Lubricant for high-strength cutting steel wire

A technology for cutting steel wire and lubricants, which is applied in the direction of lubricating compositions and the petroleum industry, etc. It can solve the problems of lubricants with poor antibacterial, anti-mildew and anti-oxidation properties, poor high-temperature resistance of lubricants, and failure to operate normally. Achieve good lubrication effect, extend the storage life cycle, improve the effect of the working range

Inactive Publication Date: 2022-01-18
张家港市耀隆金属制品有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems in the prior art that existing lubricants have poor strength per unit area and cannot be used in high-pressure environments simultaneously. It cannot be used normally, and the existing lubricants have poor antibacterial, anti-mildew and anti-oxidation properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lubricant for high-strength cutting steel wire
  • Lubricant for high-strength cutting steel wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A lubricant for high-strength steel wire cutting, comprising the following components by mass: 10-20 parts of fatty acid glycerides, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, and 2-5 parts of vulcanized asphalt 4-7 parts of oleoyl sarcosine, 2-5 parts of triethanolamine, 4-8 parts of coupling agent, 5-10 parts of complex carboxylic acid and 20-35 parts of deionized water.

[0021] Preferably, it also includes the following ingredients in parts by mass: 3-5 parts of surfactant, 4-6 parts of antibacterial and antifungal agent.

[0022] Preferably, it also includes the following ingredients in parts by mass: 2 parts of oxidized polyether, 12 parts of fatty alcohol polyoxyethylene ether and 2 parts of antioxidant.

[0023] Preferably, it includes the following ingredients in parts by mass: 10-20 parts of fatty acid glycerides, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, 2-5 parts of sulfurized pitch, 4-4 parts of o...

Embodiment 2

[0031] A lubricant for high-strength steel wire cutting, comprising the following components by mass: 10-20 parts of fatty acid glycerides, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, and 2-5 parts of vulcanized asphalt 4-7 parts of oleoyl sarcosine, 2-5 parts of triethanolamine, 4-8 parts of coupling agent, 5-10 parts of complex carboxylic acid and 20-35 parts of deionized water.

[0032] Preferably, it also includes the following ingredients in parts by mass: 3-5 parts of surfactant, 4-6 parts of antibacterial and antifungal agent.

[0033] Preferably, it also includes the following components in parts by mass: 3 parts of oxidized polyether, 13 parts of fatty alcohol polyoxyethylene ether and 3 parts of antioxidant.

[0034] Preferably, it includes the following ingredients in parts by mass: 10-20 parts of fatty acid glycerides, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, 2-5 parts of sulfurized pitch, 4-4 parts of ol...

Embodiment 3

[0042] A lubricant for high-strength steel wire cutting, comprising the following components by mass: 10-20 parts of fatty acid glycerides, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, and 2-5 parts of vulcanized asphalt 4-7 parts of oleoyl sarcosine, 2-5 parts of triethanolamine, 4-8 parts of coupling agent, 5-10 parts of complex carboxylic acid and 20-35 parts of deionized water.

[0043] Preferably, it also includes the following ingredients in parts by mass: 3-5 parts of surfactant, 4-6 parts of antibacterial and antifungal agent.

[0044] Preferably, it also includes the following ingredients in parts by mass: 4 parts of oxidized polyether, 14 parts of fatty alcohol polyoxyethylene ether and 4 parts of antioxidant.

[0045] Preferably, it includes the following ingredients in parts by mass: 10-20 parts of fatty acid glycerides, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, 2-5 parts of sulfurized pitch, 4-4 parts of o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lubricant for a high-strength cutting steel wire. The lubricant comprises the following components in parts by mass: 10-20 parts of fatty glyceride, 10-15 parts of vegetable oil, 5-10 parts of ethylenediamine carboxylate, 2-5 parts of vulcanized asphalt, 4-7 parts of oleoyl sarcosine, 2-5 parts of triethanolamine, 4-8 parts of a coupling agent, 5-10 parts of compound carboxylic acid and 20-35 parts of deionized water. The lubricant has a good lubricating effect, a long lubricating period and good high-temperature resistance, can be widely applied to daily high-temperature work, and effectively avoids the defect that an existing lubricant cannot be synchronously adapted to a high-temperature environment; and a surfactant, an antibacterial and mildew-proof agent and an antioxidant are correspondingly added into the lubricant, so the lubricant has the advantages that good activity of the lubricant is guaranteed, antibacterial, mildew-proof and corrosion-resistant properties of the lubricant are enhanced, the storage and use cycle of the lubricant is prolonged, deterioration and emulsification of the lubricant are avoided, the operation cycle of the lubricant is prolonged, and the use cost of the lubricant is reduced.

Description

technical field [0001] The invention relates to the technical field of cutting steel wires, and more specifically relates to a lubricant for high-strength cutting steel wires. Background technique [0002] Cutting wire is a high-grade steel wire, which can be used to cut various high-precision hard and brittle products. It can be used as an abrasive carrier for multi-wire saws. Cutting wire is a special steel wire. It has many characteristics such as stability, uniformity, high precision, and high strength. At present, it plays a very critical role in the production of silicon wafer cutting. More and more manufacturers are also paying attention to the development of this industry. During the production process, the cutting steel wire needs to cooperate with lubricants for auxiliary production. The lubricant is cutting steel wire The main consumables produced ensure the stable and safe operation of the cutting wire production process. [0003] The prior art has the following...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10N30/06C10N30/08C10N30/10C10N30/16
CPCC10M173/00C10N2040/22C10N2040/246C10N2030/06C10N2030/08C10N2030/10C10N2030/72C10N2030/16C10M2207/283C10M2207/40C10M2215/02C10M2219/022C10M2215/08C10M2215/042C10M2201/02C10M2207/10
Inventor 孙虎
Owner 张家港市耀隆金属制品有限公司