Method for producing bamboo board

A production method and bamboo technology, which are used in the pretreatment of molding materials, wood processing appliances, household appliances, etc., can solve the problem that the quality indicators of bamboo boards do not meet the optimal requirements, the specific methods of pressing and molding are not exactly the same, and they cannot fully meet the requirements. Use requirements and other issues, to achieve the effect of simple and easy production process, high production efficiency, and not easy to deform

Inactive Publication Date: 2007-05-30
DASSO INDASTRIAL GRUP KO LTD +1
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional processing method of bamboo boards is: take moso bamboo and break it into bamboo silk or bamboo slices, after drying, dip into the mold, and then press high pressure to solidify the molding materials. Although the existing production technology is relatively mature, the product quality is relatively high. Ideal, but due to the large changes in the process parameters in the production process and the specific methods of pressing and forming are not completely the same, the quality indicators of the bamboo boards cannot meet the best requirements, especially the density uniformity of the boards and the direction of width and thickness The anti-deformation performance needs to be further improved. Some export products are often returned because they cannot meet international standards, and cannot occupy the international market to the maximum extent.
In addition, for the boards used in some special industries, such as: outdoor decorative materials, indoor geothermal flooring, indoor swimming pool floors, etc., the existing bamboo boards cannot fully meet their use requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing bamboo board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 1) adopt commercially available moso bamboo chips, which are processed into silk-connected bamboo chips fragmented along the fiber direction through the rolling and combing of the seaming machine;

[0021] 2) After bleaching, carbonization, and modification treatments, the silk-like bamboo chips are dried or naturally dried to a moisture content of 6%;

[0022] 3) Bamboo slices after step 2) are immersed in melamine resin or phenolic resin adhesive for 360 seconds, taken out and drained vertically, dried or naturally dried to a moisture content of 10%;

[0023] 4) The density of the finished bamboo board is 1.1-1.3g / cm 3 Calculate, take the above-mentioned bamboo chip of corresponding weight, classify by bamboo chip grade, pave and install in the mould, the high grade bamboo chip is used as lining, and the low grade bamboo chip is used as base material;

[0024] 5) Send the paved bamboo chips into the hot press for pressing, the control pressure is 9.5MPa, and the time...

Embodiment 2

[0027] 1) adopt commercially available moso bamboo chips, which are processed into silk-connected bamboo chips fragmented along the fiber direction through the rolling and combing of the seaming machine;

[0028] 2) After bleaching, carbonization and modification treatments, the silk-like bamboo chips are dried or naturally dried to a moisture content of 8%;

[0029] 3) Bamboo slices after step 2) are immersed in melamine resin or phenolic resin adhesive for 420 seconds, taken out and drained vertically, dried or naturally dried to a moisture content of 11%;

[0030] 4) The density of the finished bamboo board is 1.1-1.3g / cm 3 Calculate, take the above-mentioned bamboo chip of corresponding weight, classify by bamboo chip grade, pave and install in the mould, the high grade bamboo chip is used as lining, and the low grade bamboo chip is used as base material;

[0031] 5) Send the paved bamboo chips into the hot press for pressing, the control pressure is 8.5MPa, and the time ...

Embodiment 3

[0034] 1) adopt commercially available moso bamboo chips, which are processed into silk-connected bamboo chips fragmented along the fiber direction through the rolling and combing of the seaming machine;

[0035] 2) After bleaching, carbonization and modification treatment, the silk-like bamboo chips are dried or naturally dried to a moisture content of 10%;

[0036] 3) The bamboo slices in step 2) are immersed in melamine resin or phenolic resin adhesive for 480 seconds, taken out and drained vertically, dried or naturally dried to a moisture content of 12%;

[0037] 4) The density of the finished bamboo board is 1.1-1.3g / cm 3 Calculate, take the above-mentioned bamboo chip of corresponding weight, classify by bamboo chip grade, pave and install in the mould, the high grade bamboo chip is used as lining, and the low grade bamboo chip is used as base material;

[0038] 5) Send the paved bamboo chips into the hot press for pressing, the control pressure is 7.5MPa, and the time...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

It relates to bamboo plate production method. 1) it processes bamboo fiber to thread bamboo sheet, 2) bleach, carbonize and dry after modifying property, 3) soaking the said bamboo sheet in glue agent, dry to the water content 10-12%, taking the bamboo plate of the corresponding weight based on 1.1-1.3g/cm3 intensity to fill into the mold, 5) sending the bamboo sheet to heat compressor with compression force 6-10 MPa for 30-60 minutes, setting the compression temperature 100+-5DEG C for melamine resin adhesive, or 135+-5DEG C for phenol aldehyde resin adhesive, and 6)process the compressed plate. The made bamboo plate is even in intensity, high in static curve strength and hardness, anti wearing and good in stability.

Description

technical field [0001] The invention belongs to the technical field of bamboo board production. Background technique [0002] Bamboo is used as raw material to process and make boards. Because the raw materials are cheap, easy to obtain, low cost, beautiful in appearance, high in strength and good in performance, they are widely used in flooring, furniture and other decorative boards or other industries. In particular, moso bamboo grows fast and is rich in resources. It can be a good substitute for wooden boards, saves wood resources, and is conducive to the protection of the ecological environment. Therefore, it has been paid more and more attention by the country and the industry. The traditional processing method of bamboo boards is: take moso bamboo and break it into bamboo silk or bamboo slices, after drying, dip into the mold, and then press high pressure to solidify the molding materials. Although the existing production technology is relat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N1/00B27N3/08B27N3/18B27N3/20B27N1/02
Inventor 张齐生林海来国民
Owner DASSO INDASTRIAL GRUP KO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap