Water-based high-elasticity organic rubber waterproof paste and preparation method thereof

A technology of organic rubber and waterproof paste, which is applied in the direction of rubber derivative coatings, coatings, and chloroprene homopolymer coatings. It can solve the problems of low strength, poor waterproof and weather resistance of modified asphalt, and poor water resistance. Weather resistance and anti-aging performance, good self-healing and water resistance, high tensile strength

Pending Publication Date: 2022-07-19
广州莱特建材有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, my country's waterproof coatings are generally divided into water-based waterproof coatings and oil-based waterproof coatings. Water-based waterproof coatings generally include polymer cement waterproof coatings, one-component acrylic waterproof coatings, and modified asphalt waterproof coatings. However, these types of water-based waterproof coatings exist. Some defects limit its application value, such as: polymer waterproof coatings have disadvantages such as easy cracking and poor weather resistance; single-component acrylic waterproof coatings have disadvantages such as low strength and poor water resistance; modified asphalt has problems of poor waterproof and weather resistance; oily waterproof The coatings include polyurethane waterproof coatings and polyurea waterproof coatings. These two types of oily waterproof coatings contain harmful substances when they are prepared or used, and their environmental protection indicators do not meet international requirements.
[0003] In the face of the existing problems of waterproof coatings at this stage, it is still an important challenge for researchers to prepare a water-based coating with excellent water resistance and excellent weather resistance, and the raw materials are environmentally friendly and safe, and the use of non-toxic and harmless

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based high-elasticity organic rubber waterproof paste and preparation method thereof
  • Water-based high-elasticity organic rubber waterproof paste and preparation method thereof
  • Water-based high-elasticity organic rubber waterproof paste and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0060] A second aspect of the present invention provides a method for preparing a water-based high-elasticity organic rubber waterproof paste, comprising the following steps:

[0061] 1) Add ionized water to the reactor, turn on the high-speed disperser, and rotate at 300-500r / min;

[0062] 2) Add a wetting dispersant and disperse for 5-10min;

[0063] 3) Add preservative and continue to disperse for 5-10min;

[0064] 4) Add rutile titanium dioxide, nano-zinc oxide, kaolin and micro-silica powder in turn, adjust the speed of high-speed dispersant to 800-1200r / min, and disperse for 30-60min;

[0065] 5) Add acrylic emulsion, modified styrene-butadiene resin, and chloroprene emulsion to disperse for 5-10min;

[0066] 6) Add defoamer, and crosslinking agent is dispersed for 10-20min;

[0067] 7) Add water repellent and continue to disperse for 5-20min;

[0068] 8) Add emulsified asphalt and fumed silica, disperse for 10-30min, and obtain the product of the present invention a...

Embodiment 1

[0073] A water-based high-elasticity organic rubber waterproof paste, the raw materials for preparing, in parts by weight, include: 10 parts of chloroprene emulsion, 15 parts of modified styrene-butadiene resin, 20 parts of acrylic emulsion, 10 parts of emulsified asphalt, and 0.1 part of wetting dispersant , 0.3 part of crosslinking agent, 0.3 part of defoamer, 0.2 part of anti-flash rust agent, 0.2 part of preservative, 5 parts of nano-zinc oxide, 10 parts of rutile titanium dioxide, 10 parts of calcined kaolin, 10 parts of microsilica, water repellent 0.5 part of the agent, 8.2 parts of deionized water, and 0.2 part of fumed silica.

[0074] The chloroprene emulsion, model 618, was purchased from Guangzhou Jiacheng New Material Co., Ltd.

[0075] Described modified styrene-butadiene emulsion, model ECO 7623, purchased from BASF, Germany;

[0076] The acrylic emulsion, model BLJ-6838, was purchased from Shanghai Baolijia New Material Co., Ltd.;

[0077] Described emulsif...

Embodiment 2

[0095] A water-based high-elasticity organic rubber waterproof paste, the raw materials for preparing, in parts by weight, include: 15 parts of chloroprene emulsion, 10 parts of modified styrene-butadiene resin, 20 parts of acrylic emulsion, 10 parts of emulsified asphalt, and 0.1 part of wetting dispersant , 0.3 part of crosslinking agent, 0.3 part of defoamer, 0.2 part of anti-flash rust agent, 0.2 part of preservative, 5 parts of nano-zinc oxide, 10 parts of rutile titanium dioxide, 10 parts of calcined kaolin, 10 parts of microsilica, water repellent 0.5 part of the agent, 8.2 parts of deionized water, and 0.2 part of fumed silica.

[0096] The chloroprene emulsion, model 618, was purchased from Guangzhou Jiacheng New Material Co., Ltd.

[0097] Described modified styrene-butadiene emulsion, model ECO 7623, purchased from BASF, Germany;

[0098] The acrylic emulsion, model BLJ-6838, was purchased from Shanghai Baolijia New Material Co., Ltd.;

[0099] Described emulsif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of organic rubber waterproof paste, and particularly relates to water-based high-elasticity organic rubber waterproof paste and a preparation method thereof. The water-based high-elasticity organic rubber waterproof paste at least comprises the following preparation raw materials: an organic emulsion and emulsified asphalt, the organic emulsion comprises at least one of benzene ring-containing emulsion, acrylic emulsion, organic silicon emulsion and neoprene emulsion. The water-based high-elasticity organic rubber waterproof paste prepared by the invention has the characteristics of high tensile strength, high elongation, self-healing property and good water resistance; the water-based high-elasticity organic rubber waterproof paste prepared by the preparation method disclosed by the invention has relatively good weather resistance and ageing resistance.

Description

technical field [0001] The invention belongs to the field of organic rubber waterproof paste, and more particularly relates to a water-based high-elasticity organic rubber waterproof paste and a preparation method thereof. Background technique [0002] At present, my country's waterproof coatings are generally divided into water-based waterproof coatings and oil-based waterproof coatings. Water-based waterproof coatings generally include polymer cement waterproof coatings, one-component acrylic waterproof coatings, and modified asphalt waterproof coatings. However, these types of water-based waterproof coatings exist. Some defects limit its application value, such as: polymer waterproof coating has shortcomings such as easy cracking and poor weather resistance; one-component acrylic waterproof coating has disadvantages such as low strength and poor water resistance; modified asphalt has the problem of poor waterproof and weather resistance; oily waterproof The coatings include...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D111/02C09D115/00C09D195/00C09D7/61
CPCC09D133/00C09D111/02C09D115/00C09D7/61C09D7/70C09D7/67C08L2201/08C08K2201/011C08K2003/2296C08K2003/2241C08L11/02C08L15/00C08L95/00C08K7/26C08K3/22C08K3/346C08K3/36C08L33/00
Inventor 苏文就
Owner 广州莱特建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com