Production of multi-layer metal bush tile spreading materials

A multi-layer metal and production process technology, which is applied in the production field of manufacturing multi-layer metal bearing tile expansion materials, can solve the problems of increased processing cycle, labor cost, environmental pollution, etc., to improve the bonding force and fastness, and eliminate pollution Environmental problems, economic and technical benefits are remarkable

Inactive Publication Date: 2006-08-16
胡长安
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, it costs materials, labor, and molds, increases the processing cycle, and increases the manufacturing cost of the product.
[0004] Second, the bonding firmness between steel and copper-lead alloy layers is poor
The disadvantages of these two treatment methods are: the degree of metallurgical bonding between copper alloy and steel is very small, the diffusion of non-ferrous metals to the steel layer is small, and the diffusion depth is small and uneven, resulting in a gap between the non-ferrous metal working layer of the bearing and the steel back joint surface. poor bond strength
[0005] 3. Poor production environment
In the treatment of the steel back, whether it is degreasing washing, sanding, degreasing washing, or copper plating, organic solvents and chemical agents are used for steel treatment, which brings pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] specific implementation plan

[0016] First weld a layer of copper (Cu) on one face of the expanded flat steel material (this steel material can be made according to the length and shape required by the bearing pad) used as the half garden bearing tile, and the welding method can be used Laser welded to make a steel lining with a welded copper layer. Put the steel lining with the soldered copper layer in the mold cavity, spread the pure copper powder evenly on the surface of the soldered copper layer on the steel back, and then evenly spread a layer of copper alloy powder (the copper alloy composition is lead 19%, tin 6%, copper 75%) and put into a protective atmosphere sintering furnace together with the mold, and sinter at a temperature of 870°C for 25 minutes. The composition of the protective atmosphere is 30% nitrogen and 70% hydrogen. After sintering, when it is cooled to 700 ° C, it is placed on an axial swing rolling machine, and the two loose sintered layers ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A technology for preparing the developed material of multi-layer metallic bush includes such steps as providing a developed steel plate of semi-circular bush, welding a copper layer to its one surface, spreading a layer of Cu-alloy powder, putting it along with its mould in a sinter furnace containing protecting atmosphere, sintering, cooling to 500-800 deg.C, putting it on an axial swinging-rolling machine, thermally swinging rolling on the sintered layer for compacting it, and heat treating.

Description

technical field [0001] The invention relates to a production process of a multi-layer metal bearing tile expansion material. The invention belongs to the production technical field of manufacturing multi-layer metal bearing tile expansion materials. Background technique [0002] With the rapid development of industry in recent years, there is more and more demand for high-speed and high-horsepower diesel engines. With the continuous development of high-speed and supercharged engines, the working environment of bearings is deteriorating, and the requirements for materials and manufacturing of crankshaft and connecting rod bearings are also increasing. come higher. The demand for copper-lead bearing pads and lead-bronze bearing pads with large load-bearing capacity and good fatigue resistance used in internal combustion engines is also increasing. Most of these steel-copper alloy bearing materials are copper-lead alloys and lead-bronze alloy materials, and the manufacture of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F7/04
Inventor 胡长安
Owner 胡长安
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products