Waste gum powder flexible acrylic acid water gap filling material and its preparation method

A technology of acrylic water-based and joint-filling materials, which is applied in building insulation materials, building components, etc., can solve problems such as black pollution, achieve low cost and increase economic value

Inactive Publication Date: 2007-01-31
TONGJI UNIV
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] On the other hand, countless waste automobile tires and waste automobile sealing materials are produced every year, causing increasingly serious black pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: The group distribution ratio is as follows:

[0026] Acrylic Elastic Emulsion 450g

[0027] Sodium hexametaphosphate 5g

[0028] Sodium Benzoate 3g

[0029] Ethylene glycol 8g

[0030] Propylene glycol 16g

[0031] Methylcellulose 15g

[0032] Colorant 0.6g

[0033] Polydimethylsiloxane 0.5g

[0034] Rubber powder (80 mesh) 250g

[0035] Calcium carbonate 210g

[0036] Water 42.5g

[0037] According to the above ratio of raw materials, firstly mix waste rubber powder and calcium carbonate uniformly as component A, and then mix uniformly acrylic elastic emulsion, sodium hexametaphosphate, sodium benzoate, ethylene glycol, propylene glycol, methylcellulose and colorant as component A Component B, then mix and disperse components A and B evenly, and finally add polydimethylsiloxane and water, stir evenly to obtain the desired product. Its performance index is

[0038] Drying time 2h

[0039] Adhesion strength 0.53MPa

[0040] Other indicators are...

Embodiment 2

[0041] Embodiment 2: group distribution ratio is as follows

[0042] Acrylic Elastic Emulsion 440g

[0043] Sodium hexametaphosphate 4.6g

[0044] Sodium Benzoate 3.4g

[0045] Ethylene glycol 7g

[0046] Propylene glycol 17g

[0047] Methylcellulose 15g

[0048] Colorant 0.8g

[0049] Polydimethylsiloxane 0.5g

[0050] Rubber powder (80 mesh) 250g

[0051] Calcium carbonate 210g

[0052] water 50g

[0053] According to the above ratio of raw materials, firstly mix waste rubber powder and calcium carbonate uniformly as component A, and then mix uniformly acrylic elastic emulsion, sodium hexametaphosphate, sodium benzoate, ethylene glycol, propylene glycol, methylcellulose and colorant as component A Component B, then mix and disperse components A and B evenly, and finally add polydimethylsiloxane and water, stir evenly to obtain the desired product. Its performance indicators are:

[0054] Drying time 2h

[0055] Adhesion strength 0.54MPa

[0056] Other indicators...

Embodiment 3

[0057] Embodiment 3: group distribution ratio is as follows:

[0058] Acrylic Elastic Emulsion 420g

[0059] Sodium hexametaphosphate 5g

[0060] Sodium Benzoate 3.5g

[0061] Ethylene glycol 9g

[0062] Propylene glycol 18g

[0063] Methylcellulose 15g

[0064] Colorant 1g

[0065] Polydimethylsiloxane 0.5g

[0066] 60 mesh rubber powder 250g

[0067] Calcium carbonate 220g

[0068] water 57g

[0069] According to the above ratio of raw materials, firstly mix waste rubber powder and calcium carbonate uniformly as component A, and then mix uniformly acrylic elastic emulsion, sodium hexametaphosphate, sodium benzoate, ethylene glycol, propylene glycol, methylcellulose and colorant as component A Component B, then mix and disperse components A and B evenly, and finally add polydimethylsiloxane and water, stir evenly to obtain the desired product. Its performance indicators are:

[0070] Drying time: 2h

[0071] Adhesion strength: 0.54MPa

[0072] Other indicators ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The present invention belongs to the field of building material technology, in the concrete, it relates to a waste rubber powder flexible acrylic acid water-base joint-filling material and its preparation method. It is made up by using rubber powder obtained by processing waste tyre as aggregate, and mixing it with the chemical raw materials of acrylic acid elastic emulsion, sodium hexametaphosphate, sodium benzoate, ethylene glycol, propylene glycol, polydimethylsiloxane, methyl cellulose, calcium carbonate and colouring agent according to a certain mixing ratio.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a flexible acrylic water-based joint filling material of waste rubber powder and a preparation method thereof. Background technique [0002] With the development of economy, the development of urban construction has been brought about. At present, in the field of urban construction, on the one hand, with the rapid development of municipal construction, various new energy-saving and environmentally friendly building materials are called for. Because the promotion and application of many new energy-saving building materials requires the combination of many supporting materials to become an application system that is easy to use and has perfect performance. Some new wall building materials often encounter splicing joints, shrinkage joints, external wall insulation and heat insulation after using energy-saving materials, etc., which require the application of n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/00C08K5/09E04B1/68C08L83/14C08L1/00C08K5/05C08K3/26
Inventor 曹民干余骏
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com