A kind of pb cold laminate surface control technology

A surface control and cold paste technology, which is applied in the direction of manufacturing tools, flat products, wood processing appliances, etc., can solve the problems of high process parameters, low bonding strength, foaming, etc., and achieve low process parameters and enhanced viscosity , good surface finish

Active Publication Date: 2022-07-22
佳诺威集团(河南)新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems of high process parameters in the veneering treatment of PB boards in the prior art, and the production of veneering PB boards is limited by the production process level, which is prone to problems such as glue opening, foaming, and low bonding strength. And proposed a PB cold paste board surface control process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of PB cold veneer surface control process proposed by the present invention, the PB cold veneer is connected by the composite veneer-plain board-composite veneer through the adhesive I according to the order from top to bottom, and finally cold-pressed and formed after After processing, the thickness of the adhesive I between the composite veneer and the plain board is 0.1 mm, and the gluing area is 100%; the adhesive I is composed of epichlorohydrin and polyvinyl alcohol with a mass ratio of 18:7:3:1. , methyl silicone oil and polyetheramine mixed;

[0028] Described PB cold veneer surface control process, specifically comprises the following steps:

[0029] S1. Preparation of composite veneer:

[0030] S11, by weight, take by weighing 20 parts of polyvinyl acetate, 25 parts of ethyl acetate, 1 part of magnesium oxide, 6 parts of 5mol / L ammonium chloride solution, and 3 parts of precipitated barium sulfate, for subsequent use;

[0031] S12, firstly blend the p...

Embodiment 2

[0039] A kind of PB cold veneer surface control process proposed by the present invention, the PB cold veneer is connected by the composite veneer-plain board-composite veneer through the adhesive I according to the order from top to bottom, and finally cold-pressed and formed after After processing, the thickness of the adhesive I between the composite veneer and the plain board is 0.4 mm, and the gluing area is 100%; the adhesive I is composed of epichlorohydrin and polyvinyl alcohol with a mass ratio of 21:9:4:1. , methyl silicone oil and polyetheramine mixed;

[0040] Described PB cold veneer surface control process, specifically comprises the following steps:

[0041] S1. Preparation of composite veneer:

[0042] S11, by weight, take by weighing 30 parts of polyvinyl acetate, 35 parts of ethyl acetate, 2 parts of magnesium oxide, 8 parts of 5mol / L ammonium chloride solution, and 4 parts of precipitated barium sulfate, for subsequent use;

[0043] S12. First, blend the p...

Embodiment 3

[0051] A kind of PB cold veneer surface control process proposed by the present invention, the PB cold veneer is connected by a composite veneer-plain board-composite veneer through an adhesive I according to the sequence from top to bottom, and finally cold-pressed and formed after After processing, the thickness of the adhesive I between the composite veneer and the plain board is 0.7 mm, and the gluing area is 100%; the adhesive I is composed of epichlorohydrin and polyvinyl alcohol with a mass ratio of 24:11:5:1. , methyl silicone oil and polyetheramine mixed;

[0052] Described PB cold veneer surface control process, specifically comprises the following steps:

[0053] S1. Preparation of composite veneer:

[0054] S11, by weight, take by weighing 40 parts of polyvinyl acetate, 45 parts of ethyl acetate, 3 parts of magnesium oxide, 10 parts of 5mol / L ammonium chloride solution, and 5 parts of precipitated barium sulfate, for subsequent use;

[0055] S12. First, blend the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of wood-based panel manufacturing, in particular to a surface control process for PB cold-laminated panels, which solves the problem that in the prior art, the veneering treatment of PB panels has high requirements on process parameters, and the veneered PB panels produced are subject to the level of production technology. Restriction, problems such as glue opening, blistering, and low bonding strength are prone to occur. The surface control process of the PB cold veneer, the PB cold veneer, in the order from top to bottom, is composed of composite veneer-plain board-composite veneer The surfaces are connected by the adhesive I, and finally cold-pressed and formed after post-processing. In the present invention, the composite veneer, the plain board and the adhesive I are prepared, and the composite veneer-plain board-composite veneer is connected by the adhesive I, and finally the PB cold veneer is prepared by cold pressing; the preparation method of the invention is simple, and cold pressing is adopted. The molding and cold-pressing solidification process has low requirements on process parameters, simple production operation, low preparation cost, and is suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of wood-based panel manufacturing, in particular to a surface control process of a PB cold-laminated panel. Background technique [0002] PB board refers to the use of broken wood or broken wood fiber as the main raw material, the main raw material is cut into pieces of a certain size, after drying, mixed with rubber, hardener, waterproofing agent, etc., and pressed under a certain temperature and pressure. Wood-based board, also known as particle board, particle board, particle board, particle board, bagasse board, etc. PB boards are mainly used in furniture and construction industries, as well as in the manufacture of trains and automobile carriages. [0003] China's PB board production has experienced a repeated process of rising in the 1980s, declining in the 1990s, and then rising again in 2000. After the PB board was abandoned by the market due to poor quality and other reasons, many PB board compani...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B27D1/00B27N3/02B29C48/00B29C48/07C08L31/04C08K3/22C08K3/30C08J5/18C09J129/04C09J171/00C09J183/04C09J11/06
CPCB27D1/00B27N3/02B29C48/0021B29C48/022B29C48/07C08J5/18C09J129/04C09J11/06C08J2331/04C08K2003/222C08K2003/3045C08L83/04C08L71/00C08K5/1515
Inventor 郭亚辉吕亮于西宝
Owner 佳诺威集团(河南)新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap