Polymer fiber composite decorative paper and production method thereof
A polymer fiber and production method technology, applied in the field of decorative paper, can solve the problems of poor aging resistance, poor cold resistance, easy to become brittle, etc., and achieve the effects of high strength, low transparency and superior performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0035] The preparation of the composite macromolecule polymer material comprises the following steps:
[0036] A. In terms of parts by mass, take 20-35 parts of acrylic acid, 5-10 parts of methyl acrylate, 10-15 parts of polyvinyl alcohol, 0.1-0.4 parts of Tween80, and 100-130 parts of water. Stir at 300~500r / min for 30~55min to obtain the primary mixture. Take the primary mixture and add azobisisobutylamidine hydrochloride and α-cyclodextrin according to the mass ratio of 80~110:1:0.1~0.3. 50-65kHz ultrasonic vibration for 6-10min, then move to ice water bath, use ultrasonic cell pulverizer to ultrasonically pulverize for 3-7min, under nitrogen atmosphere, irradiate with purple light for 8-13min, then centrifuge the mixture at 8000-10000rpm for 6-10min , remove the upper liquid, collect the lower microgel, wash with water, and dry to obtain the microgel matrix material;
[0037] B. In terms of parts by mass, take 80-100 parts of microgel base material, 8-15 parts of lithium ...
Embodiment 1
[0041] A polymer fiber composite decorative paper, the matrix material of the composite decorative paper is a polymer fiber matrix material, the main component of the polymer fiber matrix material is a composite polymer polymer material, and the composite polymer polymer material contains Lithium diatomaceous earth.
[0042] A production method of polymer fiber composite decorative paper, comprising the following steps:
[0043] (1) Preparation of polymer fiber matrix material:
[0044] According to the number of parts by mass, get 50 parts of composite macromolecule polymer material, 4 parts of bamboo fiber, 7 parts of viscose fiber and blend at 40 ° C, naturally cool to room temperature, and make polymer fiber matrix material after opening;
[0045] (2) Carding into a web: the polymer fiber base material is carded into fiber layers by a carding machine, and the fiber layers are stacked to form a fiber web; the grammage of the fiber web is 20g / ㎡;
[0046] (3) Spunlace reinf...
Embodiment 2
[0055] A polymer fiber composite decorative paper, the matrix material of the composite decorative paper is a polymer fiber matrix material, the main component of the polymer fiber matrix material is a composite polymer polymer material, and the composite polymer polymer material contains Lithium diatomaceous earth.
[0056] A production method of polymer fiber composite decorative paper, comprising the following steps:
[0057] (1) Preparation of polymer fiber matrix material:
[0058] According to the number of parts by mass, get 80 parts of composite polymer polymer material, 8 parts of bamboo fiber, and 12 parts of viscose fiber to blend at 55 ° C, naturally cool to room temperature, and make the polymer fiber matrix material after opening;
[0059] (2) Carding into a web: the polymer fiber base material is carded into a fiber layer by a carding machine, and the fiber layers are stacked to form a fiber web; the grammage of the fiber web is 40g / ㎡;
[0060] (3) Spunlace re...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Basis weight | aaaaa | aaaaa |
| Basis weight | aaaaa | aaaaa |
| Basis weight | aaaaa | aaaaa |