Plant fiber modified fungus powder and preparation method thereof

A plant fiber and fungus technology, which is applied to the field of plant fiber modified fungus powder and its preparation, can solve the problems that the temperature resistance needs to be enhanced, the association effect is lost, the structure is not stable enough, etc., and the temperature resistance performance and reactivity are increased. , the effect of reducing filtration loss

Active Publication Date: 2022-05-27
山东得顺源石油科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some papers and books mention that physical mixing of konjac polysaccharides and plant fiber etherified cellulose is no longer a purely physical mixed solution viscosity in terms of viscosity effect, which can be explained as plant fiber etherified cellulose will destroy konjac The hydrogen bond in the polysaccharide molecule and the binding force with water lead to the viscosity-reducing effect of the two mixtures, and the etherified cellulose of plant fiber and konjac polysaccharide can form a hydrophobic association area, but this structure is not stable enough, and it can only be relieved at high temperature. The speed of carbon chain breakage, the loss of association, and the temperature resistance need to be enhanced. Based on this, the plant fiber cellulose and polysaccharides can be combined through chemical reactions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plant fiber modified fungus powder and preparation method thereof
  • Plant fiber modified fungus powder and preparation method thereof
  • Plant fiber modified fungus powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A preparation method of plant fiber modified fungus powder, which comprises the following steps:

[0025] (1) Pretreatment of plant fiber: Take 50 parts of plant fiber kapok fiber powder, add 5 parts of 1-butyl-3-methylimidazolium tetrafluoroborate, and fully stir and swell at 95°C for 2.5 hours.

[0026] (2) Pretreatment of mushroom seed powder: take 150 parts of oyster mushroom powder, heat up to 45°C, add 20 parts of a mixture of 2% sodium hypochlorite aqueous solution and 15% tetramethylpiperidine oxide solution, and the mass ratio of the two mixtures is 5:1, add 12% sodium silicate solution to adjust the pH value to 9.5, fully react for 0.5h.

[0027] (3) Preparation of plant fiber modified fungus powder: add 100 parts of pretreated kapok flower fiber powder to 100 parts of 20% methanol solution, heat up to 70°C, add 150 parts of pretreated oyster mushroom powder, add 0.07 Parts of tetrabutyl titanate were filled with nitrogen and evacuated, and the reaction was c...

Embodiment 2

[0029] A preparation method of plant fiber modified fungus powder, which comprises the following steps:

[0030] (1) Pretreatment of plant fiber: take 150 parts of plant fiber wheat straw fiber powder, add 10 parts of 1-butyl-3-methylimidazolium tetrafluoroborate, and fully stir and swell at 55°C for 0.5h.

[0031] (2) Pretreatment of fungus powder: take 200 parts of Hericium erinaceus powder, heat up to 55°C, add 40 parts of a mixture of 7% sodium hypochlorite aqueous solution and 5% tetramethylpiperidine oxide solution, and the mass ratio of the two mixtures is 5:8, add 5% sodium silicate solution to adjust the pH value to 10.8, fully react for 4.2h.

[0032] (3) Preparation of plant fiber modified fungus powder: add 200 parts of pretreated wheat straw fiber powder to 50 parts of 55% methanol solution, heat up to 95°C, add 350 parts of pretreated monkey mushroom powder, and add 0.05 parts Tetrabutyl titanate, filled with nitrogen and evacuated, continued to react for 8 hour...

Embodiment 3

[0034] A preparation method of plant fiber modified fungus powder, which comprises the following steps:

[0035] (1) Pretreatment of plant fiber: take 100 parts of plant fiber poplar bark fiber powder, add 7 parts of 1-butyl-3-methylimidazolium tetrafluoroborate, fully stir and swell at 80°C for 2.0h .

[0036] (2) Pretreatment of mushroom seed powder: take 210 parts of shiitake mushroom powder, heat up to 65°C, add 50 parts of a mixture of 3% sodium bromate aqueous solution and 20% sodium chlorate aqueous solution, and the mass ratio of the two mixtures is 1:1 , adding 10% sodium silicate solution to adjust the pH value to 10.5, fully reacting for 3.2h.

[0037](3) Preparation of plant fiber modified fungus powder: add 120 parts of pretreated poplar bark fiber powder to 107 parts of 30% methanol solution, raise the temperature to 105°C, add 250 parts of pretreated shiitake mushroom powder, and add 0.03 parts Tetrabutyl titanate was filled with nitrogen and evacuated, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of oil field drilling fluid treating agents, and discloses plant fiber modified fungus powder and a preparation method thereof, the preparation method comprises the following three steps: (1) pretreatment of plant fibers: adding a swelling agent into plant fiber powder to fully swell; (2) pre-treating the fungus powder: adding a strong oxidizing substance into the fungus powder for reaction; and (3) preparing the plant fiber modified fungus powder: adding the pretreated plant fiber into a reaction solvent, heating, adding the pretreated fungus powder, and adding a catalyst. The plant fiber modified fungus powder is prepared by reaction of pretreated plant cellulose and oxidized fungus powder polysaccharide, not only has a cellulose rigid structure, but also can introduce fungus powder polysaccharide with a plurality of active functional groups, has better properties of temperature resistance, salt tolerance, lubrication, tackifying, filtrate loss reduction and the like, and can be used for preparing the plant fiber modified fungus powder. The material can be used as an excellent environment-friendly raw material in the field of drilling

Description

technical field [0001] The invention relates to the technical field of oilfield drilling fluid treatment agents, in particular to plant fiber modified fungus powder and a preparation method thereof. Background technique [0002] In recent years, a large number of polymer pollutants have entered the ecosystem, which has brought great challenges to the ecological environment. For this reason, renewable natural raw materials continue to receive attention. The inventor found that cellulose is a natural and environmentally friendly material that has active functional groups but is insoluble in water and most organic solvents by consulting a large amount of information. These fiber materials are rich in sources, low in price, and have unique chemical compositions. Feasibility of recycled materials. Cellulose fibers are mainly composed of cellulose, hemicellulose, lignin, etc., and have a large number of active hydroxyl groups. Intramolecular hydrogen bonds and intermolecular hyd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G81/00C09K8/035
CPCC08G81/00C09K8/035C09K2208/08C09K2208/34Y02P20/54
Inventor 王树永李文明李晓静张洁刘相兴臧运刚缪江玉王海锋王新强陈亚飞林海萍康乃静李红蕾高士鲁李远梁飞
Owner 山东得顺源石油科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com