Wet process sulfide mineral leaching-out method

A sulfide ore, all-wet technology, applied in the direction of improving process efficiency, can solve problems such as large resistance, and achieve the effects of low energy consumption, fast leaching speed, and mild reaction conditions

Inactive Publication Date: 2003-11-19
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the vast majority of micro-batteries located inside the mineral are in a closed state under normal conditions (such as pressurized heating, catalysis, etc.), so they do not work; Some defects, such as too much resistance in the loop, etc., also have little effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0008] Example 1: Add 200g of zinc sulfide mineral powder to the reactor, add 0.2g of copper sulfate, and 30g of water, mix well, heat to 70°C, and oxidize with air, control the end point pH to 2, and the leaching rate of zinc is 95% .

example 2

[0009] Example 2: Add 200g of zinc sulfide ore powder, 1.2g of copper chloride, and 500g of water into the reactor, mix well, heat to 90°C, oxidize with oxygen, control the end point pH to 1, and the zinc leaching rate is 95 %.

example 3

[0010] Example 3: Add 200g of zinc sulfide ore powder, 0.2g of lead nitrate, and 36g of water into the reactor, mix well, heat to 75°C, oxidize with air, control the pH at the end point to 6, and the leaching rate of zinc is 95% .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A process for leaching sulfide ore by full-wet method includes such steps as mixing the sulfide ore with additive, adding water, reacting at 10-150 deg.C while controlling the final pH to 0-14, and oxidizing by adding oxidizing agent. Said ore is the sulfuride of Cu, Ni, Co, or Zn. Said additive is the water-soluble compound of Cu, Pb, and Co, etc. Said oxidizing agent may be air O2, H2O2, etc. Its advantage is high leaching speed.

Description

technical field [0001] The invention belongs to the technical field of sulfide ore hydrometallurgy, and in particular provides a full wet leaching method of sulfide ore. Background technique [0002] At present, the hydrometallurgy of sulfide ores includes wet method, full wet method, heap leaching and bioleaching methods. The full wet method includes pressure leaching, catalytic leaching, etc. Due to the roasting process involved in the traditional wet process, there is a large amount of SO 2 Gas generation requires SO 2 The recovery device makes the whole process a large investment and complicated process. Pressure leaching, catalytic leaching, heap leaching and biological leaching have been paid attention to at home and abroad because of eliminating the pollution of sulfur dioxide and improving the environment, among which pressure leaching is particularly attractive. The existing pressure leaching method was born and developed in the 1950s. In 1954, the Canadian Sher...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B3/04
CPCY02P10/20
Inventor 邹兴
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products