Environment-friendly hydrotalcite synthesis process
A synthesis process, a technology of hydrotalcite, applied in the directions of aluminum compounds, inorganic chemistry, chemical instruments and methods, etc., can solve the problems of a large amount of waste water and environmental pollution, and achieve the effects of avoiding waste water, saving water resources, and avoiding the production of ammonia
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1
[0024] The present embodiment provides an environment-friendly synthetic hydrotalcite process, the following steps:
[0025] (1) The basic magnesium carbonate, ferrocene after soaking pumice chloroform saturated solution was added to the reaction vessel, was added 10 times the mass of pumice water, stirred for 1 hour;
[0026] (2) The basic magnesium carbonate and aluminum hydroxide molar ratio: 1: 1 ratio weighed aluminum hydroxide, and aluminum hydroxide is added to the kettle and heated to 200 ℃, the reaction 2.5h, after the reaction was cooled to room temperature;
[0027] (3) Step (2) obtained after the reaction solution obtained was filtered and the filtrate cake was recovered as the filtrate in step (1) in the reuse water; removing the filter cake was dried to a moisture content of less than pumice 0.5% or less obtained hydrotalcite finished.
Example Embodiment
[0028] Example 2
[0029] The present embodiment provides an environment-friendly synthetic hydrotalcite process, the following steps:
[0030] 1) The basic magnesium carbonate, ferrocene after soaking pumice chloroform saturated solution was added to the reactor, after addition of water 10 times the mass of pumice, stirred for 1 hour;
[0031] 2) The basic magnesium carbonate and aluminum hydroxide molar ratio: 3: 1 ratio of the weighed aluminum hydroxide, and aluminum hydroxide added to the kettle and heated to 180 ℃, the reaction 5h, cooled to room temperature after the reaction ;
[0032] 3) Step (2) obtained after the reaction solution obtained was filtered and the filtrate cake to recover the filtrate as a step (water 1) is reused; removing the filter cake was dried to a moisture content of less than pumice 0.5% or less finished product obtained hydrotalcite .
Example Embodiment
[0033] Example 3
[0034] The present embodiment provides an environment-friendly synthetic hydrotalcite process, the following steps:
[0035] 1) The basic magnesium carbonate, ferrocene after soaking pumice chloroform saturated solution was added to the reactor, after addition of water 10 times the mass of pumice, stirred for 1 hour;
[0036] 2) The basic magnesium carbonate and aluminum hydroxide molar ratio: 1: 1 ratio weighed aluminum hydroxide, and aluminum hydroxide added to the kettle and heated to 220 deg.] C, the reaction 2.0H, after the reaction was cooled to rt;
[0037] 3) Step (2) obtained after the reaction solution obtained was filtered and the filtrate cake to recover the filtrate as a step (water 1) is reused; removing the filter cake was dried to a moisture content of less than pumice 0.5% or less finished product obtained hydrotalcite .
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap