Moisture-absorbing easy-to-scrub coating layer and preparation method thereof

A technology that is easy to scrub and coat. It can be used in coatings and other directions to solve problems such as hidden dangers to health and mildew and deterioration of rice beans.

Inactive Publication Date: 2021-11-19
黄勤
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In a humid environment, drying clothes, towels in the bathroom for a long time, moldy chopping boards, bowls and chopsticks, and rice beans in the kitchen may cause hidden dangers to health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A moisture-absorbing and easy-to-clean coating mainly includes, by weight parts: 30 parts of modified nano-bismuth oxide, 12 parts of diphenylamine benzoic acid copolymer and 2 parts of 1,4-dichlorobutane.

[0033] A method for preparing a moisture-absorbing and easy-to-scrub coating, the preparation method of the moisture-absorbing and easy-to-scrub coating mainly includes the following preparation steps:

[0034](1) After mixing the oxygen-deficient nano-bismuth oxide and water evenly at a mass ratio of 1:20, add 3-aminopropyltrimethoxysilane which is twice the mass of the oxygen-deficient nano-bismuth oxide, and use 2000r / m at 20°C Stir at a speed of min for 1 hour, filter and freeze-dry in vacuum at -10°C for 6 hours, then pulverize the dried product with a universal pulverizer and pass it through a 50-mesh sieve to obtain modified nano-bismuth oxide;

[0035] (2) After mixing the modified nano-bismuth oxide obtained in step (1) with carboxymethyl cellulose and poly...

Embodiment 2

[0042] A moisture-absorbing and easy-to-clean coating mainly includes, by weight, 30 parts of oxygen-deficient nano bismuth oxide, 12 parts of diphenylamine benzoic acid copolymer and 2 parts of 1,4-dichlorobutane.

[0043] A method for preparing a moisture-absorbing and easy-to-scrub coating, the preparation method of the moisture-absorbing and easy-to-scrub coating mainly includes the following preparation steps:

[0044] (1) After mixing oxygen-deficient nano-bismuth oxide with carboxymethyl cellulose and polyethylene glycol in a mass ratio of 6:1:8, spread it evenly on the surface of the substrate, and adjust the power of the near-infrared lamp to 1kW radiation to heat the smear liquid , react the smear solution at 100°C for 0.5h, then adjust the power of the near-infrared lamp to 3kW, and react the smear solution at 400°C for 2h to prepare the primer layer;

[0045] (2) After mixing diphenylamine benzoic acid copolymer and polyethylene glycol in a mass ratio of 4:1, place...

Embodiment 3

[0051] A moisture-absorbing and easy-to-clean coating mainly comprises, by weight, 30 parts of modified nano bismuth oxide and 12 parts of diphenylamine benzoic acid copolymer.

[0052] A method for preparing a moisture-absorbing and easy-to-scrub coating, the preparation method of the moisture-absorbing and easy-to-scrub coating mainly includes the following preparation steps:

[0053] (1) After mixing the oxygen-deficient nano-bismuth oxide and water evenly at a mass ratio of 1:20, add 3-aminopropyltrimethoxysilane which is twice the mass of the oxygen-deficient nano-bismuth oxide, and use 2000r / m at 20°C Stir at a speed of min for 1 hour, filter and freeze-dry in vacuum at -10°C for 6 hours, then pulverize the dried product with a universal pulverizer and pass it through a 50-mesh sieve to obtain modified nano-bismuth oxide;

[0054] (2) After mixing the modified nano-bismuth oxide obtained in step (1) with carboxymethyl cellulose and polyethylene glycol in a mass ratio of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses a moisture-absorbing easy-to-scrub coating layer and a preparation method thereof, and belongs to the technical field of coating layer materials. The preparation method comprises the steps: stirring nano bismuth oxide subjected to hydrogen plasma treatment and 3-aminopropyltrimethoxysilane in water to prepare modified nano bismuth oxide, adding the modified nano bismuth oxide and carboxymethyl cellulose into polyethylene glycol, uniformly mixing, uniformly smearing, heating to prepare a bottom coating layer, and carrying out stirring reaction of 4,4-dihydroxydiphenylamine and 3,5-dichlorobenzoic acid in a sodium hydroxide solution to prepare a diphenylamine-benzoic acid copolymer; uniformly mixing the diphenylamine-benzoic acid copolymer and polyethylene glycol, and carrying out film scraping to prepare a surface coating layer; putting the surface coating layer into a 1,4-dichlorobutane alkaline solution to prepare a modified surface coating layer; and adhering the modified surface coating layer to the bottom coating layer, and heating, to obtain the moisture-absorbing easy-to-scrub coating layer. The moisture-absorbing easy-to-scrub coating prepared by the preparation method has excellent moisture absorption, and dirt on the surface is easy to scrub.

Description

technical field [0001] The invention relates to the technical field of coating materials, in particular to a hygroscopic and easy-to-clean coating and a preparation method thereof. Background technique [0002] With the improvement of living standards, people's requirements for quality of life are getting higher and higher. At the same time, our living environment is also changing. The El Niño phenomenon leads to global warming, the expansion of urban areas, and the large increase in residential population make the heat island effect worse. Most notably, clean air and water, humidity and other inconspicuous factors that have been taken for granted in the past are becoming more and more important in the impact on our health and need to be treated more carefully. People's attention tends to focus on the things they are chasing in front of them, and they are accustomed to what they already have, and they don't think about it until they lose it. [0003] Long-term humid weather...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/02C09D7/62C09D7/63
CPCC09D179/02C09D7/62C09D7/63C08K2201/011C08K9/06C08K3/22C08K5/02
Inventor 黄勤
Owner 黄勤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap