Furniture coating with quick-drying and high weather resistance and preparation method thereof

A furniture coating and performance technology, applied in the field of coatings, can solve the problems of slow drying speed, limited coating use, and low quick-drying efficiency, and achieve the effects of enhanced modification efficiency, enhanced quick-drying performance, and enhanced connection effect

Inactive Publication Date: 2022-08-02
佛山市高明区首邦化工有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing water-based polyurethane coatings are used in furniture, and the surface-drying and hard-drying speeds are slow, which limits the use of coatings. At the same time, the product needs to dry quickly in hot, humid weather, and for low-temperature, low-humidity weather, the quick-drying efficiency Very low, in order to improve the quick-drying efficiency of the product and at the same time take into account the weather resistance of the product, based on this, the present invention further improves the treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The preparation method of the modified carbon nanotubes of the present embodiment is:

[0044] S01: the carbon nanotubes are placed in a proton irradiation box for irradiation treatment, and the irradiation is completed to obtain irradiated carbon nanotubes;

[0045]S02: Add 20-30 parts of irradiated carbon nanotubes to 45-55 parts of ethanol solvent first, then add 1-3 parts of lanthanum sulfate solution and stir at 55-65°C for 30-40min, and the stirring speed is 300 -350r / min, the stirring is over, keep warm, and reserve;

[0046] S03: Then add 5-10 parts of β-cyclodextrin and 0.2-0.7 parts of potassium persulfate to the product of S02, raise the temperature to 65-75°C, and continue stirring at a speed of 650-750r / min for 1-2h, After stirring, the modified carbon nanotubes are obtained by washing with water and drying.

[0047] The irradiation processing power of S01 in this embodiment is 320-350W, and the irradiation time is 2-6min.

[0048] The mass fraction of t...

Embodiment 1

[0062] A kind of furniture coating with quick-drying and high weather resistance of the present embodiment comprises the following raw materials in parts by weight:

[0063] 35 parts of water-based polyurethane resin, 15 parts of modified carbon nanotubes, 5 parts of graphene synergist, 3 parts of wetting agent, 1 part of film-forming aid, 1 part of dispersant, and 40 parts of deionized water.

[0064] The preparation method of the modified carbon nanotubes of the present embodiment is:

[0065] S01: the carbon nanotubes are placed in a proton irradiation box for irradiation treatment, and the irradiation is completed to obtain irradiated carbon nanotubes;

[0066] S02: firstly add 20 parts of irradiated carbon nanotubes to 45 parts of ethanol solvent, then add 1 part of lanthanum sulfate solution and stir at a temperature of 55°C for 30min, the stirring speed is 300r / min, the stirring is completed, keep warm, and stand by;

[0067] S03: then add 5 parts of β-cyclodextrin and...

Embodiment 2

[0083] A kind of furniture coating with quick-drying and high weather resistance of the present embodiment comprises the following raw materials in parts by weight:

[0084] 45 parts of water-based polyurethane resin, 25 parts of modified carbon nanotubes, 10 parts of graphene synergist, 6 parts of wetting agent, 3 parts of film-forming aids, 2 parts of dispersant, and 50 parts of deionized water.

[0085] The preparation method of the modified carbon nanotubes of the present embodiment is:

[0086] S01: the carbon nanotubes are placed in a proton irradiation box for irradiation treatment, and the irradiation is completed to obtain irradiated carbon nanotubes;

[0087] S02: add 30 parts of irradiated carbon nanotubes into 55 parts of ethanol solvent first, then add 3 parts of lanthanum sulfate solution and stir at a temperature of 65 ° C for 40 min, the stirring speed is 350 r / min, the stirring is completed, keep warm, and stand by;

[0088] S03: then add 10 parts of β-cyclod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of furniture coatings, and particularly discloses a quick-drying and high-weather-resistance furniture coating and a preparation method thereof.The coating is prepared from, by weight, 35-45 parts of waterborne polyurethane resin, 15-25 parts of modified carbon nanotubes, 5-10 parts of a graphene synergist, 3-6 parts of a wetting agent, 1-3 parts of a coalescing agent, 1-2 parts of a dispersing agent and 40-50 parts of deionized water. According to the furniture coating, the waterborne polyurethane resin serves as a base material, the modified carbon nanotubes and the graphene synergist are added to enhance the quick-drying and weather resistance of a product, the furniture coating prepared through cooperation of the wetting agent, the dispersing agent and the coalescing agent has excellent performance, the modified carbon nanotubes are added to enhance the quick-drying effect of the product, and the graphene synergist is added to enhance the weather resistance of the product. By adding the graphene synergist, the effect of assisting in synergism is achieved, the weather resistance of the product is enhanced while the quick-drying performance is enhanced, and the performance of bi-directionally coordinating the product is achieved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a furniture coating with fast drying and high weather resistance and a preparation method. Background technique [0002] Water-based paints include three types: water-soluble paints, water-dilutable paints, and water-dispersible paints (latex paints). Water-soluble coatings use water-soluble resins as film-forming materials, represented by polyvinyl alcohol and its various modifications, in addition to water-soluble alkyd resins, water-soluble epoxy resins, and inorganic polymer water-based resins; Any paint that uses water as a solvent or as a dispersion medium can be called water-based paint. [0003] The existing water-based polyurethane coatings are used in furniture, and the surface drying and actual drying speed are slow, which limits the use of coatings. At the same time, the products need to dry quickly in hot and humid weather, while for low temperature and low humidit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/62
CPCC09D175/04C09D7/62C08K2201/011C08K9/08C08K3/041C08K9/02C08K3/042C08K9/06Y02P20/10
Inventor 程军峰彭鹏鸿
Owner 佛山市高明区首邦化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap