Plant polysaccharide sponge body and its preparation method

A technology of plant polysaccharides and sponges, which is applied in the field of preparation of plant polysaccharides and sponges, can solve problems such as inability to realize industrial production, fail to meet the use requirements, and complex processes, and achieve light weight, strong water or oil absorption, and low production costs. low effect

Inactive Publication Date: 2003-04-16
姜发堂
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although cotton fiber sponges that have not yet been industrially produced can be degraded, their high cost, complex process, internal structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] 1. Mix 60 parts of coarsely broken corn kernels, 2 parts of modifiers glyoxal, phosphorus oxychloride, benzyl chloride, castor oil and toluene diisocyanate, and 10 parts of water (60:10:10 by weight) and mix well , into a single-screw extruder, the screw D / L value is 25, the three-stage temperature is 95 ° C, 130 ° C, 160 ° C, and the rotation speed is 120 RPM. After extrusion, crush to 60 mesh for later use.

[0017] 2, with various raw materials by weight percentage: bamboo pulp fiber 10, modified cornstarch (i.e. the product of step 1) 70, plasticizer calcium stearate (zinc) 1, softening agent (methyl silicone oil) 2, hair Foaming agent (azodicarbonamide) 7, preservative (potassium behenate) 0.3, waterproofing agent (wax emulsion) 2, filler (calcium carbonate) 7.7, and mix evenly in a mixer.

[0018] 3. Send the uniformly mixed materials into the twin-screw extruder. The process parameters of the twin-screw extruder are: the screw D / L value is 20, the temperature of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A phytopolyose sponge is prepared from phytopolyose through adding filler, plasticizer, softening agent, foaming agent, water-proofing agent and antiseptic, high-temp. fusing-plasticizing and puffingin an extruder ,and shaping by die extruding.

Description

technical field [0001] The invention relates to a high-temperature extruded and expanded plant polysaccharide sponge, and also relates to a preparation method of the plant polysaccharide sponge. Background technique [0002] With the further development of industrial civilization, people's awareness of environmental protection of industrial products is getting stronger and stronger, and the requirements for environmental protection are getting higher and higher. At present, the sponge products on the market are mainly polyurethane sponge products. Whether it is a large amount of organic solvents used in the production process of such products, or the residue of solvents in the products, it has caused a great negative impact on the living environment and living environment of human beings, and even endangers the health of users. Polyurethane sponge products are non-biodegradable and non-recyclable. The direct consequence is that the amount of solid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08B31/00C08J9/00
Inventor 姜发堂李冬生袁世矩
Owner 姜发堂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap