Preparation method of whisker and pacticle toughening ceramic base composite

A technology for composite materials and toughened ceramics, which is applied in the field of preparation of whiskers and granular ceramic matrix composite materials, can solve the problems of low performance, limited application range of hot pressing sintering, low performance of composite materials, etc., and achieve good performance and designability Strong, toughness-increasing effect

Active Publication Date: 2005-03-23
XIAN XINGUI CERAMIC COMPOSITE MATERIAL CO LTD
View PDF0 Cites 74 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] In order to overcome the low performance of the composite material caused by the difficulty of evenly dispersing the composite material in the prior art, it is difficult to obtain large, complex and thin-walled whiskers and the green body of the particle composite material, and there is no pressure-sint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of whisker and pacticle toughening ceramic base composite
  • Preparation method of whisker and pacticle toughening ceramic base composite
  • Preparation method of whisker and pacticle toughening ceramic base composite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] This example is the preparation of silicon carbide whisker toughened silicon carbide ceramic matrix composite material.

[0031] Silicon carbide whiskers with a diameter of 1.5 μm and an aspect ratio of 8 to 10 are selected as the reinforcement, 5% PVA aqueous solution is used as the prefabricated binder, and the phenolic resin ethanol solution is used as the granulation binder, and the concentration of the solution is 0.5 g / ml.

[0032] During preparation, mix 150g of silicon carbide whiskers with 100ml of phenolic resin solution, press and crush it four times with a pressure of 10-20MPa, dry in the shade at room temperature for 24 hours, and dry at 120°C for 2 hours. After crushing, sieving and granulation, the granule group with a diameter of 0.6-1.0mm is selected to be mixed with 15-30%wt PVA aqueous solution, and prefabricated under a pressure of 3-8MPa. The molded preform was dried in the shade at room temperature for 24 hours, dried at 120°C for 2 hours, and the...

Embodiment 2

[0035] This example is the preparation of silicon nitride particle toughened silicon nitride ceramic matrix composite material

[0036] Silicon nitride powder with a diameter of 6 μm is selected as the particle reinforcement, 5% PVA aqueous solution is used as the prefabricated binder, and phenolic resin ethanol solution is used as the granulation binder, and the concentration of the solution is 0.5g / ml.

[0037] During preparation, mix 150g of silicon nitride powder with 50ml of phenolic resin solution, press and crush it four times with a pressure of 10-20MPa, dry in the shade at room temperature for 24 hours, and dry at 120°C for 2 hours. After crushing, sieving and granulation, the granule group with a diameter of 0.6-1.0mm is selected to be mixed with 10-25%wt PVA aqueous solution, and prefabricated under a pressure of 3-8MPa. The molded preform was dried in the shade at room temperature for 24 hours, dried at 120°C for 2 hours, and then placed in a deposition furnace to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

A crystal whisker and particle toughened ceramic-based composition used to make large thin-wall member is prepared through granulating to prepare the coagulated substance of crystal whiskers and particles, preparing the prefabricated body of crystal whisker-particle reinforcing body, and depositing the ceramic base in said prefabricated body by chemical vapour osmosis process.

Description

(1) Technical field: [0001] The invention relates to a method for preparing a whisker and granular ceramic matrix composite material. (two) background technology: [0002] Ceramic matrix composites are a new generation of strategic thermal structural materials that replace metals. Their outstanding advantages are high temperature resistance and low density, and they have broad application prospects in aviation, aerospace and other fields. Ceramic matrix composites mainly have three toughening methods: continuous fiber, whisker and particle toughening. Among them, fiber toughened composites have fracture behavior similar to technology, are not sensitive to cracks, and have high reliability characteristics that will not cause catastrophic damage. , while whisker and particle composites are characterized by low cost. Therefore, the three composite materials of fibers, whiskers and particles constitute a complete ceramic matrix composite system, and they all play an important r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/565C04B35/622C04B35/634C04B35/80
Inventor 成来飞张立同徐永东刘永胜李镇王晓明
Owner XIAN XINGUI CERAMIC COMPOSITE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap