Acrylate thermal polymerization resin and preparation method thereof
A technology of acrylate and isooctyl acrylate, which is applied in the field of pressure-sensitive adhesives, can solve the problems of resin performance impact, hazardous waste, high energy consumption, etc., and achieve the effects of good adhesion, short reaction time and strong adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example 1
[0018] 10% acrylic acid, 30% acrylate and 29.985% acrylic n-butyl ester monomer were put into reaction vessel, and after 2 hours of nitrogen gas, the thermal initiator was added to 100%, and then heated in a nitrogen gas to 100. When ° C is pre-initiated for 2 hours, and then the temperature is gradually warmed to 150 ° C for 2 hours to obtain an acrylic acid (ester) polymer, and finally add 30% alley octase monomer adjustment system having a viscosity of from 40,000 to 60000 cps / 60 ° C to obtain an acrylate heat Polymer resin.
Example Embodiment
[0019] Example 2
[0020] 15% acrylic, 35% acrylate and 21.98% methacrylate n-butyl methacrylate monomer were put into reaction vessel. After 2 hours of nitrogen gas, the thermal initiator was added 1.02%, and continued to heat it in a nitrogen gas to 100. When the ° C is pre-initiated for 3 hours, and then the temperature is gradually warmed to 150 ° C for 2 hours to obtain an acrylic acid (ester) polymer, and finally the octase monomer of the addition of 28% acrylate is adjusted between 400000000 CPS / 60 ° C to obtain an acrylate thermal polymerization. Resin.
Example Embodiment
[0021] Example 3
[0022] 5% acrylic acid, 30% acrylate, 15% acrylate, and 24.98% acrylic n-butyl ester monomer were put into reaction vessel, and after 2 hours of nitrogen gas, the thermal initiator was added to 0.02%, continued It was pre-initiated to 100 ° C for 3 hours in a nitrogen environment, and then gradually warmed to 150 ° C for 2 hours to obtain an acrylic acid (ester) polymer, and finally the 25% acrylate monomer monomer adjustment viscosity of 30000-60000 cps / 60 ° C. Ester thermal polymerization resin is obtained.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap