Cycloolefin polymer-polyphenyl ether resin composition as well as preparation method and application thereof

A technology of cyclic olefin polymer and polyphenylene ether resin, which is applied in the field of COP/PPO resin composition of photovoltaic junction boxes, can solve the problems of poor weather resistance, solvent resistance, environmental stress cracking, etc. Olefin polymer-polyphenylene ether COP/PPO alloy material is open, poor solvent resistance and other problems, to achieve the effect of strong mechanical properties, better mechanical properties, and excellent solvent resistance

Active Publication Date: 2021-11-02
ANHUI CHUZHO DEWEI NEW MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, since the PPO / PS alloy uses polystyrene PS as the blended resin, the PPO / PS alloy itself still has some inherent shortcomings of polystyrene PS, such as polystyrene PS weather resistance, solvent resistance, and environmental resistance. Poor performance such as stress cracking
In CN103044894B, it is mentioned that PPO / PS alloy has the problems of poor solvent resistance and poor environmental stress cracking resistance
[0005] But at present, there is no disclosure about cycloolefin polymer-polyphenylene ether COP / PPO alloy material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cycloolefin polymer-polyphenyl ether resin composition as well as preparation method and application thereof
  • Cycloolefin polymer-polyphenyl ether resin composition as well as preparation method and application thereof
  • Cycloolefin polymer-polyphenyl ether resin composition as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In the first step, 40% cycloolefin polymer (COP), 20% polyphenylene ether (PPO), 10% compatibilizer, 10% alkali-free short glass fiber, 16% phosphorus flame retardant, 2% black masterbatch , 0.5% antioxidant, 0.5% light stabilizer, and 1% lubricant are put into a high-speed mixer for pre-mixing for 6 minutes; the second step is to feed the pre-mixed raw materials into a twin-screw extruder with a length-to-diameter ratio of 56:1 , the temperature in the feeding section is 150-230°C, the temperature in the plasticizing section is 260-280°C, the temperature in the homogenizing section is 260-280°C, and the screw speed is 240rpm. After the materials are fully melted and mixed, carry out strand granulation; the third step , transport the finished plastic alloy granules to the boiling drying bin and dry at 100°C for 1 hour; step 4, carry out the second mixing and granulation of the dried plastic alloy granules according to steps 2 and 3.

Embodiment 2

[0041] In the first step, 20% cycloolefin polymer (COP), 40% polyphenylene ether (PPO), 6% compatibilizer, 20% alkali-free short glass fiber, 10% phosphorus flame retardant, 2% black masterbatch , 0.5% antioxidant, 0.5% light stabilizer, and 1% lubricant are put into a high-speed mixer for pre-mixing for 6 minutes; the second step is to feed the pre-mixed raw materials into a twin-screw extruder with a length-to-diameter ratio of 56:1 , the temperature in the feeding section is 150-230°C, the temperature in the plasticizing section is 260-280°C, the temperature in the homogenizing section is 260-280°C, and the screw speed is 240rpm. After the materials are fully melted and mixed, carry out strand granulation; the third step , transport the finished plastic alloy granules to the boiling drying bin and dry at 100°C for 1 hour; step 4, carry out the second mixing and granulation of the dried plastic alloy granules according to steps 2 and 3.

Embodiment 3

[0043] In the first step, 30% cycloolefin polymer (COP), 30% polyphenylene ether (PPO), 8% compatibilizer, 15% alkali-free short glass fiber, 13% phosphorus flame retardant, 2% black masterbatch , 0.5% antioxidant, 0.5% light stabilizer, and 1% lubricant are put into a high-speed mixer for pre-mixing for 6 minutes; the second step is to feed the pre-mixed raw materials into a twin-screw extruder with a length-to-diameter ratio of 56:1 , the temperature in the feeding section is 150-230°C, the temperature in the plasticizing section is 260-280°C, the temperature in the homogenizing section is 260-280°C, and the screw speed is 240rpm. After the materials are fully melted and mixed, carry out strand granulation; the third step , transport the finished plastic alloy granules to the boiling drying bin and dry at 100°C for 1 hour; step 4, carry out the second mixing and granulation of the dried plastic alloy granules according to steps 2 and 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
bending strengthaaaaaaaaaa
izod impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a cycloolefin polymer-polyphenyl ether resin composition as well as a preparation method and an application thereof. The cycloolefin polymer-polyphenyl ether resin composition comprises the following raw materials: 20%-40% of a cycloolefin polymer, 20%-40% of polyphenyl ether, 5%-10% of a compatilizer, 10%-20% of alkali-free short glass fiber, 10%-20% of a phosphorus flame retardant, 1%-3% of black masterbatch, 0.3%-0.8% of an antioxidant, 0.3%-0.8% of a light stabilizer and 1%-3% of a lubricant. The invention also provides a preparation method of the composition. The comprehensive indexes of the photovoltaic module junction box prepared from the composition disclosed by the invention meet the technical requirements of IEC 62790: 2020 and GB/T 37410-2019.

Description

technical field [0001] The invention relates to a cycloolefin polymer-polyphenylene ether COP / PPO resin composition, in particular to a COP / PPO resin composition used in a photovoltaic junction box. Background technique [0002] With the proposal of my country's goal of "carbon peaking and carbon neutrality", the market scale of new energy photovoltaic cell components is expanding day by day. Photovoltaic module junction box (junction box) is an important part of the photovoltaic cell module, and its main function is to connect the electricity generated by the solar cell with the external circuit. The junction box is glued to the back plate of the module through silica gel, and the lead wires in the module are connected to the external cables through the internal lines in the junction box, so that the module and the external cables are connected. It is a kind of electrical design, mechanical A cross-disciplinary comprehensive product combining design and material science. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L65/00C08L71/12C08K7/14C08K9/06
CPCC08L65/00C08L71/12C08L2201/02C08L2201/08C08L2203/20C08K2201/005C08K7/14C08K9/06Y02E10/50
Inventor 张坤邓之俊袁宝陆威章柏松
Owner ANHUI CHUZHO DEWEI NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap