High temperature resistant electromagnetic wave absorbent material film and preparing method

A technology for absorbing materials and electromagnetic waves, applied in electrical components, magnetic/electric field shielding, shielding, etc., can solve problems that endanger system safety and fail to improve electrical performance, and achieve excellent performance, simple and effective quality control, and product consistency and stability improvements

Inactive Publication Date: 2007-10-17
UNIV OF ELECTRONICS SCI & TECH OF CHINA
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the seeker of the communication system of some equipment re-enters the atmosphere, the antenna array will generate a very high temperature, and ordinary absorbing materials cannot withstand such a high temperature (300 ° C), not only cannot improve the electrical performance, On the contrary, it will endanger the safety of the entire system due to combustion and carbonization, so the development of high-temperature absorbing materials has very important significance and application prospects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The components of the following examples are all in weight percent.

[0029] fluororubber

FPM2601

Hexamethylenediamine amino

Formate

copper inhibitor

No. 65

magnesium oxide

Electromagnetic wave absorption

Agent MF18

22.1

0.2

0.1

3.3

66.5

[0030] fluororubber

FPM2601

Hexamethylenediamine amino

Formate

copper inhibitor

No. 65

Zinc oxide

Electromagnetic wave absorption

Agent MF18

24.9

0.25

0.12

3.7

62.3

[0031] fluororubber

FPM2601

Hexamethylenediamine amino

Formate

copper inhibitor

No. 65

magnesium oxide

Electromagnetic wave absorption

Agent MF18

20

0.3

0.2

4

60

[0032] fluororubber

FPM2601

Hexamethylenediamine amino

Formate

copper inhibitor

No. 65

magnesium oxide

El...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

A heat resisting electromagnetic wave absorbing material mainly belongs to electromagnetic wave absorbing material technology. The invention includes following components: fluororubber FPM2601: 20-25wt.%, Hexamethylene diamine carbamate: 0.2-0.3wt.%, copper inhibitor No.65: 0.1-0.2wt.%, vulcanizer: 2-4wt.% and electromagnetic wave absorbing agent: 60-70wt.%. The invention has a good temperature stability, consistency and a simple and effective quality control, a high tensile strength and breaking elongation.

Description

technical field [0001] The invention belongs to the technology of electromagnetic wave absorbing materials, in particular to a high temperature resistant electromagnetic wave absorbing film material and a preparation method thereof. Background technique [0002] The widely used electromagnetic wave absorbing materials (hereinafter referred to as wave absorbing materials) mainly include dielectric and magnetic. Dielectric absorbing materials are generally carburized foam absorbing materials, which have significant advantages such as light weight and high absorption rate, but have disadvantages such as thick thickness, narrow frequency band, poor high temperature resistance (generally not exceeding 120°C), and low mechanical strength. . Magnetic wave-absorbing materials are mainly divided into rubber plate and coated wave-absorbing materials, which have the advantages of wide absorption frequency band, thin thickness, high absorption rate, and good mechanical properties, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H05K9/00G12B17/02
Inventor 谢建良陈良梁迪飞陆海鹏翁小龙邓龙江
Owner UNIV OF ELECTRONICS SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap