Water-based fracturing fluid gelatinizer and producing method thereof
A water-based fracturing and thickening agent technology, applied in chemical instruments and methods, drilling compositions, etc., can solve problems such as inability to withstand ultra-high temperature, residual glue adsorption and clogging, poor shear resistance, etc., to achieve durable Good high temperature performance, high shear resistance, good sand carrying performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0039] The weight percent of each monomer and water: DMAA: DADMAC: AN: DMC (DAC): H 2 O=30:15:6:14:35.
[0040] Preparation of the solution: add 350g of distilled water to a 2000ml beaker, add 300g of DMAA monomer, 150g of DADMAC monomer, add 60g of AN monomer, add 140g of DMC (DAC) monomer, stir and dissolve for 30 minutes, slowly add in And agent (sodium hydroxide) to pH4.5. The stirring solution was continued to ripen for 30 minutes.
[0041] Adjustment of the solution: adjust the pH value to 4.5±0.5 again, and adjust the temperature to 10±1°C.
[0042] Polymerization of the solution: Blow nitrogen to remove oxygen for 15-20 minutes, add catalyst V650.5g / L, V50 0.05g / L, ammonium persulfate 0.03g / L, sodium formaldehyde sulfoxylate 0.03g / L in sequence under nitrogen protection , stop blowing nitrogen and seal the polymerization tank, induce for 15-20 minutes, and observe whether there is a temperature rise. When there is a temperature rise of 2°C during the induction perio...
Embodiment 2
[0045] The weight percent of each monomer in water: DMAA: DADMAC: AN: DMC (DAC): H 2 O=25:15:6:14:40.
[0046] Preparation of the solution: Add 400g of distilled water to a 2000ml beaker, add 250g of DMAA monomer, 150g of DADMAC monomer, add 60g of AN monomer, add 140g of DMC (DAC) monomer, stir and dissolve for 30 minutes, slowly add in And agent (sodium hydroxide) to pH4.5. The stirring solution was continued to ripen for 30 minutes.
[0047] Adjustment of the solution: adjust the pH value to 4.5±0.5 again, and adjust the temperature to 10±1°C.
[0048] Polymerization of the solution: Blow nitrogen to remove oxygen for 15-20 minutes, add catalyst V650.5g / L, V50 0.04g / L, ammonium persulfate 0.03g / L, sodium formaldehyde sulfoxylate 0.03g / L in sequence under nitrogen protection , stop blowing nitrogen and seal the polymerization tank, induce for 15-20 minutes, and observe whether there is a temperature rise. When there is a temperature rise of 2°C during the induction period...
Embodiment 3
[0051] The weight percent of each monomer and water: DMAA: DADMAC: AN: DMC (DAC): H 2 O=30:15:8:14:33.
[0052] Preparation of the solution: Add 330g of distilled water into a 2000ml beaker, add 300g of DMAA monomer, 150g of DADMAC monomer, add 80g of AN monomer, add 140g of DMC (DAC) monomer, stir and dissolve for 30 minutes, slowly add in And agent (sodium hydroxide) to pH4.5. The stirring solution was continued to ripen for 30 minutes.
[0053] Adjustment of the solution: adjust the pH value to 4.5±0.5 again, and adjust the temperature to 10±1°C.
[0054] Polymerization of liquid: Blowing nitrogen to remove oxygen for 15-20 minutes, under the protection of nitrogen, add catalyst V650.8g / L, V50 0.08g / L, ammonium persulfate 0.04g / L, sodium formaldehyde sulfoxylate 0.04g / L , stop blowing nitrogen and seal the polymerization tank, induce for 15-20 minutes, and observe whether there is a temperature rise. When there is a temperature rise of 2°C during the induction period, it...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap