Lithopone

A technology of barite powder and zinc sulfide, which is applied in the field of coloring raw materials for interior and exterior wall paint, can solve the problem of limited use range of lithopone, and achieve good anodic passivation effect, good wear resistance and good rust resistance. Effect

Inactive Publication Date: 2007-04-25
范斌远
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when lithopone is used as a coloring raw material for exterior wall paint, in the natural environment, the wall paint is easily pulverized due to the soaking of wind and rain, which limits the scope of use of lithopone.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Take 3Kg of kaolin, grind it with a 400-mesh pulverizer or use a nylon filter cloth (under 200 mesh) after screening, add 17.5Kg of zinc sulfide, 30Kg of phosphorus-zinc white, 0.5Kg of zinc oxide, 3Kg of silicon dioxide, 40Kg of precipitated calcium carbonate, Barite powder 3Kg, precipitated barium sulfate 3Kg, mix and stir with low-speed mixer for 10 - Stir for 15 minutes until evenly to obtain the Lido powder of the present invention.

Embodiment 2

[0010] Take 2Kg of kaolin, grind it with a 400-mesh pulverizer or use a nylon filter cloth (under 200 mesh) after screening, add 36.5Kg of zinc sulfide, 15Kg of phosphorus-zinc white, 0.5Kg of zinc oxide, 3Kg of silicon dioxide, 38Kg of precipitated calcium carbonate, Barite powder 3Kg, precipitated barium sulfate 2Kg, mix and stir with a low-speed mixer for 10 - Stir for 15 minutes until evenly to obtain the Lido powder of the present invention.

Embodiment 3

[0012] Take 3Kg of kaolin, grind it with a 400 mesh mill or use a nylon filter cloth (under 200 mesh) after screening, add 6.5Kg of zinc sulfide, 30Kg of phosphorus zinc white, 0.5Kg of zinc oxide, 10Kg of silicon dioxide, 40Kg of precipitated calcium carbonate, Barite powder 3Kg, precipitated barium sulfate 7Kg, mix and stir with a low-speed mixer for 10 - Stir for 15 minutes until evenly to obtain the Lido powder of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses one kind of lithopone, and the lithopone features its composition comprising zinc sulfide 6.5-36.5 (in weight portions, the same below), hopeite white 2-30, zinc oxide 0.5, silica 2-10, deposited calcium carbonate 15-40 wt%, barite powder 3, kaolin 3, and deposited barium sulfate 2-7. The lithopone of the present invention has high antirust performance, high corrosion retarding performance, high anode deactivating effect, high acid and alkali resistance, high wear resistance, high chemical stability and high adhesion.

Description

technical field [0001] The invention belongs to the field of coloring raw materials, in particular to a coloring raw material suitable for indoor and outdoor wall paints. Background technique [0002] At present, the coloring raw material of domestic wall paint is mainly lithopone (also known as: lithopone), which has the advantages of alkali resistance and heat resistance. However, when lithopone is used as a coloring raw material for exterior wall paint, in the natural environment, the wall paint is easily pulverized due to the soaking of wind and rain, which limits the range of use of lithopone. Contents of the invention [0003] The object of the present invention is to provide a Lido powder, which has good adhesion, strong wear resistance, and good anti-corrosion and anti-rust performance. [0004] For reaching above-mentioned purpose, the present invention provides a kind of Lithol powder, it is characterized in that described Lithol powder is composed of zinc sulfi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D17/00
Inventor 范斌远
Owner 范斌远
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com