Multifuntional green environmental protection nanometer titania coating and preparing method thereof

A nano-titanium dioxide, green and environmentally friendly technology, applied in the direction of coating, can solve the problems of unenvironmental protection, poor stain resistance, poor weather resistance, etc., and achieve the effect of high cost performance and excellent weather resistance

Inactive Publication Date: 2005-02-23
RESEARCH INSTITUTE OF TSINGHUA UNIVERSITY IN SHENZHEN
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a multifunctional green and environment-friendly nano-titanium dioxide coating and its preparation method. The coating can not only solve the technical problems of existing coatings such as poor stain resistance, poor weather resistance, and non-environmental protection, but also endow the coating with self-cleaning, sterilization and disinfection. , air purification and other new functions, it is a multi-functional green environmental protection coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The formula prepared in this embodiment is:

[0037] Tap water: 300 kg; Dispersant: 8 kg;

[0038] Defoamer: 4 kg; Thickener: 20 kg;

[0039] Leveling agent: 10 kg; Coalescing agent: 15 kg;

[0040] Wetting and dispersing agent: 0.2 kg Styrene-acrylic emulsion: 150 kg

[0041] Titanium dioxide: 60 kg; ultra-fine aluminum silicate: 20 kg;

[0042] Talc powder: 80 kg; Lithopone: 140 kg;

[0043] Heavy calcium carbonate: 100 kg; Light calcium carbonate: 100 kg;

[0044] Nano-titanium dioxide dispersion: 40 kg.

[0045] Its concrete preparation method is:

[0046] (1) Mix uniform nano-titanium dioxide dispersion, film-forming aid, leveling agent, dispersant, wetting and dispersing agent, defoamer, water, titanium dioxide, ultrafine aluminum silicate, talcum powder, lithopone , heavy calcium carbonate, and light calcium carbonate were weighed and added to the mixing tank, stirred evenly, and the rotating speed was controlled at 1200r / min, and stirred for 30min to obta...

Embodiment 2

[0054] The formula prepared in this embodiment is:

[0055] Tap water: 100 kg; Dispersant: 5 kg;

[0056] Defoamer: 1 kg; Thickener: 1 kg;

[0057] Leveling agent: 1 kg; Coalescing agent: 5 kg;

[0058] Wetting and dispersing agent 0.5 kg Vinegar acrylic emulsion: 400 kg

[0059] Ultrafine aluminum silicate: 10 kg; titanium dioxide: 300 kg;

[0060] Talc powder: 40 kg; Lithopone: 20 kg;

[0061] Heavy calcium carbonate: 50 kg; Light calcium carbonate: 50 kg;

[0062] Nano-titanium dioxide dispersion: 10 kg.

[0063] Its concrete preparation method is:

[0064] (1) Mix uniform nano-titanium dioxide dispersion, wetting and dispersing agent, film-forming aid, leveling agent, dispersing agent, defoamer, water, titanium dioxide, ultrafine aluminum silicate, lithopone, heavy Calcium carbonate and light calcium carbonate were respectively weighed and added to the mixing tank, stirred evenly, the rotating speed was controlled at 1200r / min, and stirred for 20min to obtain a slurry...

Embodiment 3

[0072] The formula prepared in this embodiment is:

[0073] Tap water: 100 kg; Dispersant: 12 kg;

[0074] Defoamer: 5 kg; Thickener: 15 kg;

[0075] Leveling agent: 15 kg; Coalescing agent: 10 kg;

[0076] Wetting and dispersing agent 1 kg; pure acrylic emulsion: 300 kg

[0077] Nano-titanium dioxide dispersion: 100 kg; titanium dioxide: 100 kg;

[0078] Talc powder: 100 kg; Ultrafine aluminum silicate: 50 kg;

[0079] Wollastonite powder: 120 kg; light calcium carbonate: 130 kg.

[0080] Its concrete preparation method is:

[0081] (1) Mix uniform nano-titanium dioxide dispersion, wetting and dispersing agent, film-forming aid, leveling agent, dispersing agent, defoaming agent, water, titanium dioxide, ultrafine aluminum silicate, talc powder, wollastonite powder , light calcium carbonate were respectively weighed and added to the mixing tank, stirred evenly, the rotating speed was controlled at 2000r / min, and stirred for 40min to obtain a slurry;

[0082] (2) Grindin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention is that a kind of multi-functional green nanometer two of environmental protection is oxidized Titanium coating and method of preparing, this coating can not merely be solved now. There is coating that is able to bear staining difference, is able to bear waiting difference, not the skills, such as environmental protection, etc. Skill question, it is clean to give the coating at the same time, disinfect and disinfect, Purify new functions, such as air, etc., it is the green environmental protection of more than one kind of kinetic energy Coating. Coating this by titanium white powder, exceed detailed silicic acid aluminium, nanometer Oxidize the titanium and disperse the liquid two times, the calcium carbonate of light quality, the calcium carbonate of heavy quality, Silicon lime powder, lithopone, talc powder, dispersant is moist. It is the dispersant, thickener, disappear and steep and pharmaceutical, become membrane auxiliary, flow flat pharmaceuticla, water, the cream base material, etc. make up, it is simple to prepare the craft. The cost performance is high, have very good economic benefits and social result Benefit.

Description

technical field [0001] The patent of the invention relates to the field of architectural coatings, in particular to a multifunctional green and environment-friendly nano-titanium dioxide coating and a preparation method thereof. Background technique [0002] At present, my country's architectural coatings generally have low-grade products, short service life, easy to stain, and poor weather resistance. Whether the technical problems such as poor weather resistance and easy staining can be solved is the key to whether the exterior wall coating can be widely used. [0003] With the improvement of people's living standards, higher requirements are put forward for architectural coatings. It is required that architectural coatings not only have decorative functions, but also have new functions such as sterilization, air purification, and radiation protection. [0004] Nano-titanium dioxide has stable chemical properties, oxidation resistance, safety and non-toxicity, and long s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D183/04
Inventor 李荣先陈丽琼
Owner RESEARCH INSTITUTE OF TSINGHUA UNIVERSITY IN SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com