Making process of compound wood-plastic material product

A technology of composite materials and manufacturing methods, which is applied in the field of manufacturing wood-plastic blended composite products, can solve the problems that consumers cannot feel the natural quality of wood, the filling amount of wood powder is not very high, and the appearance of wood-plastic products is not good. , to achieve the effect of high impact strength and tensile strength, high filling content and clear wood grain

Active Publication Date: 2006-03-01
浙江诚信包装有限公司
View PDF3 Cites 96 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Both of the above two patents involve the pre-drying and pre-treatment of wood powder, which will greatly reduce production efficiency and high production cost
And because the filling amount of wood flour in the mixture is not very high, the appearance of the wood-plastic product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Making process of compound wood-plastic material product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The formula of wood-plastic blended composite particles is as follows:

[0024] Wood flour (80 mesh): 100 parts

[0025] Polypropylene: 50 parts

[0026] Polypropylene-maleic anhydride graft copolymer: 3 parts

[0027] Coupling agent A-174: 1 part

[0028] Antioxidant 1010: 0.6 parts

[0029] Fiberglass: 8 parts

[0030] Toner: 0.2 parts

[0031] Stearic acid: 1 part

[0032] According to the above ratio, add the pelletizing extruder at the same time. The granulation extruder adopts a counter-rotating non-intermeshing twin-screw extruder connected in series with a single-screw extruder. Extruder screw diameter 65mm, L / D=28. The prepared pellets are extruded on a single-screw extruder, cooled and shaped, pulled, cut, and modified, and finally made into various wood-plastic products.

Embodiment 2

[0034] The formula of wood-plastic blended composite particles is as follows:

[0035] Bamboo powder (60 mesh): 100 parts

[0036] Polypropylene: 60 parts

[0037] Polypropylene-maleic anhydride graft copolymer: 3 parts

[0038] Dicumyl peroxide: 0.3 parts

[0039] Antioxidant 1010: 1 serving

[0040] Superfine Calcium Carbonate: 15 parts

[0041] Toner: 0.2 parts

[0042] Zinc stearate: 0.5 parts

[0043] Bamboo powder is processed and pulverized from the leftovers of ordinary bamboo processing, and the moisture content is 10%. According to the above ratio, add the pelletizing extruder at the same time. The granulation extruder adopts a counter-rotating non-intermeshing twin-screw extruder connected in series with a single-screw extruder. Extruder screw diameter 65mm, L / D=28. The produced pellets are extruded in a single-screw extruder, cooled and shaped, drawn, cut, modified, and finally made into various wood-plastic products.

Embodiment 3

[0045] The formula of wood-plastic blended composite particles is as follows:

[0046] Wood flour (80 mesh): 100 parts

[0047] HDPE: 70 parts

[0048] Ethylene-vinyl acetate copolymer: 3 parts

[0049]Stearic acid: 1 part

[0050] Titanate coupling agent: 2 parts

[0051] Talc powder: 15 parts

[0052] Toner: 0.2 parts

[0053] Polyoxyethylene wax: 0.5 parts

[0054] Paraffin: 0.5 parts

[0055] According to the above ratio, add the pelletizing extruder at the same time. The granulation extruder adopts a co-rotating meshing twin-screw extruder with a screw diameter of 36 mm, L / D=36, and a rotational speed of 200 rpm. The produced pellets are extruded in a twin-screw extruder, cooled and shaped, drawn, cut, modified, and finally made into various wood-plastic products.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses the making process of compound wood-plastic material product. Un-dried wood powder, plastic grain, compatibilizing agent, coupler, antioxidant, reinforcer, color powder and lubricant in certain proportion are fed to a pelletizing extruder for form granular material; and the granular material is extruded in a forming extruder and further processed through cooling to settle, drawing, cutting and decorating to produce the wood-plastic product. The present invention has the advantages of simple process, high production effect and rich material resource, and the product has timber-like texture, excellent performance and environment friendship.

Description

technical field [0001] The invention relates to a method for manufacturing a wood-plastic blended composite material product. Background technique [0002] my country's forest resources are relatively scarce, but my country is also a big timber consumer, and the consumption of wood products has ranked among the top in the world. Statistics show that in 2002, China has become the world's third largest log and sawn timber consumer. The contradiction between the possession of timber resources and the rapid economic development has become increasingly prominent, and the import volume and import ratio are increasing year by year. The huge gap in the domestic timber market will exist for a long time. [0003] Wood-plastic blended composite material (hereinafter referred to as wood-plastic material) is a new type of material developed in recent years. It is a modified thermoplastic material filled and reinforced with wood fiber or plant fiber. It has the properties and characterist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L97/02C08L23/00C08L25/06C08L27/06C08L35/04C08K7/14B29C47/38B29C48/395
CPCB29C47/0011B29C48/04
Inventor 宗宇后王猛
Owner 浙江诚信包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap