Clay acrylic surface decorating material and its preparing method

A surface decoration, acrylic technology, applied in the direction of coating, can solve the problem of no pigment, etc., achieve the effect of low cost, delicate and natural texture, and improve economic value

Inactive Publication Date: 2005-12-21
TONGJI UNIV
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] On the other hand, many buildings advocate natural style at present, and hope that the exterior wall decoration materials to be decorated do not have pigments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: The group distribution ratio is as follows:

[0024] Clay powder: 560g

[0025] Acrylic emulsion: 335g

[0026] Sodium hexametaphosphate: 6g

[0027] Sodium Benzoate: 6g

[0028] Ethylene glycol: 27g

[0029] Propylene glycol: 42g

[0030] Methylcellulose: 5g

[0031] Titanium dioxide: 17g

[0032] Dimethicone: 2g

[0033] According to above-mentioned ratio of raw material, according to the surface decoration material that the aforementioned process step makes, its performance index is:

[0034] Drying time: 1.9 hours,

[0035] Adhesion strength: 0.51MPa,

[0036] Water resistance: After 48 hours of testing, the surface of the decorative material has no bubbles, cracks, or peeling off.

[0037] Alkali resistance: After 48 hours of testing under the condition of saturated calcium hydroxide solution, there is no bubble on the surface,

[0038] Scrub resistance: After 500 times of scrubbing test, there is no bottom phenomenon,

[0039] Cold resist...

Embodiment 2

[0041] Embodiment 2: the group distribution ratio is as follows:

[0042] Clay powder: 555g

[0043] Acrylic emulsion: 345g

[0044] Sodium hexametaphosphate: 6g

[0045] Sodium Benzoate: 5g

[0046] Ethylene glycol: 25g

[0047] Propylene glycol: 44g

[0048] Methylcellulose: 5g

[0049] Titanium dioxide: 14g

[0050] Polydimethylsiloxane: 1g

[0051] According to above-mentioned raw material ratio, look for the surface decoration material that the process step described above makes, and its performance index is:

[0052] Drying time: 1.85h

[0053] Adhesion strength: 0.53MPa

[0054] Water resistance: After 48 hours of testing, the surface of the decorative material has no bubbles, cracks, or peeling off.

[0055] Alkali resistance: After 48 hours of testing under the condition of saturated calcium hydroxide solution, there is no bubble on the surface,

[0056] Scrub resistance: After 500 times of scrubbing test, there is no bottom phenomenon,

[0057] Cold resis...

Embodiment 3

[0059] Embodiment 3: group distribution ratio is as follows:

[0060] Clay powder: 555g

[0061] Acrylic emulsion: 337g

[0062] Sodium hexametaphosphate: 7g

[0063] Sodium Benzoate: 6g

[0064] Ethylene glycol: 25g

[0065] Propylene glycol: 45g

[0066] Methylcellulose: 5g

[0067] Titanium dioxide: 20

[0068] Dimethicone: 2g

[0069] According to above-mentioned raw material ratio, look for the surface decoration material that the process step described above makes, and its performance index is:

[0070] Drying time: 2h

[0071]Adhesion strength: 0.51MPa

[0072] Water resistance: After 48 hours of testing, the surface of the decorative material has no bubbles, cracks, or peeling off.

[0073] Alkali resistance: After 48 hours of testing under the condition of saturated calcium hydroxide solution, there is no bubble on the surface,

[0074] Scrub resistance: After 500 times of scrubbing test, there is no bottom phenomenon,

[0075] Cold resistance: at a temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
timeaaaaaaaaaa
Login to View More

Abstract

The invention is a kind of dual environmental protection building surface ornamenting material produced by using brick powders of grinded waste construction clay bricks as main materials and its producing method. The invention makes clay brick powders as main materials, and is compounded from such chemical industry materials as acrylic acid emulsion, sodium hexametaphosphate, sodium benzoate, glycol, trimethylene glycol, polydimethyl siloxanes, methylcellulose and titanium oxide powder as per certain proportion. The invention has simple technics, convenient and sanitary construction, and can be used both in upscale wall surface and surfaces of column, tablet and board. After ornamented, it has elegant and vivid brick wall style, especially suitably used for outer ornament and repair of building wall surfaces whose outer walls need brick wall structures.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a clay acrylic surface decoration material made of waste resources and a preparation method thereof. Background technique [0002] With the development of the economy, the development of urban construction has been brought about. At present, in the field of urban construction, on the one hand, a large number of abandoned dilapidated bricks and discarded clay building materials become construction waste and bring great pollution to the city. The accumulation of construction waste has seriously affected the ecological environment of relevant areas. People have gradually realized that it is an excellent resource for sustainable utilization of material processing. [0003] On the other hand, in the field of building surface decoration, there are continuous innovation requirements for water-based environmental protection surface decoration materials in order to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/02
Inventor 曹民干
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com