Austenitic stainless steel

A technology of austenitic stainless steel and stainless steel, applied in the field of austenitic stainless steel, can solve the problems of high energy consumption, high work hardening rate, large deformation resistance, etc., and achieve the reduction of raw material cost, good cold and hot processing performance, and good mechanical properties and the effect on tensile properties

Inactive Publication Date: 2008-03-12
宁波耀义新材料有限公司
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1) 0Cr 18 Ni 9 The nickel content in steel is relatively high, which is 8% to 10%. However, the nickel resources in our country are scarce, and the price of nickel has risen rapidly in recent years, resulting in the high price of this brand of stainless steel.
[0004] 2) 0Cr 18 Ni 9 Steel has high deformation resistance and high work hardening ra

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Below in conjunction with embodiment the present invention is described in further detail.

[0017] The preparation method of the stainless steel alloy sample of the embodiment of the present invention is: batching adopts 08F scrap steel, micro-carbon ferrochrome (C: 0.1%, Cr: 60%), electrolytic metal manganese (Mn: 99.9%), nitrided electrolytic metal manganese (Mn: 90%, N: 6%). Except electrolytic manganese nitride, all of them are smelted in intermediate frequency furnace.

[0018] When the molten steel is completely melted and the temperature reaches 1570°C, remove the oxidized slag and add lime and fluorite to make slag. ) for 12 batches of diffusion deoxidation, and the samples in front of the furnace were taken for spectral analysis. According to the analysis results, adjust the alloy composition, add nitrided electrolytic metal manganese, and then use silicon calcium powder to diffuse and deoxidize 8 batches, and refine for 10 minutes. Add silicon-calcium bloc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an austenite stainless steel comprising by weight Cr12%-14%, Mn 16%-18%, C 0.03%-0.15%, and N 0.15%-0.35%, the remainder are Fe and unavoidable foreign matters, which are Si, P, S and Ni, the allowable percentages by weight of which are Si<=1.0%, P<=0.035%, S<=0.03%, and Ni<=0.35%. The austenite stainless steel is of excellent cold and hot machining plasticity, good tensile property, is free from any magnetism after tensioning, and is of good resistance to corrosion and relatively cheap price.

Description

technical field [0001] The invention relates to an austenitic stainless steel. Background technique [0002] National standard 0Cr 18 Ni 9 (304) steel, as a widely used steel, has good corrosion resistance, heat resistance, low temperature strength and mechanical properties. Widely used in household goods, auto parts, medical appliances, building materials, chemicals, food industry, agriculture, ship parts, etc., can be made into samples of various shapes and specifications, such as steel wire, round steel, square steel, forgings, flanges Wait. However, currently, the national standard 0Cr 18 Ni 9 (304) steel still has the following deficiencies: [0003] 1) 0Cr 18 Ni 9 The nickel content in steel is relatively high, which is 8% to 10%. However, my country's nickel resources are scarce, and in recent years, the price of nickel has risen rapidly, resulting in the high price of stainless steel of this grade. [0004] 2) 0Cr 18 Ni 9 Steel has high deformation resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/38C22C38/58
Inventor 张跃
Owner 宁波耀义新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap