. Background technique [0002] Perovskite nanocrystals have excellent luminescent properties and can be used in lighting, display, light filtering and other fields. Inkjet printing is considered to be an important way of display integration of perovskite nanocrystals, which requires the preparation of suitable printing inks. [0003] Most of the perovskite nanocrystal ink methods that have been reported so far are to prepare perovskite nanocrystals first, and then formulate them into solutions. Low. Another method is to add a polymer to the perovskite precursor solution, and use the limitation of the polymer to realize the preparation of nanocrystals, but the high viscosity of the polymer is often not conducive to inkjet printing. Therefore, existing quantum dot inks still need to be improved. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/30C09D11/101C09D11/38G09F9/33
CPCC09D11/30C09D11/101C09D11/38G09F9/33
Inventor 施立甫钟海政孟令海柏泽龙王晶晶
Owner ZHIJING NANOTECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap