Hard polyvinyl chloride active impact resistant assistants

A technology of rigid polyvinyl chloride and coagent, applied in the field of anti-impact coagent, which can solve the problems of affecting performance and reducing tensile strength, and achieve the effects of improving compatibility, improving tensile performance and increasing dosage

Inactive Publication Date: 2005-06-15
四川新元材料工程研究所
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of use, it was found that although these impact resistance additives can improve the impact resistance of rigid polyvinyl chloride (UPVC) products, but at the same time bring about a significant decrease in tensile strength, which directly affects the performance of its products, such as water supply Pressure resistance of fittings and tubing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Use 4 parts of porous flake-shaped V-type polyvinyl chloride micropowder, 3 parts of ultrafine activated calcium carbonate or 5 parts of nano-scale activated calcium carbonate with a maximum particle size of no more than 30 microns and an average particle size of no more than 10 microns, in the mixer Mix evenly in the medium to prepare polyvinyl chloride anti-impact active additive. With the anti-shock active auxiliary agent of the present invention as the anti-impact auxiliary agent, the following formula can be adopted for the production of PVC-U water supply pipe fittings: 100 parts of VII type PVC, 7 parts of anti-impact active auxiliary agent, 3 parts of processing aid, ordinary precipitated carbonic acid 5 parts of calcium, 2 parts of titanium dioxide, 6 parts of bear brand EP2305 stabilizer. After the kneaded raw materials are injection molded, various specifications of PVC-U water supply pipe fittings with a diameter of 63 to 110 mm can be produced with all indi...

Embodiment 2

[0020] Use 4 parts of porous flake-shaped V-type polyvinyl chloride micropowder, 3 parts of ultrafine activated calcium carbonate or 5 parts of nano-scale activated calcium carbonate with a maximum particle size of no more than 30 microns and an average particle size of no more than 10 microns, in the mixer Mix evenly in the medium to prepare polyvinyl chloride anti-impact active additive. Using the anti-shock active auxiliary agent of the present invention as the anti-impact auxiliary agent, the following formula can be adopted for the production of PVC-U water supply pipe fittings: 100 parts of VII type PVC, 4 parts of active anti-impact auxiliary agent, 1.5 parts of processing aid, ordinary precipitated carbonic acid 5 parts of calcium, 2 parts of titanium dioxide, 4.8 parts of bear brand EP2305 stabilizer. After the kneaded raw materials are injection molded, various specifications of PVC-U water supply pipe fittings with a diameter of 16 to 50mm can be produced with all i...

Embodiment 3

[0022] Adopt 6 parts of porous sheet-like VII type polyvinyl chloride micropowder, 2.5 parts of superfine or nano-scale unactivated calcium carbonate with a maximum particle size of not more than 30 microns and an average particle size of not more than 10 microns, and mix them uniformly in a mixer. That is, the polyvinyl chloride anti-impact active additive is obtained. Using the anti-shock active auxiliary agent of the present invention as the anti-impact auxiliary agent, the following formula can be adopted for the production of PVC-U drainage pipe fittings: 100 parts of VII type PVC, 5 parts of active anti-impact auxiliary agent, 2.5 parts of processing aid, ordinary precipitated carbonic acid 15 parts of calcium, 2 parts of titanium dioxide, 4.8 parts of bear brand EP2305 stabilizer. After the kneaded raw materials are injection molded, various specifications of PVC-U drainage pipe fittings with a diameter of 90 to 110 mm can be produced, with all indicators meeting the na...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A kind of active auxiliary agent that can be used to improve the impact resistance of rigid polyvinyl chloride. Modified organic materials and inorganic materials are compounded. The appearance of the additive is white powder, which is easy to mix with the base material; on the premise of basically maintaining the original tensile strength of PVC, it can effectively improve the impact resistance of PVC products; it can promote plasticization and improve the processing performance of UPVC; The micro-crosslinking generated by the activity can also improve the comprehensive mechanical properties and heat resistance of the product; at the same time, using it can reduce the amount of processing aids and increase the amount of inorganic materials under the premise of ensuring the quality of the product, so it can effectively reduce the material of the product. cost. The UPVC impact-resistant active auxiliary has significant economic and social benefits.

Description

1. Technical field [0001] The invention relates to a general polymer plastic and its molding process. More specifically, the present invention relates to an anti-impact active additive for improving the impact resistance of rigid polyvinyl chloride products. 2. Background technology [0002] Polyvinyl chloride (PVC) is an important general-purpose plastic, accounting for about 27% of the total plastic, and its output ranks second in the world's resin production, second only to polyethylene. PVC has many excellent properties, such as high strength, flame retardant, good transparency, chemical corrosion resistance, low price, etc., but rigid PVC has high melting point, high viscosity, poor thermal stability, and difficult molding process. The product is brittle, so processing and application are limited. In order to improve the thermal stability of PVC and improve the mechanical properties and appearance of products, various additives need to be added, among which anti-impac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K3/34C08L27/06
Inventor 林伟雷勇
Owner 四川新元材料工程研究所