Fiber concrete and preparation method thereof

A technology of fiber concrete and fiber, which is applied in the field of concrete, can solve the problems of reducing concrete strength, water loss, and reducing the toughening effect of natural fibers, so as to reduce the possibility of cracking, improve water retention, and reduce premature aging.

Active Publication Date: 2022-06-14
东莞市建业混凝土有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the fiber filling used in concrete mainly includes natural fiber, glass fiber, polypropylene fiber and steel fiber, etc. Among them, the cost of steel fiber is high and the construction difficulty is relatively large; glass fiber and polypropylene fiber are compared with natural fiber. The price is high, so natural fibers are used, but natural fibers are light and not easy to fill, which makes the filling of natural fibers uneven and reduces the strength of concrete. At the same time, after long-term exposure of concrete, the temperature of concrete increases and water loss , thereby accelerating the aging of natural fibers, reducing the toughening effect of natural fibers, and causing concrete to crack easily

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0047] A water-retaining agent, obtained by the following steps:

[0048] Weigh 32Kg of acrylic emulsion with a solid content of 55%, 5Kg of KH550 silane coupling agent, 1Kg of betaine, 3Kg of sodium carboxymethyl cellulose, 0.5Kg of wetting agent and 58.5Kg of water, mix them evenly, and place them in an ultrasonic wave for 30min. , to obtain a water-retaining agent.

preparation example 2

[0050] A water-retaining agent, obtained by the following steps:

[0051] Weigh 40Kg of acrylic emulsion with a solid content of 50%, 7Kg of KH550 silane coupling agent, 2Kg of betaine, 4Kg of sodium carboxymethylcellulose, 0.8Kg of wetting agent and 46.2Kg of water, mix them evenly, and place them in an ultrasonic wave for 40min. , to obtain a water-retaining agent.

preparation example 3

[0053] A water-retaining agent, obtained by the following steps:

[0054] Weigh 45Kg of acrylic emulsion with a solid content of 45%, 8Kg of KH550 silane coupling agent, 3Kg of betaine, 5Kg of sodium carboxymethyl cellulose, 1Kg of wetting agent and 38Kg of water, mix well, put it into an ultrasonic wave and shake for 60min to obtain Aquasorb.

[0055] Preparation of comparative examples

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of concrete, in particular to a preparation method of fiber concrete. The preparation method comprises the following steps: 1, performing strong acid soaking treatment on plant fibers, then performing strong alkali soaking treatment, and performing shearing and drying to obtain pretreated fibers; 2, the pretreated fibers are weighed and soaked in a water-retaining agent, stirring is conducted for 1-1.5 h, then an antioxidant is added, uniform mixing, heating and stirring are conducted, and modified plant fibers are obtained; 3, the recycled aggregate, the water reducing agent, the inorganic filler, the defoaming agent, the cement, the water, the corrosion inhibitor and the surfactant are weighed and evenly mixed with the modified plant fibers, stirring is conducted for 40-80 min, fiber concrete slurry is obtained, the fiber concrete slurry is poured into a mold to be fixed and formed, and the fiber concrete is obtained and has the good anti-cracking effect.

Description

technical field [0001] The present application relates to the technical field of concrete, and more particularly, to a fiber concrete and a preparation method thereof. Background technique [0002] Fiber reinforced concrete is a cement-based composite material composed of cement slurry, mortar or concrete as the base material and fiber as the reinforcing material. Due to the high tensile strength and elongation of fibers, the tensile, flexural, impact strength, elongation and toughness of concrete can be improved. [0003] At present, the fiber filling used in concrete mainly includes natural fibers, glass fibers, polypropylene fibers and steel fibers. Among them, the cost of steel fibers is high and the construction difficulty is relatively large. Compared with natural fibers, glass fibers and polypropylene fibers are more difficult to fill. The price is high, so natural fibers are used, but natural fibers are light in weight and are not easy to be filled, so that the natu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B20/10
CPCC04B28/00C04B20/1051C04B18/248C04B18/265C04B18/16C04B14/06C04B2103/302C04B18/12C04B14/106C04B2103/50C04B2103/61C04B24/20C04B20/023C04B20/1033C04B20/1048C04B20/1022C04B20/1037Y02W30/91
Inventor 王文董晓朋李泽群林冬明
Owner 东莞市建业混凝土有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products