High voltage withstanding over current protection element and its manufacturing method
A technology for protecting components and manufacturing methods, which is applied in the direction of resistance manufacturing, electrical components, and current-responsive resistors. The effect of uniform production speed and current density
Inactive Publication Date: 2007-02-07
KUNSHAN POLYSTAR ELECTRONICS
View PDF2 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In addition, if cobalt 60 (Co 60 ) γ-ray irradiation, it must take a considerable amount of time because of its low energy, and reduce the throughput (throughput)
If electron beam (E-beam) is used for irradiation, it will often generate high heat and cause internal stress, and its manufacturing process is not easy to control, which will affect the quality of output, and its manufacturing cost is relatively high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0028] Hereinafter, an embodiment of the overcurrent protection element and the manufacturing method thereof of the present invention will be described by means of drawings.
[0029] figure 1 It is a sheet-shaped polymer substrate 10, which is manufactured through a part of chemical cross-linking process (including two steps of mixing and pressing). First, 3.85 grams of a first polymer (copolymer containing 8% glycidyl methylacrylate (GMA) and polyethylene), a second polymer (containing 0.9% maleic anhydride) Maleic anhydride grafted polyethylene) 1.65 g, carbon black RU430 15.4 g, magnesium hydroxide 11.55 g, Talc 6.60 g and HDPE 15.95 g are added to a batch mixer for mixing, and the mixing is controlled Process conditions: a temperature of 160°C, a rotation speed of 60 rpm and a time of 9 minutes to form a polymer mixture with the first degree of crosslinking and the characteristics of crystalline thermoplastic plastics. After mixing, the polymer mixture was hot-pressed under ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to an over-current protector, which comprises: a substrate with chemical crosslink positive-temperature factor (PTC) and two electrode foils, wherein its production comprises: a, providing the macromolecule mixture with PTC character, which has the first polymer with function group X, the second polymer with the function group Y, and the conductive powder, heating it into the polymer softening point to mixed melt, to obtain the character of crystal thermal plastic; b, compressing the macromolecule mixture into sheet macromolecule substrate; c, stacking the sheet macromolecule substrates into one-layer stacked polymer layer; d, connecting two electrode foils into the upper and lower surfaces of said polymer layer; e, thermally compressing the upper and lower electrode foils and the stacked polymer layer, to generate the original chemical crosslink reaction of function group X and function group Y, to form one chemical crosslink PTC substrate. The inventive substrate can resist the high voltage at 600V.
Description
Technical field [0001] The present invention relates to a high-voltage and over-current protection element and a manufacturing method thereof, in particular to a high-voltage and over-current protection element having a positive temperature coefficient (PTC) characteristic and a manufacturing method thereof. Background technique [0002] The resistance value of the conventional PTC element is quite sensitive to temperature changes. When the PTC element is in normal use, its resistance can maintain the lowest value so that the circuit can operate normally. However, when an over-current or over-temperature phenomenon occurs and the temperature rises to a critical temperature, the resistance value instantly bounces to a high-resistance state (for example, 10 4 ohm or more) and reverse the excess current to achieve the purpose of protecting the battery or circuit components. Since the PTC element can effectively protect electronic products, it has been seen that the PTC element is in...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): H01C7/02H01C7/13H01C17/00
Inventor 蔡东成朱复华王绍裘
Owner KUNSHAN POLYSTAR ELECTRONICS